Semi-solid casting of high speed steel ingots using inclined slope pre-crystallization method

Abstract

Semi-solid casting of M2 high speed steel ingots was investigated by inclined slope pre-crystallization method. Effects of casting temperature and slope length on the microstructure of M2 HSS ingots were investigated. M2 cast ingots of non-dendritic primary austenite and fine eutectic ledeburite network carbide structure were obtained, with the casting temperature, slope length and angle of 1480 °C, 500 mm and 60° respectively. Meanwhile, the microstructure of cast samples was quantitatively assessed by Image tool software. Results show that optimum mean equivalent diameter of primary austenite crystal grain is 50.8 µm, shape factor is 0.83, and mean thickness of network carbide is 5.21 µm.

Keywords

M2 high speed steel / semi-solid / pre-crystallization / inclined slope

References

[1] Deng Y. K., Chen J. R., Wang S. Z. High Speed Tool Steel[M], 2002 Beijing Metallurgical Industry Press

[2] Li Z. B. Analysis on Strategy to Develop High Speed Steel in China[J]. Iron & Steel, 2005, 1(40): 1-7.

[3] Song X. Q., Zhang W. X. Effect of Different Smelting Process on the Properties of High Speed Tool Steel[J]. Tool Engineering, 2004, 10: 79-80.

[4] Hetzner D. W. Refining Carbide Size Distributions in M1 High Speed Steel by Processing an Alloying[J]. Materials Characterization, 2001, 46: 175-182.

[5] W Jiratticharoean, H Jones, H V Atkinson. Thixoforming of Aluminium 7xxx Alloys Produced Using a Cooling Slope[C]. Semi-solid Processing of the 8 ^th International Conference. Limassol, Cyprus, 2004

[6] Haga T., Suzuki S. Casting of Aluminum Alloy Ingots for Thixoforming Using a Cooling Slope[J]. Journal materials Processing Technology, 2001, 118: 169-172.

[7] T Grimming, J Aguilar, M Fehlbier. Optimization of the Rheocasting Process under Consideration of the Main Influence Parameters on the Microstructure[C]. Semi-solid Processing of the 8 ^th International Conference. Limassol, Cyprus, 2004

[8] C I T, T Motegi, F Tanabe. New Semi-solid Casting of Copper Alloys Using an Inclined Cooling Plate[C]. Semi-solid Processing of the 8 ^th International Conference. Limassol, Cyprus, 2004

[9] S Salarfar, F Akhlaghi, M Nili-Ahmadabadi. Influence of Pouring Conditions in the Inclined Plate Process and Reheating on the Microstructure of the Semi-solid A356 Aluminum Alloy [C]. Semi-solid Processing of the 8 ^th International Conference. Limassol, Cyprus, 2004

[10] F Pahlevani, S Salarfar, M Nili-Ahmadabadi. Dendritic-globular Structure Transition of Ductile Iron in Semi-solid Casting Using Cooling Slope Plate[C]. Semi-solid Processing of the 8 ^th International Conference. Limassol, Cyprus, 2004

[11] Guan R. G., Li C., Li J. P. Preparing Semisolid Stainless Steel 1Cr18Ni9Ti by Sloping Shearing and Cooling[J]. Journal of Northeastern University, 2005, 9(26): 867-870.

[12] Tian Q., Zhou R. F., Jiang Y. H., . Inclined Angle Influence to Semi-solid Structure of Hypoeutectic High Chromium Cast Iron[J]. Special Casting & Non-ferrous Alloys, 2006, 26(3): 159-161.