Multi-level flocculation structures of fresh cement paste by confocal laser scanning microscope

Abstract

Under saturation dosage of all kinds of SP, the free water amount was examined by centrifuge. The distribution of solution and flocculation microstructures in fresh cement paste was observed in three-dimensional space by confocal laser scanning microscope(CLSM). Results indicate that SP can increase the free water amount by destroying the flocculated cement particle structure and different free water amount is released by different kinds of SP. The changes of the size of flocculation structures and the dispersion of solution were obviously detected with confocal laser scanning microscope: the size of flocculation structures was smaller and more dispersed in fresh cement paste with polycarboxylate superplasticizer, but the size of flocculation structures was bigger and cannot be dispersed uniformly in fresh cement paste with others SP. The multi-level flocculation structures theoretical model of fresh cement paste was then set up. The theory indicates that different kinds of SP with different dispersion strength will open the flocculation structures at different levels, which in turn present different water reducing rate.

Keywords

multi-level flocculation structure / CLSM / SP / free water amount

References

[1] Powers TC Structure and Rheological Characteristics of Fresh Concrete[M], 1983 Beijing China Architecture & Building Press 177-187.

[2] Qian XL, Zhao SL Performances and Mechanism of Concrete Superplasticizer[J]. J. Nanjing Univ. Technol., 2002, 24(2): 61-66.

[3] Powers T C The Properties of Fresh Concrete[M], 1968 533-652.

[4] Steinour HH Rate of Sedimentation: Nonflocculated Suspension of Uniform Spheres[J]. Indusir. and Eng. Chem., 1944, 36: 617-640.

[5] Zuo YF, Sui TB, Wang DM Effect of Superplasticizers on Rheologic Performance of Fresh Cement Paste[J]. Concr., 2004 38-39.

[6] Wang LJ, Tan XQ, Cao ML Study of Cement Flocculation[J]. Concr., 2007, 1: 29-31.

[7] Zhang DM, Qian HP Civil Engineering Materials[M], 2005 337-342.

[8] Wang LJ, Tan XQ Research on the Fractal Characteristics of Flocculated Structure in Fresh Cement Paste with Superplasticizer[J]. Bull. Chin. Ceramic Soc., 2010, 2: 473-476.

[9] Wang DM, Zhang LR, Zhang WL Effect of Superplasticizers on Multi-Level Model of Fresh Cement Paste[J]. J. Build Mater., 2012, 12(6): 754-758.

[10] Huang BJ, Li JJ Study on the Mechanism of RhB by Fluorescence Spectroscopy[J]. J. Tianjin Norm. Univ. (Natural Science Edition), 2005, 25(3): 8-10.

[11] Elke K, Ozlem C, Koenraad VB, . Effect of Free Water Removal from Early-age Hydrated Cement Pastes on Thermal Analysis[J]. Constr. Build Mater., 2009, 23: 3 431-3 438.

[12] Wang ZM The Interface Chemistry Phenomena and Rheological Properties of Cement-Water-Superplasticizer System[D], 2006 Beijing Beijing University of Technology(Chinese)

[13] Han S, Yan PY, Kong XM Study on the Compatibility of Cement-Superplasticizer System Based on the Amount of Free Solution[J]. Sci. China Tech. Sci., 2011, 54: 183-189.