Controlling growth of ZnO nanostructures via a solution route

Abstract

A solution method was developed for fabricating ZnO nanostructures using (NH₄)₂CO₃ as starting material. SEM analysis shows that ZnO nanostructures exhibit nanorod, branch and flower-like morphologies. The crystal phase of as-synthesized products was characterized by X-ray diffraction (XRD). The growth process, formation mechanism and optical property were also discussed by means of transmission electronic microscopy (TEM), high resolution transmission microscopy (HRTEM) and photoluminescence (PL). The growth direction of ZnO nanostructures was investigated based on the results of HRTEM. The PL spectrum shows two strong peaks (centered at around ∼387 and ∼470 nm) and a broad peak (centered at around ∼580 nm).

Keywords

ZnO nanostructures / pH / solvent / luminescence property

References

[1] Gudiksen M. S., Lauhon L. J., Wang J., . Growth of Nanowire Superlattice Structures for Nanoscale Photonics and Electronics[J]. Nature (London), 2002, 415: 617-620.

[2] Huang M. H., Maom S., Feick H., . Room-Temperature Ultraviolet Nanowire Nanolasers[J]. Science, 2001, 292: 1897-1899.

[3] Pan Z. W., Dai Z. R., Wang Z. L. Nanobelts of Semiconducting Oxides[J]. Science, 2001, 291: 1947-1949.

[4] Sun Y. G., Gates B., Mayers B., . Crystalline Silver Nanowires by Soft Solution Processing[J]. Nano Lett., 2002, 2: 165-168.

[5] Service R. F. Will UV Lasers Beat the Blue[J]. Science., 1997, 276: 895-897.

[6] Zamfirescu M., Kavokin A., Gil B., . ZnO as A Material Mostly Adapted for the Realization of Room-temperature Polariton Lasers[J]. Phys. Rev. B., 2002, 65: 161205-161208.

[7] Wu J. J., Liu S. C. Low-Temperature Growth of Well-Aligned ZnO Nanorods by Chemical Vapor Deposition[J]. Adv. Mater., 2002, 14: 215-218.

[8] Park W., Yi G. C., Kim M., . Quantum Confinement Observed in ZnO/ZnMgO Nanorod Heterostructures[J]. Adv. Mater., 2003, 13: 351-354.

[9] Kong Y. C., Yu D. P., Zhang B., . Ultraviolet-emitting ZnO Nanowires Synthesized by a Physical Vapor Deposition[J]. Appl. Phys. Lett., 2001, 78: 407-409.

[10] Guo L., Ji Y. L., Xu H. B., . Regularly Shaped, Single-Crystalline ZnO Nanorods with Wurtzite Structure[J]. J. Am. Chem. Soc., 2002, 124: 14864-14865.

[11] Xing Y. J., Xi Z. H., Xue Z. Q., . Optical Properties of the ZnO Nanotubes Synthesized Via Vapor Phase Growth[J]. Appl. Phys. Lett., 2003, 83: 1689-1691.

[12] Gao P. X., Wang Z. L. Mesoporous Polyhedral Cages and Shells Formed by Textured Self-Assembly of ZnO Nanocrystals[J]. J. Am. Chem. Soc., 2003, 125: 11299-11305.

[13] Yan Y. F., Liu P., Wen J. G., . In-Situ Formation of ZnO Nanobelts and Metallic Zn Nanobelts and Nanodisks[J]. J. Phys. Chem. B, 2003, 107: 9701-9704.

[14] Lao J. Y., Huang J. Y., Wang D. Z., . ZnO Nanobridges and Nanonails[J]. Nano Lett., 2003, 3: 235-238.

[15] Li Q., Kumar V., Li Y., Zhang H., . Fabrication of ZnO Nanorods and Nanotubes in Aqueous Solutions[J]. Chem. Mater., 2005, 17: 1001-1006.

[16] Li G. R., Lu X. H., Zhao W. X., . Controllable Electrochemical Synthesis of Ce⁴⁺-Doped ZnO Nanostructures from Nanotubes to Nanorods and Nanocages[J]. Cryst. Growth Des., 2008, 8: 1276-1281.

