Microstructral evolution of well-aligned ZnO nanorods array films in aqueous solution

Abstract

By means of scanning electron microscopope and X-ray diffraction, microstructural evolution of well-aligned ZnO nanorod array films was studied. The films were prepared on a glass using direct deposition method in an aqueous solution. The experimental results show that the highly oriented rods grew from the randomly oriented crystals. Those rod-like randomly oriented crystals began to impinge on other neighboring crystals and their growth became physically limited; only the rods perpendicular to the substrate were allowed to grow freely. This kinetically controlled nucleation and growth would be responsible for producing the uniformly oriented nanorods. During the ZnO rods’ growth, the topology of their top faces changed from flat, prismatic to finally flat.

Keywords

nanostructure / scanning electron microscopy (SEM) / compound semiconductors / ZnO / thin films

References

[1] Wang Z. L. Zinc Oxide Nanostructures: Growth, Properties and Applications[J]. J. Physics Condensed Matter., 2004, 16: R829-R858.

[2] Huang M. H., Mao S., Feick H., . Room-temperature Ultraviolet Nanowire Nanolasers[J]. Science, 2001, 292: 1897-1899.

[3] Pearton S. J., Norton D. P., Ip K., . Recent Advances in Processing of ZnO[J]. J. Vac. Sci. Techol., B, 2004, 22(3): 932-946.

[4] Wu J., Liu S. C. Low-temperature Growth of Well-alligned ZnO Nanorods by Chemical Vapor Deposition[J]. Adv Mater., 2002, 14: 215-218.

[5] Wessler B., Steinecker A., Mader W. Epitaxial Growth of ZnO. Thin Films on ScAlMgO4 (0001) by Chemical Solution Deposition[J]. J. Cryst. Growth, 2002, 242: 283-292.

[6] Liu C., Masuda Y., Wu Y., . A Simple Route for Growing Thin Films of Uniform ZnO Nanorod Arrays on Functionalized Si Surfaces. Thin Solid Films, 2006, 503: 110-114.

[7] Vayssieres L. Growth of Arrayed Nanorods and Nanowires of ZnO from Aqueous Solutions[J]. Adv. Mater., 2003, 15: 464-466.

[8] Saito N., Haneda H., Seo W. S., . Low-temperature Fabrication of Light-Emitting Zinc Oxide Micropatterns Using Self-Assembled Monolayers[J]. Langmuir., 2001, 17: 1461-1463.

[9] Muthukumar S., Gorla C. R., Emanetoglu N. W., . Control of Morphology and Orientation of ZnO Thin Films Grown on SiO2/ Si Substrates[J]. J. Cryst. Growth, 2001, 225: 197-201.

[10] Yamabi S., Imai H. Growth Conditions for Wurtzite Znic Oxide Films in Aqueous Solutions[J]. J. Mater. Chem., 2002, 12: 3773-3778.

[11] Nishizawa H., Yuasa K. Preparation of Highly Oriented ZnO Thin Film under Hydrothermal Conditions[J]. J. Mater. Sci. Lett., 1998, 17: 985-987.

[12] Liu S.-C., Wu J.-J. Low-Temperature and Catalyst-Free Synthesis of Well-Aligned ZnO Nanorods on Si (100) [J]. J. Mater. Chem., 2002, 12: 3125-3129.

[13] Li W. J., Shi E. W., Zhong W. Z., . Growth Mechanism and Growth Habit of Oxide Crystals[J]. J. Cryst. Growth, 1999, 203: 186-196.

[14] Hartman P., Perdok W. G. On the Telations between Structure and Morphology of Crystals[J]. Acta Cryst., 1955, 8: 49-55.

[15] Hartman P., Perdok W. G. On the Relations between Structure and Morphology of Crystals II [J]. Acta Cryst., 1955, 8: 525-531.