Electrochemical corrosion behavior of the laser continuous heat treatment welded joints of 2205 duplex stainless steel

Heping Liu , Xuejun Jin

Journal of Wuhan University of Technology Materials Science Edition ›› 2011, Vol. 26 ›› Issue (6) : 1140 -1147.

PDF
Journal of Wuhan University of Technology Materials Science Edition ›› 2011, Vol. 26 ›› Issue (6) : 1140 -1147. DOI: 10.1007/s11595-011-0378-y
Article

Electrochemical corrosion behavior of the laser continuous heat treatment welded joints of 2205 duplex stainless steel

Author information +
History +
PDF

Abstract

The electrochemical corrosion behaviors of the welded joints of 2205 duplex stainless steel with the laser continuous heat treatment were investigated. The secondary austenite formation is the outcome of thermodynamic equilibrium breach of the alloy during heat treatment and the result of the continuous heat treatment which has the most important effect on the weld material. The partitioning behaviors of chromium and molybdenum as well as the volume fraction of ferrite and austenite have a remarkable influence on the composition of the individual phase. Mechanical examination of the laser trated weld demonstrates that the tensile strength and yield strength increase with increasing the amount of the secondary austenite. It is shown that the ultimate tensile strength of the 6 kW laser-treated weld is higher about 20 MPa than no heat treatment weld and the ductility can be further improved without compromising strength. The results indicate that the welding alters the corrosion behavior because of different post heat treatment power and the broad active peak is not identified which is attributed to the dissolution of the secondary austenitic in the ferrite phase. It is indicated that pitting resistance equivalent (PRE) values of base metal and 6 kW weld are higher than that of other welds; base metal is 33.7, 6 kW weld 33.3, no treatment 32.4, 4 kW weld 32.8, 8 kW weld 32.5. The extent of corrosion resistance improvement after reheating treatment is mainly caused by the removal of nitrogen from ferritic regions, which occurred as a consequence of secondary austenite growth.

Keywords

potentiodynamic polarization / duplex stainless steel / continuous heat treatment / secondary austenite

Cite this article

Download citation ▾
Heping Liu, Xuejun Jin. Electrochemical corrosion behavior of the laser continuous heat treatment welded joints of 2205 duplex stainless steel. Journal of Wuhan University of Technology Materials Science Edition, 2011, 26(6): 1140-1147 DOI:10.1007/s11595-011-0378-y

登录浏览全文

4963

注册一个新账户 忘记密码

References

[1]

Muthupandi V., Srinivasan P., Seshadri S.K., . Effect of Weld Metal Chemistry and Heat Input on the Structure and Properties of Duplex Stainless Steel Welds[J]. Mater. Sci. Eng. A, 2003, 358: 9-16.

[2]

Kordatos J.D., Fourlaris G., Papadimitriou G. The Effect of Cooling Rate on the Mechanical and Corrosion Properties of SAF 2205 (UNS 31803) Duplex Stainless Steel Welds[J]. Scripta Mater., 2001, 44: 401-408.

[3]

Kobayashi D.Y., Wolynec S. Evaluation of the Low Corrosion Resistant Phase Formed during the Sigma Phase Precipitation in Duplex Stainless Steels [J]. Mater. Res., 1999, 2: 239-247.

[4]

Park C.J., Rao V.S., Kwon H.S. Effects of Sigma Phase on the Initiation and Propagation of Pitting Corrosion of Duplex Stainless Steel[J]. Corros., 2005, 61: 76-83.

[5]

Chen C.Y., Yen H.W., Yang J.R. Sympathetic Nucleation of Austenite in a Fe-22Cr-5Ni Duplex Stainless Steel [J]. Scripta Mater., 2007, 56: 673-676.

[6]

Wang S.H., Chiu P.K., Yang J.R., . Gamma (Γ) Phase Transformation in Pulsed GTAW Weld Metal of Duplex Stainless Steel[J]. Mater. Sci. Eng. A, 2006, 420: 26-33.

[7]

Wu H.C., Tsay L.W., Chen C. Laser Beam Welding of 2205 Duplex Stainless Steel with Metal Power Additions[J]. ISIJ Int., 2004, 44: 1720-1726.

