Microscopic and dynamic rheological characteristics of crumb rubber modified asphalt

Abstract

A test for crumb rubber modified asphalt containing 20% crumb rubber particles (30 mesh) was performed using a scanning electron microscope (SEM). The experimental results indicate that the crumb rubber particles are evenly distributed in the asphalt. Shear rate sweep and shear-temperature sweep tests on the crumb rubber modified asphalt at −20–80 °C using a dynamic shear rheology (DSR) instrument, were carried out. The tests show that the complex modulus decreases with increasing temperature; at equivalent temperature, higher load frequencies lead to a larger complex modulus, and this value increasingly decreases as the temperature increases; the phase angle increases with temperature and decreases as the load frequency increases. It can be concluded that the rutting resistance limiting temperature of crumb rubber modified asphalt is 78 °C, and the anti-fatigue limiting temperature is 16 °C, which shows that the asphalt has preferable rutting resistance characteristics at high temperature, as well as anti-fatigue characteristics. In addition, the complex modulus master curve at different temperatures was plotted according to the time temperature equivalence principle, which allows the study of the dynamic state behavior of crumb rubber modified asphalt at a wide range of load frequency.

Keywords

crumb rubber modified asphalt / microcosmic characteristic / rheology characteristic / complex modulus / phase angle

References

[1] Mull M. A., Stuary K., Yehia A. Fracture Resistance Characterization of Chemically Modified Crumb Rubber Asphalt Pavement[J]. Journal of Materials Science, 2002, 37: 557-566.

[2] Navarro F. J., Partal P., Martínez-Boza F., Valencia C., Gallegos C. Rheological Characteristics of Ground tire Rubber-modified Bitumens[J]. Chemical Engineering Joural, 2002, 89: 53-61.

[3] Navarro F. J., Partal P., Martínez-Boza F., Gallegos C. Thermo-rheological Behaviour and Storage Stability of Ground tire Rubber-modified Bitumens[J]. Chemical Engineering Joural, 2004, 83: 2041-2049.

[4] Palit S. K., Sudhakar Reddy K., Pandey B. B. Laboratory Evaluation of Crumb Rubber Modified Asphalt Mixes[J]. Journal of Materials in Civit Engineering, 2004, 45: 0899-1561.

[5] Wong C.-g., Wong W.-gun. Effect of Crumb Rubber Modifiers on High Temperature Susceptibility of Wearing Course Mixtures[J]. Construction and Building Materialls, 2007, 21: 1741-1745.

[6] Judith C., Wang S.M. ASCE Zeng X., Asce M. Influence of Temperature and Pressure on the Dynamic Properties of Rubber-Modified Asphalt Concrete[J]. Journal of Materials in Civil Engineering, 2006, 125: 0899-1561.

[7] Palit S. K., Sudhakar Reddy K., Pandey B. B. Laboratory Evaluation of Crumb Rubber Modified Asphalt Mixes[J]. Journal of Materials in Civil Engineering, 2004, 45: 45-53.

[8] Let’Icia Socal Da Silva. Study of Rheological Properties of Pure and Polymer-modified Brazilian Asphalt Binders[J]. Journal of Materials Science, 2004, 39: 539-546.

[9] Champion L., Gerard J. F., Planche J. P., Martin D., Erson D. Low Temperature Fracture Properties of Polymer-modified Asphalts Relationships with the Morphology[J]. Journal of Materials Science, 2001, 36: 451-460.

[10] Osman Nuri Celik, Cengiz Duran Atis. Compactibility of hot Bituminous Mixtures Made with Crumb Rubber-modified Binders[J]. Construction and Building Materials, 2007, 10(5): 1-5.