Effects of quenching process on mechanical properties and microstructure of high strength steel

Abstract

The effects of direct quenching and tempering (DQ-T) process and conventional reheat quenching and tempering (RQ-T) processes on mechanical properties and microstructure of high strength steel were investigated. The DQ process was found to enhance the hardenability of steel effectively. The tensile strength and yield strength of DQ specimen was 975 MPa and 925 MPa respectively, which were higher than those of RQ specimen’s of 920 MPa and 871 MPa. In contrast, low temperature toughness (−40 °C, AKV) of DQ-T specimen (124 J) was generally inferior to that of RQ-T specimen (156 J). The direct quenching temperature was one of the potential process parameters to determine strength/toughness balance of steel manufactured by DQ process. The experimental results showed that excellent strength/toughness balance was obtained when the specimens was quenched at temperature in the range of 850–910 °C. The yield strength and impact energy (−40 °C) of DQ steel decreased significantly with increasing of quenching temperature, although the tensile strength was nearly stable.

Keywords

direct quenching / reheat quenching / mechanical properties / microstructure

References

[1] Iwasaki Y., Kobayashi K., Ueno K., . Production of HSLA Seamless Steel Pipes for Offshore Structures and Line Pipes by Direct-quench and Tempering [J]. Transactions ISIJ, 1985, 25: 1 059-1 068.

[2] Ouchi C. Development of Steel Plates by Intensive Use of TMCP and Direct Quenching Processes[J]. ISIJ Int., 2001, 41(6): 542-553.

[3] Taylor K.A., Hansen S.S. Effects of Vanadium and Processing Parameters on the Structures and Properties of Direct-Quenched Low-Carbon Mo-B Steel[J]. Metall. Mater. Trans. A, 1991, 22(10): 2 359-2 374.

[4] Taylor K.A., Hansen S.S. The Boron Hardenability Effect in Thermomechanically Processed Direct-Quenched 0.2% Carbon Steels [J]. Metall. Mater. Trans. A, 1990, 21(6): 1 697-1 708.

[5] Hwang G.C., Lee S., Yoo J.Y., . Effect of Direct Quenching on Microstructure and Mechanical Properties of Copper-Bearing High-Strength Alloy Steels[J]. Material Science and Engineering, 1998, 252(2): 256-268.

[6] Xiao G.Z., Di H.S., Zhu F.X. Influence of Direct Quenching on Microstructure and Mechanical Properties of Steel Plate for Large Oil Storage Tanks[J]. JMEPEG, 2010, 19(6): 868-872.

[7] Mekkawy M.F., Fawakhry K.A., Mishreky M.L., . Direct Quenching of Low Manganese Steels Microalloyed with Vanadium or Titanium [J]. Iron Steel Maker, 1990, 17(10): 75-83.

[8] Taylor K.A. Hardenability and Mechanical Properties of 0.5Mo-B Steels: Direct Quenching Versus Reheat Quenching [J]. Iron Steel Maker, 1993, 19(2): 43-51.

[9] Chang W.S. Microstructure and Mechanical Properties of 780 MPa High Strength Steel Produced by Direct-Quenching and Tempering Process [J]. J. Mater. Sci., 2002, 37(10): 1 973-1 979.

[10] Yoo J.Y., Choo W.Y., Park T.W. Microstructures and Age Hardening Characteristics of Direct Quenched Cu Bearing HSLA Steel[J]. ISIJ Int., 1995, 35(8): 1 034-1 040.

[11] Qiu J., Jua X., Xin Y. Effect of Direct and Reheated Quenching on Microstructure and Mechanical Properties of CLAM Steels[J]. Journal of Nuclear Materials, 2010, 407(3): 189-194.