Highly oriented ZnO rod arrays on Si substrates from aqueous solution

Abstract

Ordered zinc oxide (ZnO) rod arrays with very high orientation were fabricated on Si substrates by using a solution method. The substrate surfaces were functionalized by Self-Assembly Monolayers (SAMs). In the very early growth stage, the oriented ZnO crystals had already grown, which appeared to be the main reason why ZnO nanorods showed very high orientation. The un-dense and un-uniform SAMs provided a surface that was heterogeneous to ZnO nucleation. Consequently, highly oriented ZnO rods were selectively grown on the “coin-like” SAM-uncovered regions. The route developed here can provide some helpful information to control the nucleation and orientation of ZnO in aqueous solution. Also, the site-selective growth mechanisms can indicate a clue to grow patterned highly oriented ZnO nanorod arrays by the organic template.

Keywords

zinc oxide (ZnO) / self assembly monolayers (SAMs) / crystal growth / nanostructures / site-selective growth / solution method

References

[1] Wang Z. L. Zinc Oxide Nanostructures: Growth, Properties and Applications[J]. J. Physics: Condensed Matter., 2004, 16: 829-858.

[2] Tian Z. R., Voigt J. A., Liu J. Complex and Oriented ZnO Nanostructures[J]. Nature materials, 2003, 2: 821-826.

[3] Huang M. H., Mao S., Feick H. Room-temperature Ultraviolet Nanowire Nanolasers[J]. Science, 2001, 292: 1 897-1 899.

[4] Beermann N., Vayssieres L., Lindquist S. E,. Photoelectrochemical Studies of Oriented Nanorod Thin Films of Hematite[J]. J. Electrochem. Soc., 2000, 147: 2 456-2 461.

[5] Wu J., Liu S. Low-temperature Growth of Well-alligned ZnO Nanorods by Chemical Vapor Deposition[J]. Adv. Mater., 2002, 14: 215-218.

[6] Petrella A. J., Deng H., Roberts N. K,. Single-source Chemical Vapor Deposition Growth of ZnO Thin Films Using Zn₄O(CO₂NEt₂)₆[J]. Chem. Mater., 2002, 14: 4 339-4 342.

[7] Park W. I., Kim D. H., Jung S. W,. Metalorganic Vapor-phase Epitaxial Growth of Vertically Well-aligned ZnO Nanorods[J]. Appl. Phys. Lett., 2002, 80: 4 232-4 234.

[8] Pauporte T., Cortes R., Froment M. Electrocrystallization of Epitaxial Zinc Oxide onto Gallium Nitride[J]. Chem. Mater., 2002, 14: 4 702-4 708.

[9] Ohyama M., Kozuka H., Yoko T. Sol-gel Preparation of ZnO Films with Extremely Preferred Orientation along (002) Plane from Zinc Acetate Solution[J]. Thin solid films, 1997, 306: 78-85.

[10] Liu C. S., Li Z. W., Gao Y. F,. Microstructural Evolution of Well-aligned ZnO Nanorods Array Films in Aqueous Solution[J]. J. Wuhan Univ. Tech.-Mater. Sci. Ed, 2007, 22(4): 603-606.

[11] Vayssieres L. Growth of Arrayed Nanorods and Nanowires of ZnO from Aqueous Solutions[J]. Adv. Mater., 2003, 15: 464-466.

[12] Liu C., Zapien J. A., Yao Y. High-density, Ordered Ultraviolet Light-emitting ZnO Nanowire Arrays[J]. Adv. Mater., 2003, 15: 838-841.

[13] Park W. I., Yi G. C., Jang H. M. Metalorganic Vapor-phase Epitaxial Growth and Photoluminescent Properties of Zn₁-_xMg_xO (0≤x≤0.49) Thin Films[J]. Appl. Phys. Lett., 2001, 79: 2 022-2 024.

[14] Chen Y. F., Hong S. K., Ko H. J,. Plasma-assisted Molecularbeam Epitaxy of ZnO Epilayers on Atomically Flat MgAl₂O₄ (111) Substrates[J]. Appl. Phys. Lett., 2000, 76: 245-247.

[15] Matsubara K., Fons P., Yamada A. Epitaxial Growth of ZnO Thin Films on LiNbO₃ Substrates[J]. Thin Solid Films, 1998, 347: 238-240.

[16] Wessler B, Steinecker A, Mader W. Epitaxial Growth of ZnO Thin Films on ScAlMgO₄ (0 001) by Chemical Solution Deposition[J]. J. Crys. Growth, 2002, 242, 283

[17] Liu C. S., Masuda Y., Wu Y. A Simple Route for Growing Thin Films of Uniform ZnO Nanorod Arrays on Functionalized i Surfaces[J]. Thin Solid Films, 2006, 503: 110-114.

[18] Sugimura H., Hozumi A., Kameyama T. Organosilane Self-assembled Monolayers Formed at the Vapour/Solid Interface[J]. Surface & Interface Analysis, 2002, 34: 550-554.