Preparation and characterization of nanocomposite MgFe₂O₄/SiO₂

Abstract

Nanocomposites MgFe₂O₄/SiO₂ were successfully synthesized by the sol-gel method in the presence of N, N-dimethylformamide (DMF). The formation of pure MgFe₂O₄ was confirmed by powder X-ray diffraction (XRD) and electron diffraction. The structural evolution of MgFe₂O₄ nanocrystals was followed by powder X-ray diffraction and IR absorption spectroscopy. The formation of spinel structure of MgFe₂O₄ started at 800 °C, and completed at 900 °C. The transmission electron microscopy (TEM) measurements suggest that the particle sizes increase with the increasing annealing temperature, and the mean particle sizes of the spherical samples annealed at 800 °C, 900 °C and 1 050 °C are ca. 3 nm, 8 nm and 11 nm, respectively. Magnetization measurements at room temperature and 78 K indicate superparamagnetic nature of these MgFe₂O₄ nanocrystals.

Keywords

nanocomposite / sol-gel / magnesium ferrite / magnetic property

References

[1] Leslie-Pelecky D. L., Rieke R. D. Magnetic Properties of Nanostructured Materials[J]. Chem. Mater., 1996, 8(8): 1 770-1 783.

[2] Huang X. H., Chen Z. H. Synthesis of Nanocomposites of Nickel Ferrite Dispersed in Silica Matrix[J]. Guisuanyan Xuebao (J. Chin. Ceramic Soc.), 2004, 32(9): 1 115-1 120.

[3] Silva J. B., Mohallem N. D. S. Preparation of Composites of Nickel Ferrites Dispersed in Silica Matrix[J]. J. Magn. Magn. Mater., 2001, 226: 1 393-1 396.

[4] Li L., Li G. R., Smith L., . Microstructural Evolution and Magnetic Properties of NiFe₂O₄ Nanocrystals Dispersed in Amorphous Silica[J]. Chem. Mater., 2000, 12: 3 705-3 714.

[5] Hutlova A., Niznansky D., Plocek J., . Nanocomposites NiFe₂O₄/SiO₂ and CoFe₂O₄/ SiO₂-preparation by Sol-gel Method and Physical Properties[J]. J. Sol-gel. Sci. Tech., 2003, 26: 473-477.

[6] Rajić N., Čeh M., Gabrovšek R., . Formation of. Nanocrystalline Transition-metal Ferrites inside a Silica Matrix[J]. J. Am. Ceram. Soc., 2002, 85: 1 719-1 724.

[7] Zhou Z. H., Xue J. M., Chan H. S. O., . Transparent Magnetic Composites of ZnFeO Nanoparticles in Silica[J]. J. Apply. Phys., 2001, 90: 4 169-4 174.

[8] Zhou Z. H., Wang J., Xue J. M., . Nanohybrids of Non-stoichiometric Zinc Ferrite in Amorphous Silica[J]. J. Mater. Chem., 2001, 11: 3 110-3 115.

[9] Plocek J., Hutlova A., Niznansky D., . Preparation of ZnFe₂O₄/SiO₂ and CdFe₂O₄/SiO₂ Nanocomposites by Sol-gel Method[J]. J. Non-Cryst. Solids, 2003, 315: 70-76.

[10] Li H. B., Chen J. Y., Liu M., . Preparation and Characterization of CoFe₂O₄/SiO₂ Nano-composites[J]. Gaodeng Xuexiao Huaxue Xuebao (Chemical Journal of Chinese Universities), 2007, 28(4): 614-616.

[11] Cannas C., Musinu A., Peddis D., . Synthesis and Characterization of CoFe₂O₄ Nanoparticles Dispersed in a Silica Matrix by a Sol-gel Autocombustion Method[J]. Chem. Mater., 2006, 18(16): 3 835-3 842.

[12] Hutlova A., Niznansky D., Rehspringer J. L., . High Coercive Field for Nanoparticules of CoFe₂O₄ in Amorphous Silica Sol-gel[J]. Adv. Mater., 2003, 15: 1 622-1 625.

