Pore size distribution of high performance metakaolin concrete

Abstract

The Compressive strength, porosity and pore size distribution of high performance metakaolin (MK) concrete were investigated. Concretes containing 0.5%, 10% and 20% metakaolin were prepared at a water/cementitious material ratio (W/C) of 0.30. In parallel, concrete mixtures with the replacement of cement by 20% fly ash or 5 and 10% silica fume were prepared for comparison. The specimens were cured in water at 27°C for 3 to 90 days. The results show that at the early age of curing (3 days and 7 days), metakaolin replacements increase the compressive strength but silica fume replacement slightly reduces the compressive strength. At the age of and after 28 days, the compressive strength of the concrete with metakaolin and silica fume replacement increases. A strong reduction in the total porosity and average pore diameter were observed in the concrete with MK 20% and 10% in the first 7 days.

Keywords

high performance concrete / metakaolin / pore size distribution

References

[1] Massazza F, Oberti G. Malhotra V. M.. Durability of Pozzolanic Cements and Italian Experience in Mass Concrete. 2nd Inter Conference on Durability and Concrete, 1991, Montreal, Canada: American Concrete Institute, 1259-1283.

[2] Gjorv O. Malhotra V. M.. High Strength Concrete. Advances in Concrete Technology, 1992, Montreal, Canada: American Concrete Institute, 21-77.

[3] Bredy P, Chabannet M, Pera J. Microstructure and Porosity of Metakaolin Blended Cements. Mat Res Soc Symp proc., 1989, 137: 431-436.

[4] De Silva P S, Glasser F P. Pozzolanic Activation of Metakaolin. Adv. Cem. Res., 1992, 4(16): 167-178.

[5] Feldman R F, Cheng-yi Huang. Properties of Portland Cementsilica Fume Pastes I. Porosity and Surface Properties. Cem. Concr. Res., 1985, 15(5): 765-774.

[6] Ambroise J, Murat M, Pera J. Hydration Reaction and Hardening of Calcined Clays and Related Minerals. V. Extension of the Research and General Conclusion. Cem. Concr. Res., 1985, 15(2): 261-268.

[7] Murat M. Hydration Reaction and Hardening of Calcined Clays and Related Minerals. I. Preliminary Investigation on Metakaolinite. Cem. Concr. Res., 1983, 13(2): 259-266.

[8] Ambroise J, Maximilien S, Pera J. Properties of Metakaolin Blended Cements. Adv. Cem. Mat. (US), 1994, 1: 161-168.

[9] Kostuch J A, Walters G V, Jones T R. High Performance Concretes Incorporating Metakaolin-a Review.Concrete, 2000, Dundee Conf, 1993, Sept.: 1799–1811

[10] Caldarone M K, Gruber K A, Burg R G. High-reactivity Metakaolin: A New Generation Mineral Admixture. Concr. Int., 1994, 16(11): 37-40.

[11] B B Sabir, S Wild, J Bai. Metakaolin and Calcined Clays as Pozzolans for Concrete: a Review.Cement and Concrete Composites, 2001.

[12] Khatib J M, Wild S. Pore Size Distribution of Metakaolin Pastes. Cem. Concr. Res., 1996, 26(10): 1545-1553.

[13] Frises M, Cabrera J. Pore Size Distribution and Degree of Hydration of Metakaolin-Cement Pastes. Cem. Concr. Res., 2001, 30: 561-569.

[14] Day L, Marsh B K. Measurement of Porosity in blended Cement Pastes. Cem. Concr. Res., 1988, 18: 63-73.

[15] Taylor H F W. Cement Chemistry, 1990, London: Academic Press.

[16] Zhang M H, Malhotra V M. Characteristics of a Thermally Activated Alumino-silicate Pozzolanic Material and Its Use in Concrete. Cem. Concr. Res., 1995, 25(8): 1713-1725.