Synthesis, characterization and flame-retardant properties of epoxy resins and AACHH composites

Abstract

Flame retardant epoxy resins were prepared by a simple mixed method using ammonium aluminum carbonate hydroxy hydrate (AACHH) as a halogen-free flame retardant. The prepared samples were characterized by X-ray diffraction, thermogravimetric and differential scanning calorimetry, scanning electron microscope and limiting oxygen index(LOI) experiments. Effects of AACHH content on LOI of epoxy resins/AACHH composite and flame retardant mechanism were investigated and discussed. Results show that AACHH exhibites excellent flame-retardant properties in epoxy resin(EP). When the content of AACHH was 47.4%, the LOI of EP reached 32.2%. Moreover, the initial and terminal decomposition temperature of EP increased by 48°C and 40 °C, respectively. The flame retarded mechanism of AACHH is due to the synergic flame retardant effects of diluting, cooling, decomposition resisting and obstructing.

Keywords

epoxy resin(EP) / flame retardant / ammonium aluminum carbonate hydroxy hydrate (AACHH) / composite

References

[1] Toldy A., Anna P., Csontos I., . Intrinsically Flame Retardant Epoxy Resin-fire Performance and Background-Part I[J]. Polym. Degrad. Stab., 2007, 92: 2223-2230.

[2] Ren H., Sun J. Z., Wu B. J., . Synthesis and Properties of a Phosphorus-containing Flame Retardant Epoxy Resin Based on Bis-phenoxy (3-hydroxy) Phenyl Phosphine Oxide[J]. Polym. Degrad. Stab., 2007, 92: 956-961.

[3] Chang Z. H., Guo F., Yu J. H., . Synergistic Flame Retardant Effects of Nano-kaolin and Nano-HAO on LDPE/EPDM Composites[J]. Polym. Degrad. Stab., 2007, 92: 1204-1212.

[4] Chigwada G., Jash P., Jiang D. D., . Synergy Between Nanocomposite Formation and Low Levels of Bromine on Fire Retardancy in Polystyrenes[J]. Polym. Degrad. Stab., 2005, 88: 382-393.

[5] Finberg I., Yaakov Y. B., Georlette P. New Flame Retardant Systems for Styrenic Plastics and Method of Preparation[J]. Polym. Degrad. Stab., 1999, 64: 465-470.

[6] Rosa A. D. L., Recca A., Carter J. T., . An Oxygen Index Evaluation of Flammability on Modified Epoxy/Polyester Systems[J]. Polymer, 1999, 40: 4093-4098.

[7] Hippi U., Mattila J., Korhonen M., . Compatibilization of Polyethylene/Aluminum Hydroxide (PE/ATH) and Polyethylene/Magnesium Hydroxide (PE/MH) Composites with Functionalized Polyethylenes[J]. Polymer, 2003, 44: 1193-1201.

[8] Laoutid F., Gaudon P., Taulemesse J. M., . Study of Hydromagnesite and Magnesium Hydroxide Based Fire Retardant Systems for Ethyleneevinyl Acetate Containing Organo-Modified Montmorillonite[J]. Polym. Degrad. Stab., 2006, 91: 3074-3082.

[9] Pinto U. A., Visconte L. L. Y., Nunes R. C. R. Mechanical Properties of Thermoplastic Polyurethane Elastomers with Mica and Aluminum Trihydrate[J]. Eur. Polym. J., 2001, 37: 1935-1937.

[10] Schartel B., Knoll U., Hartwig A., . Phosphonium-Modified Layered Silicate Epoxy Resins Nanocomposites and their Combinations with ATH and Organo-Phosphorus Fire retardant[J]. Polym. Adv. Technol., 2006, 17: 281-293.

[11] Ristolainen N., Hippi U., Seppälä J., . Properties of Polypropylene/Aluminum Trihydroxide Composites Containing Nano-sized Organoclay[J]. Polym. Eng. Sci., 2005, 45: 1568-1575.

[12] Du L., Qu B., Xu Z. Flammability Characteristics and Synergistic Effect of Hydrotalcite with Microencapsulated Red Phosphorus in Halogen-free Flame Retardant EVA Composite[ J]. Polym. Degrad. Stab., 2006, 91: 995-1001.

[13] Lu H., Hu Y., Yang L., . Study of the Fire Performance of Magnesium Hydroxide Sulfate Hydrate Whisker Flame Retardant Polyethylene[J]. Macromol. Mater. Eng., 2004, 289: 984-989.

[14] Zilberman J., Hull T. R., Price D., . Flame Retardancy of Some Ethyleneevinyl Acetate Copolymer-based Formulations[ J]. Fire Mater., 2000, 24: 159-164.

[15] Lynch T. J., Chen T., Riley D. Advances in ATH Benefit Composite Products[J]. Reinf. Plast., 2003, 47: 44-46.

[16] Camino G., Maffezzoli A., Braglia M., . Effect of Hydroxides and Hydroxycarbonate Structure on Fire Retardant Effectiveness and Mechanical Properties in Ethyleneevinyl Acetate Copolymer[J]. Polym. Degrad. Stab., 2001, 74: 457-464.

[17] McGarry K., Zilberman J., Hull T. R., . Decomposition and Combustion of EVA and LDPE Alone and when Fire Retarded with ATH[J]. Polym. Int., 2000, 49: 1193-1198.

[18] Xiao W. D., He P. X., He B. Q. On the Flame-retarding Mechanism of Al₂O₃·3H₂O Towards Cured Epoxy Resin[J]. Chinese J. Appl. Chem., 2000, 17(4): 397-400.

[19] Arthur H. L. Handbook of Plastics Flammability and Combustion Toxicology[M], 1983 New Jersey Noyes Publication 63