Application of image analysis based on SEM and chemical mapping on PC mortars under sulfate attack

Abstract

The degradation mechanisms of cementitious materials exposed to sulfate solutions have been controversial, despite considerable research. In this paper, two methodologies of image analysis based on scanning electron microscope and chemical mapping are used to analyse Portland cement mortars exposed to sodium sulfate solution. The effects of sulfate concentration in solution and water to cement ratio of mortar, which are considered as the most sensitive factors to sulfate attack, are investigated respectively by comparing the macro expansion with microstructure analysis. It is found that the sulfate concentration in pore solution, expressed as sulfate content in C-S-H, plays a critical role on the supersaturation with respect to ettringite and so on the expansion force generated.

Keywords

image analysis / mapping / sulfate attack / pore solution

References

[1] Maltais Y, Samson E, Marchand J Predicting the Durability of Portland Cement Systems in Aggressive Environments—Laboratory Validation[J]. Cem. Concr. Res., 2004, 34(9): 1 579-1 589.

[2] Lothenbach B, Bary B, Le Bescop P, . Sulfate Ingress in Portland Cement[J]. Cem. Concr. Res., 2010, 40(8): 1 211-1 225.

[3] Marchand J, Skalny J P Materials Science of Concrete: Sulfate Attack Mechanisms, Special Volume[M], 2006 New York Wiley

[4] Santhanam M, Cohen M D, Olek J Mechanism of Sulfate Attack: A Fresh Look: Part 1: Summary of Experimental Results[J]. Cem. Concr. Res., 2002, 32(6): 915-921.

[5] Irassar E F, Bonavetti V L, González M Microstructural Study of Sulfate Attack on Ordinary and Limestone Portland Cements at Ambient Temperature[J]. Cem. Concr. Res., 2003, 33(1): 31-41.

[6] Mehta P K Mechanism of Expansion Associated with Ettringite Formation[J]. Cem. Concr. Res., 1973, 3(1): 1-6.

[7] Cohen M D Theories of Expansion in Sulfoaluminate — Type Expansive Cements: Schools of Thought[J]. Cem. Concr. Res., 1983, 13(6): 809-818.

[8] Mehta P K Mechanism of Sulfate Attack on Portland Cement Concrete-Another Look[J]. Cem. Concr. Res., 1983, 13(3): 401-406.

[9] Scherer G W Stress From Crystallization of salt[J]. Cem. Concr. Res., 2004, 34(9): 1 613-1 624.

[10] Scherer G W Crystallization in Pores[J]. Cem. Concr. Res., 1999, 29(8): 1 347-1 358.

[11] Mouret M, Ringot E, Bascoul A Image Analysis: A Tool for the Characterisation of Hydration of Cement in Concrete — Metrological Aspects of Magnification on Measurement[J]. Cem. Concr. Compos., 2001, 23(2–3): 201-206.

[12] Brough A R, Atkinson A Automated Identification of the Aggregate-Paste Interfacial Ttransition Zone in Mortars of Silica Sand with Portland or Alkali-Activated Slag Cement Paste[J]. Cem. Concr. Res., 2000, 30(6): 849-854.

[13] Igarashi S, Kawamura M, Watanabe A Analysis of Cement Pastes and Mortars by a Combination of Backscatter-Based SEM Image Analysis and Calculations Based on the Powers Model[J]. Cem. Concr. Compos., 2004, 26(8): 977-985.

[14] Scrivener K L Backscattered Electron Imaging of Cementitious Microstructures: Understanding and Quantification[J]. Cem. Concr. Compos., 2004, 26(8): 935-945.

[15] Kjellsen K O, Detwiler R J, Gjørv O E Backscattered Electron Image Analysis of Cement Paste Specimens: Specimen Preparation and Analytical Methods[J]. Cem. Concr. Res., 1991, 21(2–3): 388-390.

[16] Kocaba V, Gallucci E, Scrivener K L Methods for Determination of Degree of Reaction of Slag in Blended Cement Pastes[J]. Cem. Concr. Res., 2012, 42(3): 511-525.

[17] Sezer G I, Ramyar K, Karasu B, . Image Analysis of Sulfate Attack on Hardened Cement Paste[J]. Mater. Des., 2008, 29(1): 224-231.

[18] Gutierrez-Padilla M G D, Bielefeldt A, Ovtchinnikov S, . Simple Scanner-Based Image Analysis for Corrosion Testing: Concrete Application[J]. J. Mater. Process. Technol., 2009, 209(1): 51-57.

[19] Haha MB, Gallucci E, Guidoum A, . Relation of Expansion due to Alkali Silica Reaction to the Degree of Reaction Measured by SEM Image Analysis[J]. Cem. Concr. Res., 2007, 37(8): 1 206-1 214.

[20] Barbarulo R, Peycelon H, Prene S Experimental Study and Modelling of Sulfate Sorption on Calcium Silicate Hydrates[J]. Annales de Chimie: Science des Materiaux, 2003, 28: S5-S10.