Morphology difference between the alkali activated cement and portland cement paste on multi-scale

Abstract

The features of alkali activated slag(AAS) and portland cement (PC) were observed on multi-scale, the crack and fracture sections were observed with naked eyes, and SEM and AFM were used to study the structure morphology differences between PC and AAS on micrometer to nano meter scale. The experimental results indicated that the AAS paste had soil like fracture texture and it was composed of mainly C-S-H gel but lacks of crystals, and it had a very strong tendency to shrink and crack. AAS paste is much denser and more homogeneous than PC, and on the nano scale C-S-H nano particle in the AAS paste is much smaller and packs much denser than PC paste.

Keywords

morphology / alkali activated cement / portland cement / multi-scale / nano particle

References

[1] Davidovits J. Ancient and Modern Concretes: What is the Real Difference? [J]. Concrete International, 1987, 29(12): 23-35.

[2] Roy D. M. Alkali-activated Cements: Opportunities and Challenges [J]. Cement and Concrete Research, 1999, 29(2): 249-254.

[3] Wang S., Pu X., Scrivener K. L., Pratt P. L. Alkali-activated Slag Cement and Concrete: A Reviewer of Properties and Problem [J]. Advance in Cement Research, 1995, 27(7): 93-102.

[4] Roy D. M., Idorn G. M. Hydration, Structure, and Properties of Blast Furnace Slag Cements, Mortars, and Concrete [J]. ACI Material Journal., 1982, 79(12): 444-457.

[5] Krizana D. Branislav Zivanovic Effects of Dosage and Modulus of Water Glass on Early Hydration of Alkali-Slag Cements [J]. Cement and Concrete Research, 2002, 32(9): 1181-1188.

[6] Glukhovsky V., Zaitsev Y., Pakhomow V., . Slag-alkali Cement and Concrete: Structure, Properties and Technological and Economical Aspects of Use[J]. Silic Ind., 1983, 48(10): 197-200.

[7] Brough A. R., Atkinson A. Sodium Silicate-Based, Alkali-Activated Slag Mortars Part I. Strength, Hydration and Microstructure [J]. Cement and Concrete Research, 2002, 32(5): 865-879.

[8] Shi C., Day R. L. Some Factors Affecting Early Hydration of Alkali-Slag Cements[J]. Cement and Concrete Research, 1996, 26(3): 439-447.

[9] Collins F., Sanjayan J. G. Microcracking and Strength Development of Alkali Activated Slag Concrete[J]. Cement and Concrete Composites, 1993, 23(2): 345-352.

[10] Wang S. D., Scrivener K. L., Pratt P. L. Factors Affecting the Strength of Alkali-Activated Slag [J]. Cement and Concrete Research, 1994, 24(6): 1033-1043.

[11] Wang S., Scrivener K. L. Hydration Products of Alkali-Activated Slag Cement[J]. Cement and Concrete Research, 1995, 25(3): 561-571.

[12] Collins F., Sanjayan J. G. Cracking Tendency of Alkali-Activated Slag Concrete Subjected to Restrained Shrinkage[J]. Cement and Concrete Research, 2000, 30(4): 791-798.

[13] Collinsa F., Sanjayan J. G. Effect of Pore Size Distribution on Drying Shrinkage of Alkali-Activated Slag Concrete[J]. Cement and Concrete Research, 2000, 30(10): 1401-1406.

[14] Jennings H. M. Colloid Model of C-S-H and Implication to the Problem of Creep and Shrinkage[J]. Material and Structure / Concrete and Engineering, 2004, 37(1): 59-70.

[15] Atis C. D., Kilic A., Sevim U. K. Strength and Shrinkage Properties of Mortar Containing a Nonstandard High-calcium Fly ash[J]. Cement and Concrete Research, 2004, 34(1): 99-102.

[16] Taylor H. F. W. Nano Scale Microstructure of C-S-H: Current Status [J]. Advance Cement Material, 1993, 1: 38-46.

[17] Jennings H. M. Colloid Model of C-S-H and Implications to the Problem of Creep and Shrinkage[J]. Concrete Science and Engineering, 2004, 37(1): 59-70.

[18] Allen A. J., Thomas J. J., Jennings H. b. M. Composition and Density of Nano Scale Calcium Silicate Hydrate in Cement[ J]. Nature Materials, 2007, 6(2): 311-316.

[19] Ulm F.-J., Vandamme M., Bobko C., . Statistical Indentation Techniques for Hydrated Nanocomposites: Concrete, Bone, and Shale [J]. J. Am. Ceram. Soc., 2007, 90(9): 2677-2692.

[20] Nonat A. The Structure and Stoichiometry of C-S-H [J]. Cement and Concrete Research, 2004, 34(6): 1521-1528.

[21] Shen W., Xiao L., Ma W., . Investigation on Nano-scale Microstructure of C-S-H with Atomic Force Microscopy[J]. Jounal of The Chinese Ceramic Society, 2008, 36(4): 487-493.