Long-term durability of cement-based materials with very low w/b

Abstract

To investigate the durability, especially the long-term stability of cement-based materials with very low w/b, the air permeability test, carbonation test, capillary absorption rate test and dilation potential test were adopted under long-term heat treatment condition. Microstructure of these materials is also analyzed by scanning electronic microscopy (SEM) and mercury intrusion porosimeter (MIP) in order to further unveil its mechanism and interrelation between microstructure and its properties. The results indicate that in the area investigated, cement-based material with w/b 0.17, like RPC, possesses low porosity and excellent durability. Moreover, its porosity will further decrease under long-term heat treatment compared with normal heat treatment. Its long-term durability is much superior to that of other cement-based materials with w/b 0.25 or 0.35 as high strength concrete(HSC).

Keywords

cement-based material / durability / dilatability potential / air permeability / carbonation / capillary absorption

References

[1] Mangat P. S., Limbachiya M. K. Repair Material Properties Which Influence Long-term Performance of Concrete Structures[J]. Construction and Building Materials, 1995, 9(2): 81-90.

[2] Xu Z. Z., Tang M. S., Beaudoin J. J. Relationship between Composition, Structure and Mechanical Properties of Very Low Porosity Cementitious Systems[J]. Cement and Concrete Research, 1993, 23(1): 187-190.

[3] Sherman N., Beretka J., Santoro L., . Long-term Behavior of Hydraulic Binders Based on Calcium Sulfoaluminate and Calcium Sulfosilicate[J]. Cement and Concrete Research, 1995, 25(1): 113-126.

[4] Bangert F., Grasberger S., Kuhl D., . Environmentally Induced Deterioration of Concrete: Physical Motivation and Numerical Modeling[J]. Engineering Fracture Mechanics, 2003, 70: 891-910.

[5] Taylor H. F. W., Famy C., Scrivener K. L. Delayed Ettringite Formation[J]. Cement and Concrete Research, 2001, 31(4): 683-693.

[6] Marcel Cheyrezy. Structural Applications of RPC[J]. Concrete International, 1999, (1): 20–23

[7] Richard P., Cheyrezy M. Composition of Reactive Powder Concrete[J]. Cement and Concrete Research, 1995, 25(7): 1 501-1 511.

[8] Pierre Richard. Reactive Powder Concrete: A New Ultra-High Strength Cementitious Material[C]. In: The 4th International Symposium on Utilization of High Strength/high Performance concrete. Paris, 1996:1 343–1 349

[9] Feng N. Q. High Strength Concrete: Microstructure Character and Problem of Durability, Durability of High Performance Concrete[M], 1998. Beijing: Science press. 9-17.

[10] Xu Z. Z., Tang M. S. Study the Related Question of T. C. Powers[J]. China Ceramic Society, 1991, 19(2): 104-110.

[11] Feng N. Q. Is the Durability of High Performance Concrete with w/b≤0.30 Poor, Durability of High Performance Concrete[M], 1998. Beijing: Science Press. 40-43.

[12] Igarashi S. I., Hiroshi R. K., Kawamura M. Longterm Volume Changes and Microcracks Formation in High Strength Mortars[J]. Cement and Concrete Research, 2000, 30(6): 943-950.

[13] Durekovic A. Cement Pastes of Low Water to Solid Ratio: An Investigation of the Porosity Characteristics under the Influence of A Superplasticizer and Silica Fume[J]. Cement and Concrete Research, 1995, 25(2): 365-375.