Preparation and characterization of polylactide/montmorillonite nanocomposites

Abstract

The montmorillonite, a form of layered silicate, was successfully intercalated into polylactide (PLA) matrix through solvent-casting technique. In addition, PLA/MMT nanocomposite films were produced, in which homogenous distribution of the silicate lamellae plays a key role in the mechanical properties of the films. A small amount(5wt%) of OMMT intercalated into the PLA matrix resulted in their flexibility enhancement, from 3.68%(pure PLA film) to 352.65%. The results of wide-angle X-ray diffraction (WAXD) patterns confirmed that the silicate interlayer distance increased from 3.044 nm (for OMMT) to 3.56nm (for 5wt%, maximum) with increasing OMMT contents, but decreased to 3.319 nm when OMMT content was over 8wt%. FT-IR also verified the molecular-level associations between PLA chains and OMMT lamellae by vibration variances of hydrogen bonding. DSC thermograms demonstrated that thermal stabilities of the nanocomposite films enhanced, due to the silicate lamellae dispersed into PLA matrix.

Keywords

polylactide / montmorillonite / nanocomposite / characterization / thermo-mechanical property

References

[1] Ragauskas A. J., Williams C. K., Davison B. H., . The Path forward for Biofuels and Biomaterials [J]. Science, 2006, 311: 484-489.

[2] Ljungberg N., Wesslen B. Preparation and Properties of Plasticized Poly(lactic acid) Films [J]. Biomacromolecules, 2005, 6: 1789-1796.

[3] Wang Y., Hillmyer M. A. Polyethylene-Poly (L-lactide) Diblock Copolymers: Synthesis and Compatibilization of Poly(L-lactide)/Polyethy-lene Blends [J]. J. Polym. Sci. Part A: Polym. Chem., 2001, 39: 2755-2766.

[4] Shibata M., Inoue Y., Miyoshi Y. Mechanical Properties, Morphology, and Crystallization Behavior of Blends of Poly(L-lactide) with Poly (butylene succinate-co-L-lactate) and Poly (butylene succinate)[J]. Polymer, 2006, 47: 3557-3564.

[5] Jin H. J., Chin I. J., Kim M. N., . Blending of Poly(L-lactic acid) with Poly (cis-1,4-isoprene) [J]. Eur. Polym. J., 2000, 36: 165-169.

[6] Ray S. S., Bousmina M. Biodegradable Polymers and Their Layered Silicate Nanocomposites. Greening the 21st Century Materials World[J]. Progress in Materials Science, 2005, 50: 962-1079.

[7] Ray S. S., Okamoto M. Polymer/Layered Silicate Nanocomposites: A Review from Preparation to Processing[J]. Prog. Polym. Sci., 2003, 28: 1539-1641.

[8] Ray S. S., Maiti P., Okamoto M., . New Polylactide/Layered Silicate Nanocomposites. 1.Preparation, Charact-erization, and Properties[J]. Macromolecules, 2002, 35(8): 3104-3110.

[9] Ray S. S., Yamada K., Okamoto M., . New Polyactide-Layered Silicate Nanocomposites. 2. Concurrent Improvements of Material Properties, Biodegradability and Melt Rheology[J]. Polym-er, 2003, 44(3): 857-866.

[10] Ray S. S., Yamada K., Okamoto M., . New Polylactide/Layered Silicate Nanocomposites. 3. High Performance Biogradable Materials [J]. Chem. Mater., 2003, 15(7): 1456-1465.

[11] Ray S. S., Yamada K., Okamoto M., . New Polyactide-Layered Silicate Nanocomposites. 5. Designing of Materials with Desired Properties [J].Polymer, 2003, 44(21): 6633-6646.

[12] Krikorian V., Pochan D. J. Poly(L-lactic acid)/Layered Silicate Nanocomposite: Fabrication, Characterization, and Properties [J]. Chem. Mater., 2003, 15: 4317-4324.

[13] Lee S., Kim C. H., Park J. K. Improvement of Processability of Clay/Polylactide Nanocomposit -es by a Combinational Method: In Situ Polymerization of L-lactide and Melt Compounding of Polylactide[J]. J.Appl. Polm. Sci., 2006, 101: 1664-1669.

[14] Chang J. H., An Y. U., Cho D., . Poly(L-lactic acid) Nanocomposites: Comparison of Their Properties with Montmorillonite and Synthetic Mica(II) [J]. Polymer, 2003, 44: 3715-3720.

[15] Paul M. A., Alexandre M., Degee P., . New Nanocomposite Materials Based on Plasticized Poly(L-lactide) and Organo-modified Montmorill-onites: Thermal and Morphological Study[J]. Polymer, 2003, 44: 443-450.

[16] Thellen C., Orroth C., Froio D., . Influence of Montmorillonite Layered Silicate on Plasticized Poly(L-lactide) Blown Films[J]. Polymer, 2005, 46(25): 11176-111727.

[17] Lee J. H., Park T. G., Park H. S., . Thermal and Mechanical Characteristics of Poly(L-lactic acid) Nanocomposite Scaffold[ J]. Biomaterials, 2003, 24: 2773-2778.

[18] Pluta M., Galeski A., Alexandre M., . Polylactide/Montmorillonite Nanocomposites and Microcomposites Prepared by Melt Blending: Structure and Some Physical Properties[J]. J.Appl.Polm.Sci., 2002, 86: 1497-1506.

[19] Chen G. X., Kim H. S., Shim J. H., . Role of Epoxy Groups on Clay Surface in the Improvement of Morphology of Poly(L-lactide)/Clay Composites [J]. Macromolecules, 2005, 38: 3738-3744.

[20] Paul M. A., Alexandre M., Degée P., . Exfoliated Polylactide/Clay Nanocomposites by In-Situ Coordination-Insertion Polymerization [J]. Macromol. Rapid Commun., 2003, 24: 561-566.

[21] Wan Y., Wu H., Yu A., . Biodegradable Polylactide/Chitosan Blend Membranes[J]. Biomacromolecules, 2006, 7: 1362-1372.

[22] Yu J., Cui G., Wei M., . Facile Exfoliation of Rectorite Nanoplatelets in Soy Protein Matrix and Reinforced Bionano-composites Thereof [J]. J. Appl. Polym. Sci., 2007, 104: 3367-3377.

[23] Yu J., Ai F., Dufresne A., . Structure and Mechanical Properties of Poly(lactic acid) Filled with (Starch nanocrystal)-graft-poly (ε-caprolactone) [J]. Macromol. Mater. Eng., 2008, 293: 763-770.