Multilayer clad plate of stainless steel/aluminum/aluminum alloy

Abstract

The 3, 5, 20 layer clad plate from austenitic stainless steel, pure aluminum and aluminum alloy sheets were fabricated in different ways. The stretch and interface properties were measured. The result shows that 20 layer clad plate is better than the others. Well-bonded clad plate was successfully obtained in the following procedure: Basic clad sheet from 18 layer Al1060/Al3003 sheets was firstly obtained with an initial rolling reduction of 44% at 450 °C, followed by annealing at 300 °C, and then with reduction of 50% at 550 °C from STS304 on each side. The best 20 layer clad plate was of 129 MPa bonding strength and 225 MPa stretch strength.

Keywords

multilayer clad plate / hot rolling / bonding strength / stretch strength

References

[1] Rhee K. Y., Han W. Y., Park H. J., . Fabrication of Aluminum/Copper Clad Composite Using Hot Hydrostatic Extrusion Process and Its Material Characteristics[J]. Materials Science and Engineering, 2004, 384: 70-76.

[2] Lee J. E., Bae D. H., Chung W. S. Effects of Annealing on the Mechanical and Interface Properties of Stainless Steel/Aluminum/Copper Clad-metal Sheets[J]. Journal of Materials Processing Technology, 2007, 187–188: 546-549.

[3] Zhou J. J. Studies on the Roll-forming and Properties of Stainless Steel/Aluminum/Stainless Steel Laminated Sheet[D], 2006 Xi’an Xi’an University of Architecture & Technology

[4] Yuan J. W. Study on Compound Rolling Process of Stainless Steel/Aluminum (Aluminum Alloy)[D], 2007 Xi’an Xi’an University of Architecture & Technology