Effect of lightweight aggregate pre-wetting on microstructure and permeability of mixed aggregate concrete

Abstract

The influence of lightweight aggregate (LWA) pre-wetting on the chemical bound water and pore structure of the paste around aggregate as well as concrete permeability were investigated. The results show that, in early age the dry LWA has significant effect on the formation of dense paste around it and improving the concrete impermeability. However the prewetted LWA has strong water-releasing effect in later age, which increases the hydration degree of the paste around it, and makes the adjacent paste develop a structure with low porosity and finer aperture, furthermore the concrete impermeability can be improved. It is suggested that, as for concrete with low durability requirement, the LWA without pre-wetting treatment can be used as long as meet the workability requirement of fresh concrete, the good impermeability of concrete can be gained as well. As for concrete with high durability requirement, the prewetted LWA should be used, and the pre-wetting time should be extended as long as possible, in order to optimize the concrete structure in long term, and improve the concrete durability.

Keywords

lightweight aggregate / pre-wetting / pore structure / internal curing

References

[1] Lo T. Y., Cui H. Z., Li Z. G. Influence of Aggregate Pre-wetting and Fly Ash on Mechanical Properties of Lightweight Concrete[J]. Waste Management, 2004, 24(4): 333-338.

[2] Bentur A., Igarashi S., Kovler K. Prevention of Autogenous Shrinkage in High-strength Concrete by Internal Curing Using Wet Lightweight Aggregates[J]. Cement and Concrete Research, 2001, 31(11): 1587-1591.

[3] Kovler K., Souslikov A., Bentur A. Pre-soaked Lightweight Aggregates as Additives for Internal Curing of High-strength Concretes[J]. Cement and Concrete Research, 2004, 26(2): 131-138.

[4] P Schwesinger, G Sickert. Reducing Shrinkage in HPC by Internal Curing by Using Pre-soaked LWA[C]. Proceedings of International Workshop on Control of Cracking in Early-age Concrete, Tohoku University, 2000

[5] Zhutovsky S., Kovler K., Bentur A. Efficiency of Lightweight Aggregates for Internal Curing of High Strength Concrete to Eliminate Autogenous Shrinkage[J]. Materials and Structures, 2002, 35(246): 97-101.

[6] X H Zheng. Water Absorbing and Releasing Character of Ceramsite and the Influence on the Structure and Performance of Lightweight Aggregate Concrete[D]. Harbin Institute of Technology, 2005

[7] J T Ding, Y S Guo, K Kimura. State-of-the-art of the Application of Structural Lightweight Aggregate Concrete in Foreign Countries[J]. Concrete, 2002(9): 23–25

[8] C L Li, X Y Lu, H X Zhang. Rapid Test Method for Determining Chloride Diffusivities in Cementicious Materials[J]. Industrial Construction, 1998(28): 41–43

[9] Elsharief A., Cohen M. D., Olek J. Influence of Lightweight Aggregate on the Microstructure and Durability of Mortar[J]. Cement and Concrete Research, 2005, 35(7): 1368-1376.

[10] Martys N. S., Ferraris C. F. Capillary Transport in Mortars and Concrete[J]. Cement and Concrete Research, 1997, 27(5): 747-760.