[8]

Capello E., Chiarello P., Previtali B., . Laser Welding and Surface Treatment of a 22Cr-5Ni-3Mo Duplex Stainless Steel [J]. Mater. Sci. Eng., A, 2003, 351: 334-343.

[9]

Fourie J.W., Robinson F.P.A. Literature Review on the Influence of Weld-heat Inputs on the Mechanical and Corrosion Properties of Duplex Stainless Steels[J]. J. S. Afri. Min. Metall., 1990, 90: 59-65.

[10]

Nowacki J., Rybicki P. Influence of Heat Input on Corrosion Resistance of SAW Welded Duplex Joints[J]. J.Achieve. Mater. Manufact. Eng., 2006, 17: 113-116.

[11]

Capello E, Castelnuovo M, Previtali B, et al. Laser Surface Treatment of Laser Welded Duplex Stainless Steel[C]. In: Proc. 34th int. Matador Conf., 2004

[12]

Garfias-Mesias L.F., Sykes J.M., Tuck C.D.S. The Effect of Phase Compositions on the Pitting Corrosion of 25 Cr Duplex Stainless Steel in Chloride Solutions[J]. Corros. Sci., 1996, 38: 1319-1330.

[13]

Liou H.Y., Hsieh R.I., Tsai W.T. Microstructure and Pitting Porrosion in Simulated Heat-affected Zones of Duplex Stainless Steels[J]. Mater. Chem. Phys., 2002, 74: 33-42.

[14]

Zhang L., Zhang W., Jiang Y., . Influence of Annealing Treatment on the Corrosion Resistance of Lean Duplex Stainless Steel 2101[J]. Electrochim. Acta, 2009, 54: 5387-5392.

[15]

Martins M., Casteletti L.C. Microstructural Characteristics and Corrosion Behavior of a Super Duplex Stainless Steel Casting[J]. Mater. Charact., 2009, 60: 150-155.

[16]

Kurt B., Calik A. Interface Structure of Diffusion Bonded Duplex Stainless Steel and Medium Carbon Steel Couple[J]. Mater. Charact., 2009, 60: 1035-1040.

[17]

Bautista A., Blanco G., Velasco F., . Corrosion Performance of Welded Stainless Steels Reinforcements in Simulated Pore Solutions[J]. Constr. Build. Mater., 2007, 21: 1267-1276.

[18]

Velasco F., Blanco G., Bautista A., . Effect of Welding on Local Mechanical Properties of Stainless Steels for Concrete Structures Using Universal Hardness Tests[J]. Constr. Build. Mater., 2009, 23: 1883-1891.

[19]

Hussain EAM. An Electrochemical Investigation of Erosion Corrosion of Duplex Stainless Steel in Seawater Containing Sand Particles[D]. Cranfield University, 2001

[20]

Hussain E.A.M., Robinson M.J. Erosion-corrosion of 2205 Duplex Stainless Steel in Flowing Seawater Containing Sand Particles[J]. Corros. Sci., 2007, 49: 1737-1754.

[21]

Symniotis E. Galvanic Effects on the Active Dissolution of Duplex Stainless Steels[J]. Corros., 1990, 46: 2-12.

[22]

Lo I.H., Fu Y., Lin C.J., . Effect of Electrolyte Composition on the Active-to-passive Transition Behavior of 2205 Duplex Stainless Steel in H2SO4/HCl Solutions[J]. Corros. Sci., 2006, 48: 696-708.

[23]

Nelson T.W., Lippold J.C., Mills M.J. Nature and Evolution of the Fusion Boundary in Ferritic-austenitic Dissimilar Weld Metals[J]. Weld. J., 1999, 78: 329-337.

[24]

Garzón C.M., Serna C.A., Brandi S.D., . The Relationship Between Atomic Partitioning and Corrosion Resistance in the Weld-heat Affected Zone Microstructures of UNS S32304 Duplex Stainless Steel[J]. J. Mater. Sci., 2007, 42: 9021-9029.

AI Summary AI Mindmap
PDF

118

Accesses

0

Citation

Detail

Sections
Recommended

AI思维导图

/