[13] Huang X. H., Chen Z. H. Sol-gel Preparation and Characterization of CoFe₂O₄-SiO₂ Nanocomposites[J]. Solid State Commun., 2004, 132(12): 845-850.

[14] Ennas G., Casula M. F., Falqui A., . Non-stoichiometric CoFe₂O₄ Nanoparticles Supported on an Amorphous Silica Matrix[J]. J. Sol-gel Sci. Tech., 2003, 26(1–3): 463-466.

[15] Ponce-Castaneda S., Martinez J. R., Sanchez S. A. P., . Formation of Nickel-Zinc Ferrite Embedded in a SilicaXerogel Matrix[J]. J. Sol-gel Sci. Tech., 2002, 25: 37-41.

[16] Mandal K., Mandal S. P., Agudo P., . A Study of Nanocrystalline (Mn-Zn) Ferrite in SiO₂ Matrix[J]. App. Surf. Sci., 2001, 182: 386-389.

[17] Ennas G., Musinu A., Piccaluga G., . Characterization of Iron-oxide Nanoparticles in a Fe₂O₃-SiO₂ Composite Prepared by a Sol-gel Method[J]. Chem. Mater., 1998, 10(2): 495-502.

[18] Cannas C., Gatteschi D., Musinu A., . Structural and Magnetic Properties of Fe₂O₃-SiO₂ Nanoparticles Dispersed over a Silica Matrix[J]. J. Phys. Chem. B, 1998, 102: 7 721-7 726.

[19] Monte F., Morales M. P., Levy D., . Formation of γ-Fe₂O₃ Isolated Nanoparticles in a Silica Matrix[J]. Langmuir, 1997, 13: 3 627-3 634.

[20] Moreno E. M., Zayat M., Morales M. P., . Preparation of Narrow Size Distribution Superparamagnetic γ-Fe₂O₃ Nanoparticles in a Sol-gel Transparent SiO₂ Matrix[J]. Langmuir, 2002, 18: 4 972-4 978.

[21] Guerrero H., Rosa G., Morales M. P., . Faraday Rotation in Magnetic γ-Fe₂O₃/SiO₂ Nanocomposites[J]. Appl. Phys. Lett., 1997, 71: 2 698-2 700.

[22] Liu X., Ding J., Wang J. An α-Fe₂O₃ Powder of Nanosized Particles via Precursor Dispersion[J]. J. Mater. Res., 1999, 14(8): 3 355-3 362.

[23] Niznansky D., Viart N., Rehspringer R. J. Nanocomposites Fe₂O₃/SiO₂-preparation by Sol-gel Method and Physical Properties[J]. J. Sol-gel Sci. Tech., 1997, 8: 615-618.

[24] Nogami M. A. Preparation of γ-Fe₂O₃-containing Silica Glasses by the Sol-gel Process[J]. J. Mater. Sci. Lett., 1993, 12(21): 1 705-1 707.

[25] Ulrich D. R. Prospects of Sol-gel Progresses[J]. J. Non-Cryst. Solids, 1988, 100: 174-193.

[26] Rao A. V., Wagh P. B., Haranath D., . Influence of Temperature on the Physical Properties of TEOS Silica Xerogels[ J]. Ceram. Int., 1999, 25(6): 505-509.

[27] Efimov A. M. Quantitative IR Spectroscopy: Applications to Studying Glass Structure and Properties[J]. J. Non-Cryst. Solids, 1996, 203: 1-11.

[28] Bruni S., Cariati F., Casu M., . IR and NMR Study of Nanoparticle-support Interactions a Fe₂O₃-SiO₂ Nanocomposite Prepared by a Sol-gel Method[J]. Nanostruct. Mater., 1999, 11(5): 573-586.

[29] Feltin N., Pileni M. P. New Technique for Synthesizing Iron Ferrite Magnetic Nanosized Particles[J]. Langmuir, 1997, 13: 3 927-3 933.