Synthesis and characteristics of mesoporous silica aerogels with one-step solvent exchange/surface modification

Abstract

The synthesis procedures and physical properties of the ambient dried hydrophobic silica aerogels by using different contents of ethanol (EtOH)/trimethylchlorosilane (TMCS)/n-Hexane as surface modification agent were investigated. One-step solvent exchange and surface modification were simultaneously progressed by immersing silica hydrogels in EtOH/TMCS/n-Hexane solution. It is found that microstructures as well as properties of silica aerogels like porosity, specific density and specific surface area are affected by the contents of surface modification agent in the sol from the results of SEM, TEM morphology, FT-IR chemical structure, BET surface area and BJH pore size analyses. The volume of TMCS is of 10% and 20% of hydrogels, and the final product is hydrophilic xerogels. When TMCS’s percent (v/v) is elevated to 75%–100%, hydrophobic silica aerogels with good performance are synthesized, the porosities of aerogels are in the range of 93.5%–95.8% and the average pore size diameter is less than 20 nm.

Keywords

silica aerogel / surface modification / ambient drying synthesis / microstructure / hydrophobicity

References

[1] Shi F., Wang L. J., Liu J. X. Synthesis and Characterization of Silica Aerogels by a Novel Fast Ambient Pressure Drying Process [J]. Materials Letters, 2006, 60(29–30): 3718-3722.

[2] Sharad D., Bhagat Kim Y. H., . Rapid Synthesis of Water-glass Based Aerogels by in situ Surface Modification of the Hydrogels [J]. Applied Surface Science, 2007, 253(6): 3231-3236.

[3] Reim M., Korner W., Manara J., . Silica Aerogel Granulate Material for Thermal Insulation and Daylighting [J]. Solar Energy, 2005, 79(2): 131-139.

[4] Ackerman W. C., Vlachos M., Rouanet S., . Use of Surface Treated Aerogels Derived from Various Silica Precursors in Translucent Insulation Panels [J]. J. Non-Cryst. Solids, 2001, 285(1–3): 264-271.

[5] Brinker C. J., Scherer G. W. Sol-Gel Science, 1990 2 Sandiego Academic Press 662

[6] Parvathy R. A., Venkateswara R. A., Pajonk G. M. Hydrophobic and Physical Properties of the Ambient Pressure Dried Silica Aerogels with Sodium Silicate Precursor Using Various Surface Modification Agents [J]. Applied Surface Science, 2007, 253(14): 6032-6040.

[7] Einarsrud M. A., Nilsen E. Strengthening of Water Glass and Colloidal Sol Based Silica Gels by Aging in TEOS [J]. J. Non-Cryst. Solids, 1998, 226(1–2): 122-124.

[8] Venkateswara R. A., Nilsen E., Einarsrud M. A. Effect of Precursors, Methylation Agents and Solvents on the Physicochemical Properties of Silica Aerogels Prepared by Atmospheric Pressure Drying Method [J]. J. Non-Cryst. Solids, 2001, 296(3): 165

[9] Schwertfeger F., Frank D., Schmidt M. Hydrophobic Water-Glass Based Aerogels without Solvent Exchange or Supercritical Drying [J]. J. Non-Cryst. Solids, 1998, 225(1): 24-29.

[10] Kim G. S., Hyun S. H. Effect of Mixing on Thermal and Mechanical Properties of Aerogel-PVB Composites [J]. J. Mater. Sci., 2003, 38(9): 1961-1966.

[11] Lee S., Chad Y. C., Hwang H. J., . The Effect of pH on the Physicochemical Properties of Silica Aerogels Prepared by an Ambient Pressure Drying Method [J]. Materials Letters, 2007, 61(14–15): 3130-3133.

[12] Muller C. A., Maciejewski M., Mallat T., Baiker A. Organically Modified Titania-Silica Aerogels for the Epoxidation of Olefins and Allylic Alcohols [J]. J. Catal., 1999, 184(1): 280-293.

[13] Maury S., Buisson P., Perrard A., . Influence of the Sol-gel Chemistry on the Activity of a Lipase Encapsulated in a Silica Aerogel [J]. J. Mol. Catal. B: Enzym., 2004, 29(1–6): 133-148.

[14] Jeong A. Y., Goo S. M., Kim D. P. Characterization of Hydrophobic Si0₂ Powders Prepared by Surface Modification on Wet Gel [J]. J. Sol-Gel Sci. & Technol., 2000, 19(1–3): 483-487.

[15] Venkateswara R. A., Kulkarni M. M., Amalnerkar D. P., . Surface Chemical Modification of Silica Aerogels Using Various Alkyl-alkoxy/Chloro Silanes [J]. Appl. Surf. Sci., 2003, 206(1–4): 262-270.

[16] Shi F., Wang L. J. Rapid Synthesis of Silica Aerogels via a New Ambient Pressure Drying Process [J]. J. Dalian Uni. of Technol., 2006, 46(2): 241-245.