Mechanical properties and microstructure evolution of cold-deformed high-nitrogen nickelfree austenitic stainless steel during annealing

Abstract

The mechanical properties and microstructure evolution of cold-deformed CrMnN austenitic stainless steel annealed in a temperature ranging from 50 °C to 650 °C for 90 min and at 550 °C for different time were investigated by tensile test, micro hardness test, and Transmission Electron Microscope (TEM). The steel was strengthened when it got annealed at temperatures ranging from 100 °C to 550 °C, while it was softened when it got annealed at temperatures ranging from 550 °C to 650 °C. Annealing temperature had stronger effect on mechanical properties than annealing time. TEM observations showed that nano-sized precipitates formed when the steel was annealed at 150 °C for 90 min, but the size and density of precipitates had no noticeable change with annealing temperature and time. Recrystallization occurred when the steel was annealed at temperatures above 550 °C for 90 min, and its scale increased with annealing temperature. Nanosized annealing twins were observed. The mechanisms that controlled the mechanical behaviors of the steel were discussed.

Keywords

annealing / mechanical property / microstructure / twinning / high nitrogen austenitic stainless steel

References

[1] Simmons J. W. Mechanical Properties of Isothermally Aged Highnitrogen Stainless Steel[J]. Metall. Mater. Trans., 1995, 26A(8): 2 579-2 595.

[2] Saller G., Hahn K. S., Scheu C., . Microstructural Evolution of Cr-Mn-N Austenitic Steels during Cold Work Hardening[J]. Mater. Sci. Eng., 2006, 427A(1–2): 246-254.

[3] Wang S. T., Yang K., Shan Y. Y., . Plastic Deformation and Fracture Behaviors of Nitrogen-alloyed Austenitic Stainless Steels[J]. Mater. Sci. Eng., 2008, 490A(1–2): 95-104.

[4] Lee T. H., Oh C. S., Kim S. J., . Deformation Twinning in Highnitrogen Austenitic Stainless Steel[J]. Acta Mater., 2007, 55(11): 3 649-3 662.

[5] Yakubtsov I. A., Ariapour A., Perovic D. D. Effect of Nitrogen on Stacking Fault Energy of F.C.C. Iron-based Alloys[J]. Acta Mater., 1999, 47(4): 1 271-1 279.

[6] Fréchard S., Redjaïmia A., Lach E., . Dynamical Behavior and Microstructural Evolution of A Nitrogen-alloyed Austenitic Stainless Steel[J]. Mater. Sci. Eng., 2008, 480A(1–2): 89-95.

[7] Dischino A., Barteri M., Kenny J. M. Effects of Grain Size on the Properties of A Low Nickel Austenitic Stainless Steel[J]. J. Mater. Sci., 2003, 38(23): 4 725-4 733.

[8] Bhavsingh B., Sivakumar K., Balakrishnabhat T. Effect of Cold Rolling on Mechanical Properties and Ballistic Performance of Nitrogenalloyed Austenitic Steels[J]. Int. J. Impact Eng., 2009, 36(4): 611-620.

[9] Lu G. X., Zhao Z. W. Fundamentals of Physical Metallurgy[M], 1980 Shanghai Shanghai Science and Technology Press

[10] Zhang S. Y., Yao J. H. Study on Hardening Constituent by Lowtemperature Annealing of 1Cr18Ni9Ti Steel[J]. J. Tianjin inst. Text. Sci. Technol., 1999, 18(2): 78-81.

[11] Karaman I., Sehitoglu H., Chumlyakov Y. I., . The Deformation of Low-stacking-fault-energy Austenitic Steels[J]. JOM, 2002, 51(7): 31-37.

[12] Humphreys F. J., Hatherly M. Recovery after Deformation[M], 1996 Oxford Pergamon Press

[13] Yang D. Z. Dislocations and Strengthening Mechanisms in Metals[M], 1991 Harbin Harbin Institute of Technology Press

[14] Dash S., Brown N. An Investigation of the Origin and Growth of Annealing Twins[J]. Acta Metall., 1963, 11(9): 1 067-1 075.

[15] Kim Y. S., Nama S. M., Kim S. J. Strain Rate Dependence of Deformation Behavior of High-nitrogen Austenitic Steels[J]. J. Mater. Process. Technol., 2007, 187–188: 575-577.

[16] Vanderschaeve F., Taillard R., Foct J. Discontinuous Precipitation of Cr₂N in A High Nitrogen, Chromium-manganese Austenitic Stainless Steel[J]. J. Mater. Sci., 1995, 30(23): 6 035-6 046.