Correlation between microhardness and microstructure of anodic film on 2024 aluminum alloy

Abstract

The correlation between the microhardness and microstructure features of anodic films on 2024 aluminum alloy formed in the mixed sulfuric acid/oxalic acid electrolyte was studied using micro-hardness tester and scanning electron microscope (SEM). The results show that the microhardness of the anodic film is influenced by the microstructure of the anodic film such as the film porosity, and the order and continuity of the hexagon columnar cells. The film microhardness increases as the porosity of the anodic film decreases and the order and continuity of the film cells increase. With the same current density, as the anodic film thickens with anodizing time, the film microhardness increases because the film porosity decreases and the order and continuity of the cells are also improved. Under the condition of the same anodizing time, as the current density increases, the film microhardness decreases due to the higher film porosity and the poorer order and continuity of the film cells. The film porosity increases because the increased current density can accelerate the oxidation reaction, strengthen the filed-assisted dissolution and the heating effect in the anodic film, resulting in decreased film order and continuity.

Keywords

aluminum alloy / anodizing / microhardness / porosity / microstructure

References

[1] Thompson G E. Porous Anodic Alumina-Fabrication, Characterization and Applications [J]. Thin Solid Films, 1997, 297(1–2): 192-201.

[2] Keller F, Hunter M S, Robinson D L. Structural Features of Oxide Coatings on Aluminum [J]. J. Electrochem. Soc., 1953, 100(9): 411-419.

[3] Morks M F, Hamdy A S, Fahim N F, et al. Growth and Characterization of Anodic Films on Aluminum Alloys in 5-sulfosalicylic Acid Solution [J]. Surf. Coat. Technol., 2006, 200(16–17): 5 071-5 076.

[4] González J A, Morcillo M, Escudero E, et al. Atmospheric Corrosion of Bare and Anodized Aluminium in a Wide Range of Environmental Conditions. Part I: Visual Observations and Gravimetric Results [J]. Surf. Coat. Technol., 2002, 153(2–3): 225-234.

[5] Im K H S, Kim D H, Lee W, et al. Tribological Properties of Nanoporous Anodic Aluminum Oxide Film [J]. Surf. Coat. Technol., 2010, 205(5): 1 431-1 437.

[6] Takaya M, Hashimoto K, Toda Y, et al. Novel Tribological Properties of Anodic Oxide Coating of Aluminum Impregnated with Iodine Compound [J]. Surf. Coat. Technol., 2003, 169–170: 160-162.

[7] Tian L P, Zuo Y, Zhao X H, et al. The Improved Corrosion Resistance of Anodic Films on Aluminum by Nickel Ions Implantation [J]. Surf. Coat. Technol., 2006, 201(4): 3 246-3 252.

[8] Cirik E, Genel K. Effect of Anodic Oxidation on Fatigue Performance of 7075-T6 Alloy [J]. Surf. Coat. Technol., 2008, 202(21): 5 190-5 201.

[9] Fratila-Apachitei L E, Duszczyk J, Katgerman L. Vickers Microhardness of AlSi(Cu) Anodic Oxide Layers Formed in H2SO4 at Low Temperature [J]. Surf. Coat. Technol., 2003, 165(3): 309-315.

[10] Fratila-Apachitei L E, Duszczyk J, Katgerman L. AlSi(Cu) Anodic Oxide Layers Formed in H2SO4 at Low Temperature Using Different Current Waveforms [J]. Surf. Coat. Technol., 2003, 165(3): 232-240.

[11] Ma S J, Luo P, Zhou H H, et al. Preparation of Anodic Films on 2024 Aluminum Alloy in Boric Acid-Containing Mixed Electrolyte [J]. Trans. Nonferrous Met. Soc. China, 2008, 18(4): 825-830.

[12] Belwalkar A, Grasing E, Van Geertruyden W, et al. Effect of Processing Parameters on Pore Structure and Thickness of Anodic Aluminum Oxide (AAO) Tubular Membranes [J]. J. Membrane Sci., 2008, 319(1–2): 192-198.

[13] Garcia-Vergara S J, Skeldon P, Thompson G E, et al. A Flow Model of Porous Anodic Film Growth on Aluminum [J]. Electrochim. Acta, 2006, 52(2): 681-687.

[14] Ren J J, Zuo Y. The Anodizing Behavior of Aluminum in Malonic Acid Solution and Morphology of the Anodic Films [J]. Appl. Surf. Sci., 2012, 261: 193-200.

[15] Bensalah W, Elleuch K, Feki M, et al. Comparative Study of Mechanical and Tribological Properties of Alumina Coatings Formed on Aluminium in Various Conditions [J]. Materials Design, 2009, 30(9): 3 731-3 737.

[16] Chung C K, Liao M W, Chang H C, et al. Effects of Temperature and Voltage Mode on Nanoporous Anodic Aluminum Oxide Films by One-Step Anodization [J]. Thin Solid Films, 2011, 520(5): 1 554-1 558.