Preparation of superfine-cemented carbide by spark plasma sintering

Xie Yingfang; Wang Xingqing; Chen Lidong; Li Xiaodong; Guo Hailiang

doi:10.1007/BF02861467

Journal of Wuhan University of Technology Materials Science Edition ›› 2006, Vol. 21 ›› Issue (1) : 42 -45. DOI: 10.1007/BF02861467

Article

Preparation of superfine-cemented carbide by spark plasma sintering

Author information +

History +

PDF

Abstract

92WC-8 Co powder mixture with superfine-tungsten carbide was respectively sintered by spark plasma sintering(SPS) and sintering isostatic pressure (SIP). Complete dense samples with 200 nm WC grains and 94.2 HRA hardness were prepared by spark plasma sintering at 1 150 °C and under 4.5 kN for 5 minutes. SIP was carried out at 1 400 °C for 30 minutes with a result of 300–400 nm WC grains and 93 HRA hardness. The results show that sintering temperature is greatly decreased by SPS, sintering time is largely shortened and WC grain growth is effectively retarded. Micropores and drawbacks in superfine-cemented carbide made by SPS are greatly declined, which is very useful to improving mechanical properties.

Keywords

spark plasma sintering / cemented carbide / superfine grain / sintering mechanism

Cite this article

Download citation ▾

Xie Yingfang, Wang Xingqing, Chen Lidong, Li Xiaodong, Guo Hailiang. Preparation of superfine-cemented carbide by spark plasma sintering. Journal of Wuhan University of Technology Materials Science Edition, 2006, 21(1): 42-45 DOI:10.1007/BF02861467

登录浏览全文

4963

注册一个新账户忘记密码

References

Publishing order | Descend order by publishing year | Descend order by cited within

[1]	She Zhen-hui. The Development of Sintering Technique of Cemented Carbide. Cemented Carbide, 1998, 15(1): 49-53.

[2]	Zhang Dong-ming, Fu Zheng-yi. Mechanism and Application of Spark Plasma Sintering Technology. Journal of Wuhan University of Technology-Mater. Sci. Ed., 1999, 21(6): 15-17.

[3]	Luo Xi-yu. Current Progress of Materials Produced by Spark Plasma Sintering. Powder Metallurgy Industry, 2001, 11(6): 7-16.

[4]	Zhang Jiu-xing, Liu Ke-gao, . The Development and Application of Spark Plasma Sintering. Powder Metallurgy Technology, 2002, 20(3): 129-134.

[5]	Zhang Dong-ming, Fu Zheng-yi, . Equivalent Resistance in Pulse Electric Current Sintering. Wuhan Univ. Tech.-Mat. Sci. Ed., 2002, 17(2): 30-32.

[6]	Fu Zheng-yi, Pang Ting-ting. Effect of Heating Rate on Spark Plasma Sintering TiB₂ Ceramic. Chinese Journal of Materials Research, 2001, 15(4): 484-486.

[7]	Seung I Cha, Soon H Hong, Byung K Kim. Spark Plasma Sintering Behavior of Superfinecrystalline WC-10Co Cemented Carbide Powders. Materials Science and Engineering, 2003, A351: 31-38.

[8]	Jing Shang-jie. New Metal Processing, 1978 Tokyo: The Institute of Process Technology of Wei Ta, Japan.

[9]	Hong H, Cha I. The Collect of Spark Plasma Sintering (SPS) Basing Lecture in 2000, 2000 Tokyo: The Japanese Institute of Spark Plasma Sintering, Japan. B31-B31.

[10]	Li Guo-hua, Huang Zhi-chu, . Specific Property of Ultrafine Particle Classification. Wuhan Univ. Tech. -Mat. Sci. Ed., 2003, 18(2): 82-84.

[11]	Han Feng-lin. Metal Directory, Edition 7, 1994 Beijing: Chinese Mechanical Press.

[12]	Li Wei, Gao Lian, . Fabrication of Superfine 3Y-TZP by Spark Plasma Sintering. Journal of Inorganic Materials, 1999, 14(6): 985-988.

[13]	Liu Jun-fang, Fu Zheng-yi, . Aliminum Nitride Ceramics Consolidated by Spark Plasma Sintering. Journal of Ceramics, 2001, 22(3): 157-160.

[14]	Gao Lian, Hong Jin-sheng. Superfast Densification of Oxide Cermaics by Spark Plasma Sintering. Journal of Inorganic Materials, 1998, 13(1): 18-22.