Microstructure and mechanical properties of high-Cr cast iron bars reinforced Hadfield steel matrix composites

Abstract

To obtain the compatible material of high hardness and high toughness, Hadfield steel matrix composites, reinforced by high-Cr cast iron bars made of flux-cored welding wires, which were inserted into the Hadfield steel melt, were investigated. The mechanical properties of three materials, i e, composites for as-cast and quenching-water condition, as well as Hadfield steel, were compared. The results show that the alloy powder inside flux-cored welding wires can be melted by the heat capacity of Hadfield steel melt and solidify into high-Cr cast iron bars. The impact toughness of the composite for quenching-water condition is higher than that of the composite for as-cast condition and is lower than that of the Hadfield steel, but it can still meet the requirements of hardness and toughness in industrial application. Regardless of load variation, composite for quenching-water condition shows better wear resistance than those of the composite for as-cast condition and Hadfield steel. The modified fracture toughness and wear resistance of composites are attributed to not only the combining actions of Hadfield steel matrix and high-Cr cast iron bars, but also the effect of heat treatment.

Keywords

composites / flux-cored welding wires / impact toughness / hadfield steel

References

[1] Srivastava Das A. K. Microstructure and Abrasive Wear Study of (Ti,W)C-reinforced High-manganese Austenitic Steel Matrix Composite[J]. Mater. Lett., 2008, 62: 3 947-3 950.

[2] Du X., Kai H., Kai D., . Influence of Impact Energy on Impact Corrosion-abrasion of High Manganese Steel[J]. Journal of Wuhan University of Technology, 2007, 22(3): 412-416.

[3] Proskurovsky D. I., Rotshtein V. P., Ozur G. E., . Physical Foundations for Surface Treatment of Materials with Low Energy, High Current Electron Beams[J]. Surf. Coat. Technol., 2000, 125: 49-56.

[4] You X. Q., Ren H., Si T. Z. Wear Resistance of WC/steel Composites in Electroslag Melting and Casting[J]. Foundry, 2003, 6: 1 170-1 172.

[5] Zhang G.-S., Xing J.-D., Gao Y.-M. Impact Wear Resistance of WC/Hadfield Steel Composite and Its Interfacial Characteristics [J]. Wear, 2006, 260: 728-734.

[6] Kambakas K., Tsakiropoulos P. Solidification of High-Cr White Cast Iron-WC Particle Reinforced Composites[J]. Mater. Sci. and Eng. A, 2005, 413–414: 538-541.

[7] Bedolla-Jacuinde Correa R., Mejía I., . The Effect of Titanium on the Wear Behaviour of a 16 %Cr White Cast Iron Under Pure Sliding[J]. Wear, 2007, 263: 808-820.

[8] Matsubara Y., Ogi K., Matsuda K. Eutectic Solidification of High Chromium Cast Iron-eutectic Structures and Their Quantitative Analysis[J]. AFS Trans., 1981, 89: 183-196.

[9] Lou D., Hellman J., Luhulima D., . Interactions Between Tungsten Carbide(WC) Particulates and Metal Matrix in WC-reinforced Composites[J]. Mater. Sci. and Eng. A, 2003, 340: 155-162.

[10] Xu Y., Fang L., Cen Q., . Nano Structure and Transformation Mechanism of White Layer for AISI1045 Steel During Impact Wear[J]. Wear, 2005, 258: 537-544.

[11] Kim J. -k., Kim G. -m., Kim S. -j. The Effect of Manganese on the Strain-induced Martensitic Transformation and High Temperature Wear Resistance of Fe-20Cr-1C-1Si Hardfacing Alloy[J]. J. Nucl. Mater., 2001, 289: 263-269.