Ir protective coatings for carbon structural materials

Abstract

Ir coatings were deposited on the heat-treated C/C composites and graphite by double glow plasma. Microstructure and morphology of the coating and substrate were observed by SEM and TEM. The effect of the surface treatment for the carbon structural materials on the microstructure of the coating was investigated. Many large gaps and pores appeared on the surface of the substrates after heat treatment. The Ir coating did not fully covered on the surface of heat-treated C/C composite and graphite substrates because of the large gaps and pores on the surface of substrates. The Ir coating exhibited excellent ablation resistance at super-high temperature. After super-high temperature ablation, the coating kept the integrity, but the coating was weekly bonded to the substrates. Some microcracks and micropores appeared on the surface of as-ablated coating. The Ir coating would need thick enough to cover and fill the large microgaps and micropores on the surface of the heat-treated C/C and graphite substrates.

Keywords

coating / iridium / ablation / graphite / carbon/carbon composites

References

[1] Chen Z.F., Wu W.P., Cheng H., Liu Y., Wang S.M. Microstructure and Evolution of Iridium Coating on the C/C composites Ablated by Oxyacetylene Torch[J]. Acta Astronaut., 2010, 66: 682-687.

[2] Wu W.P., Chen Z.F., Cheng H., Wang L.B., Zhang Y. Tungsten and Iridium Multilayered Structure by DGP as Ablation-resistance Coatings for Graphite[J]. Appl. Surf. Sci., 2011, 257: 7 295-7 304.

[3] Criscione JM, Mercuri PA, Scham EP, Smith AW, Volk HF. High Temperature Protective Coating for Graphite[R]. ML-TDR-64-173, Part I, 1964

[4] Criscione JM, Mercuri PA, Scham EP, Smith AW, Volk HF. High Temperature Protective Coating for Graphite[R]. ML-TDR-64-173, Part II, 1964

[5] Wu W.P., Chen Z.F., Lin X., Li B.B., Cong X.N. Effects of Bias Voltage and Gas Pressure on Orientation and Microstructure of Iridium Coating by Double Glow Plasma[J]. Vacuum, 2011, 86: 429-437.

[6] Chen Z.F., Wu W.P., Cong X.N., Wang L.B. Study on Iridium Coating Produced by Double Glow Plasma[J]. Advanced Materials Research, 2011, 314–316: 214-218.

[7] Wang L.B., Chen Z.F., Zhang Y., Wu W.P. Ir Coating Prepared on Nb substrate by Double Glow Plasma[J]. Inter. J. Refractory Metal. Hard Mater., 2009, 27(3): 590-594.

[8] Garcia J.R.V., Goto T. Chemical Vapor Deposition of Iridium, Platinum, Rhodium and Palladium[J]. Mater. Trans., 2003, 44: 1 717-1 728.

[9] Yang W.B., Zhang L.T., Hua Y.F., Cheng L.F. Thermal Stability of Iridium Coating Prepared by MOCVD[J]. Int. J. Refract. Met. Hard Mater., 2009, 22: 33-36.

[10] Cai H.Z., Chen L., Wei Y., Hu C.Y. Deposition Effectiveness Investigation of Ir Film Prepared by MOCVD[J]. Rare Metal Mater. Eng., 2010, 39: 209-212.

[11] Ohriner E.K. Processing of Iridium and Iridium Alloys: Methods From Purification to Fabrication[J]. Platinum Metals Rev., 2008, 186: 186-197.

[12] El Khakani M.A., Chaker M., Le Drogoff B. Iridium Thin Films Deposited by Radiofrequency Magnetron Sputtering[J]. J. Vac. Sci. Technol. A, 1998, 16: 885-888.

[13] Gong Y.S., Wang C.B., Shen Q., Zhang L.M. Low-temperature Deposition of Iridium Thin Films by Pulsed Laser Deposition[J]. Vacuum, 2008, 82: 594-598.

[14] Snell L., Nelson A., Molian P. A Novel Laser Technique for Oxidationresistant Coating of Carbon-carbon Composite[J]. Carbon, 2001, 39: 991-999.

[15] Etenko A., McKechnie T., Shchetkovskiy A., Smirnov A. Oxidationprotective Iridium and Iridium-rhodium Coatings Produced by Electrodeposition from Molten Salts[J]. ECS Trans., 2007, 3: 151-167.

[16] Čukman D., Vuković M., Milun M. Enhanced Oxygen Evolution on an Electrodeposited Ruthenium+ iridium Coating on Titanium[J]. J. Electroanal. Chem., 1995, 389: 209-213.

[17] Wang L.B., Chen Z.F., Zhang P.Z., Wu W.P., Zhang Y. Ir Coating Prepared on Mo Substrate by Double Glow Plasma[J]. J. Coat. Technol. Res., 2009, 6(4): 517-522.

[18] Ultramet-Advanced Materials Solutions. Propulsion System Components, Liquid Rocket Engines [OL]. http://www.ultramet.com/propulsion_system_components_liquid_rocket.html

[19] Zhang Y., Chen Z.F., Wang L.B., Wu W.P., Fang D. Effect of Heat Treatment at 1 300 °C on W Coating Prepared by Double-glow Plasma on Carbon/carbon Composite[J]. J. Coat. Technol. Res., 2009, 6(2): 237-241.

[20] Zhang Y., Chen Z.F., Wang L.B., Yan B., Li C., Fang D. Phase and Microstructure of Tungsten Coating on C/C Composite Prepared by Double-glow Plasma[J]. Fusion Engin. Design, 2009, 84: 15-18.

[21] Wu W.P., Lin X., Chen Z.F., Chen Z., Cong X.N., Xu T.Z., Qiu J.L. Microstructural Characterization and Mechanical Property of Iridium Coating Produced by Double Glow Plasma[J]. Plasma Chem. Plasma Process, 2011, 31: 465-475.

[22] Farhan S., Li K.Z., Guo L.J., Gao Q.M., Lan F.T. Effect of Density and Fibre Orientation on the Ablation Behaviour of Carbon-carbon Composites[J]. New Carbon Materials, 2010, 25: 161-167.

[23] Fang D., Chen Z.F., Song Y.D., Sun Z.G. Morphology and Microstructure of 2.5 Dimension C/SiC Composites Ablated by Oxyacetylene Torch[J]. Ceram. Int., 2009, 35: 1 249-1 253.

[24] Li K.Z., Shen X.T., Li H.J., Zhang S.Y., Feng T., Zhang L.L. Ablation of the Carbon/carbon Composite Nozzle-throats in a Small Solid Rocket Motor[J]. Carbon, 2011, 49: 1 208-1 215.

[25] Han J.C., He X.D., Du S.Y. Oxidation and Ablation of 3D Carbon-carbon Composite at up to 3000 °C[J]. Carbon, 1995, 33: 473-478.

[26] Wang J.M., Zhang Z.W., Xu Z.H., Lin X., Wu W.P., Chen Z.F. Oxidation of Double Glow Plasma Discharge Coatings of Iridium on Molybdenum for Liquid Fueled Rocket Motor Casings[J]. Corrosion Engineering, Science and Technology, 2011, 46(6): 732-736.

[27] Wimber R.T., Hills S.W., Wahl N.K., Tempero C.R. Kinetics of Evaporation/ Oxidation of Iridium[J]. Metallurgical Transactions A, 1977, 8: 193-199.

[28] Bao Z.B., Murakami H., Yamabe-Mitarai Y. Effects of Thermal Exposure on Ir-based Alloys with and without Pt Coating[J]. Corr. Sci., 2011, 53: 1 224-1 229.