Synthesis of a macromer, MPEGAA, used to prepare an AMPS-modified polyacrylic acid superplasticizer

Abstract

A macromer, methoxypolyethylene glycol acrylate (MPEGAA), was synthesized by direct esterification using methoxypolyethylene glycol (MPEG-1200) and acrylic acid (AA) as the main materials. MPEGAA was then used to prepare a polyacrylic acid superplasticizer modified with 2-acrylamido-2-methylpropane sulfonic acid (AMPS). A single-factor test was performed to investigate the effects of the molar ratio of acid to alcohol (n(AA)/n(MPEG)), inhibitor amount, catalyst amount, temperature, and time of esterification on the synthesis of MPEGAA. The experimental results showed that the optimal esterification conditions were as follows: n(AA)/n(MPEG), 3.5:1; amount of hydroquinone (as an inhibitor), 1.2%; amount of para-toluenesulfonic acid (as a catalyst), 5.5%; reaction temperature, 95 °C; and reaction time, 6 h. The AMPS-modified polyacrylic acid superplasticizer prepared under the optimal esterification conditions enabled the achievement and maintenance of high cement dispersibility. At an admixture amount of 0.15%, the cement paste fluidity was initially as high as 300 mm, and then decreased to 315 mm after 1 h and to 290 mm after 2 h.

Keywords

AMPS-modified polyacrylic acid superplasticizer / esterification reaction / macromer / esterification ratio

References

[1] Xu ZN, Xiao GM, Zhou JN Kinetics of Carboxylic Acid Terpolymer High Performance Water-reducing Agent[J]. Polym. Mater. Sci. Eng., 2010, 26(1): 26-28.

[2] Palacios M, Puertas F, Bowen P, . Effect of PCs Superplasticizers on the Rheological Properties and Hydration Process of Slag-blended Cement Slurrys[J]. J. Mater. Sci., 2009, 44(10): 2 714-2 723.

[3] Yoshioka K, Tazawa E, Kawai K, . Adsoprtion Characteristics of Superplasticizers on Cement Component Minerals[J]. Cem. Concr. Compos., 2002, 32(10): 1 507-1 513.

[4] Papayianni I, Tsohos G, Oikonomou N, . Influence of Superplasticizer Type and Mix Design Parameters on the Performance of Them in Concrete Mixtures[J]. Cem. Concr. Compos., 2005, 27(2): 217-222.

[5] Li CZ, Feng NQ, Li YD, . Effect s of Polyethlene Oxide Chains on the Performance of Polycarboxylate-type Water-reducers [J]. Cem. Concr. Res., 2005, 35(5): 867-873.

[6] Li S, Wen ZY Dispersibility and Airentraining Performance of Polycarboxylate-type Water Reducers[J]. J. Chin. Ceram. Soc., 2009, 37(4): 616-621.

[7] Jiang YQ, Gong MZ Effect of Superplasticizer Type on Early Age Hydration of Cement[C]. 1st International Conference on Microstructure Related Durability of Cementitious Composites, Southeast Univ., 2008

[8] Pei MS, Li C, Wang ZF The Synthesis of Carboxyl Calcium Lignosulfonate and Its Applications as Water reducer[J]. J. Dispersion Sci. Technol., 2008, 29(4): 530-534.

[9] Wu SS, Luo YL, Ran QP Effects of Comb Copolymer PAA-g-MPEO on Rheological and Dispersion Properties of Aqueous CaCO₃ Suspensions[J]. Polym. Bull., 2007, 59(3): 363-369.

[10] Chang W, Li H, Wei M Effects of Polycarboxylic Acid Based Superplasticiser on Properties of Sulphoaluminate Cement[J]. Mater. Res. Innovations, 2009, 13(1): 7-10.

[11] Deng SS, Ran QP, Wu SS Effect of PAA-g-MPEO Comb Polymer on TiO₂ Suspensions[J]. Polym. plast. Technol. Eng., 2008, 47(12): 1 278-1 282.

[12] Gong JL, Guan XM, Zhang RY, . Development and Study of a New Polycarboxylic Series Concrete High Performance Water-Reducer[J]. J. Henan Polyt. Univ., 2006, 25(1): 65-68.

[13] Etsuo S, Kazuo Y, Akira O Molecular Structure and Dispersionadsorption Mechanisms of Comb-type Superplasticizers Used in Japan[J]. J. Adv. Concr. Technol., 2003, 1(1): 16-25.

[14] Kazuo Y, Shoichi O, Shunsuke H Controlling of the Adsorption and Dispersing Force of Polyacrylic-type Superplasticizer by Sulfateion Concentration in Aqueous Phase[J]. Cem. Concr. Res., 2001, 31(2): 375-383.

[15] Zhang ZQ, Ding XC, Wei F e a1 Synthesis of Macromonomer for Polycarboxylic Acid Type Water-reducers[J]. J. Chongqing Building Univ., 2007, 29(4): 111-114.

[16] Zhu BW, Xi Q, Gao H e a1 The Relationship between Structure and Properties of Copolymers of Polycarboxylate SuperpIasticizer[J]. J. Wuhan Inst. of Chem. Technol., 2005, 27(1): 15-19.