[17] Hsu J. W. P., Tian Z. R., Simmons N. C., . Directed Spatial Organization of Zinc Oxide Nanorods[J]. Nano Lett., 2005, 5: 83-86.

[18] Liu B., Zeng H. C. Hydrothermal Synthesis of ZnO Nanorods in the Diameter Regime of 50 nm[J]. J. Am. Chem. Soc., 2003, 125: 4430-443.

[19] Shen L., Bao N., Yanagisawa K., . Controlled Synthesis and Assembly of Nanostructured ZnO Architectures by a Solvothermal Soft Chemistry Process[J]. Cryst. Growth Des., 2007, 7: 2742-2748.

[20] Tian Z. R., Voigt J. A., Liu J., . Complex and Oriented ZnO Nanostructures[J]. Nature Materials, 2003, 2: 821-826.

[21] Zhang J., Sun L. D., Yin J. L., . Control of ZnO Morphology Via a Simple Solution Route[J]. Chem. Mater., 2002, 14: 4172-4177.

[22] Zhang H., Yang D. R., Ji Y. J., . Low Temperature Synthesis of Flowerlike ZnO Nanostructures by Cetyltrimethylammonium Bromide-Assisted Hydrothermal Process[J]. J. Phys. Chem. B, 2004, 108: 3955-3958.

[23] Kiely C. J., Fink J., Brust M., . Spontaneous Ordering of Bimodal Ensembles of Nanoscopic Gold Clusters[J]. Nature, 1998, 396: 444-446.

[24] Shevchenko E. V., Talapin D. V., Kotov N. A., . Structural Diversity in Binary Nanoparticle Superlattices[J]. Nature, 2006, 439: 55-59.

[25] Noskov S. Y., Lamoureux G., Roux B. J. Molecular Dynamics Study of Hydration in Ethanol-Water Mixtures Using a Polarizable Force Field[J]. Phys. Chem. B, 2005, 109: 6705-6713.

[26] Han L., Luo J., Kariuki N. N., . Novel Interparticle Spatial Properties of Hydrogen-Bonding Mediated Nanoparticle Assembly[J]. J. Chem. Mater., 2003, 15: 29-37.

[27] Yu W. D., Li X. M., Gao X. D. Catalytic Synthesis and Structural Characteristics of High-Quality Tetrapod-Like ZnO Nanocrystals by a Modified Vapor Transport Process[J]. Cryst. Growth Des., 2005, 5: 151-155.

[28] Hsu J. W. P., Tallant D. R., Simpson R. L., . Luminescent Properties of Solution-grown ZnO nanorods[J]. Appl. Phys. Lett., 2006, 88: 252103-252105.

[29] Vanheusden K., Warren W. L., Seager C. H., . Mechanisms behind Green Photoluminescence in ZnO Phosphor Powders[J]. J. Appl. Phys., 1996, 79: 7983-7990.

[30] Chen J., Feng Z. C., Ying P. L., . Laser-induced Luminescence Spectroscopy of ZnO/SiO₂[J]. Phys. Chem. Chem. Phys., 2004, 6: 2074-2077.

[31] Huang M. H., Feick Y. Y., Tran N., . Catalytic Growth of ZnO Nanowire by Vapor Transport [J]. Adv. Mater., 2001, 13: 113-116.

[32] Fu Z., Lin B., Liao G., Wu Z. The Effect of Zn Buffer Layer on Growth and Luminescence of ZnO Films Deposited on Si Substrates[J]. J. Cryst. Growth, 1998, 193: 316-321.

[33] Du G H, Xu F, Yuan Z Y, Tendeloo G V Flowerlike ZnO Nanocones and Nanowires: Preparation, Structure, and Luminescence[J]. Appl. Phys. Lett., 2006, 88: 243101 1-243101.3

[34] Zhang D. H., Xue Z. Y., Wang Q. P. The Mechanisms of Blue Emission from ZnO Films Deposited on Glass Substrate by r.f. Magnetron Sputtering[J]. J. Phys. D: Appl. Phys., 2002, 35: 2837-2840.