Effects of austempering on the mechanical properties of the hot rolled Si−Mn TRIP steels

Abstract

The effect of austempering on the mechanical properties of the hot rolled Si−Mn TRIP steels was studied. The mechanism of transformation induced plasticity (TRIP) was discussed through the examination of the microstructure and the mechanical properties of the specimens. The results show that the microstructures of the steels were comprised of polygonal ferrite, granular bainite and a significant amount of stable retained austenite. The specimen exhibits excellent mechanical properties for the TRIP effect. Isothermal holding time for austempering affects the stability of retained austenite. The mechanical properties such as tensile strength, total elongation and strength ductility balance reach their optimal values (776MPa, 33% and 25608 MPa%, respectively) when the specimen is held at 400°C for 25 min.

Keywords

austempering / hot rolling / transformation induced plasticity / mechanical properties

References

[1] Eberle K, Cantinieaux P, Harlet P. New Thermomechanical Strategy for Production of High Strength Low Alloyed Multiphase Steel Showing Transformation Induced Plasticity Effect[J]. Ironmaking and Steelmaking, 1999, 26: 176-181.

[2] Zackay V F, Parker E R, Fahr D, . The Enhancement of Ductility on High-Strength Steels[J]. Tans. ASM, 1967, 60: 252-259.

[3] Sakuma Y, Matsumura O, Takechi H. Mechanical Properties and Retained Austenite in Intercritically Heat-treated Bainite-transformed Steel and Their Variation With Si and Mn Additions[J]. Metall. Trans., 1991, 22A: 489-498.

[4] Ryu H A, Speer J G, Wise J P. Effect of Thermomechanical Processing on the Retained Austenite Content in a Si−Mn Transformation-Induced-Plasticity Steel[J]. Metall. Trans, 2002, 33A: 2 811-2 816.

[5] Hanzaki A Z, Hodgson P D, Yue S. The Influence of Bainite on Retained Austenite Characteristics in Si−Mn TRIP Steels[J]. ISIJ Int., 1995, 35: 79-85.

[6] Pereloma E V, Timokhina I B, Hodgson P D. Transformation Behaviour in Thermomechanically Processed C−Mn−Si TRIP Steels with and without Nb[J]. Mater. Sci. Eng., 1999, 273: 448-452.

[7] Hanzaki A Z, Hodgson P D, Yue S. Hot Deformation Characteristics of Si−Mn TRIP Steels with and without Nb Microalloy Additions[J]. ISIJ Int., 1995, 35: 324-331.

[8] Timokhina I B, Hodgson P D, Pereloma E V. Effect of Deformation Schedule on the Microstructure and Mechanical Properties of a Thermomechanically Processed C−Mn−Si Transformation-Induced Plasticity Steel[J]. Metall. Trans., 2003, 34A: 1 599-1 609.

[9] Basuki A, Aernoudt E. Influence of Rolling of TRIP Steel in the Intercritical Region on the Stability of Retained Austenite [J]. J. Mater. Process. Technol., 1999, 89–90: 37-43.

[10] Hanzaki A Z, Hodgson P D, Yue S. Ferrite Formation Characteristics in Si−Mn TRIP Steels[J]. ISIJ Int., 1997, 37: 583-589.

[11] Haiwen L, Lie Z, Kruijver S O. Effect of Intercritical Deformation on Bainite Formation in Al-containing TRIP Steel[J]. ISIJ Int., 2003, 43: 1 219-1 227.

[12] Mahieu J, Maki J, Cooman B C D. Phase Transformation and Mechanical Properties of Si-Free CMnAl Transformation-Induced Plasticity-Aided Steel [J]. Metall Trans, 2002, 33A: 2 573-2 580.

[13] Stéphane G, Philippe H, Francis D, . Effect of Hot-Rolling Conditions on the Tensile Properties of Multiphase Steels Exhibiting a TRIP Effect[J]. Steel research, 2002, 73: 280-286.

[14] Sugitomo K, Nagasaka A, Kobayashi M, . Effects of Retained Austenite Parameters on Warm Stretch-Flange-Ability in TRIP-Aided Dual Phase Sheet Steels[J]. ISIJ International, 1999, 39(1): 56-63.

[15] Meyer M D, Vanderschueren D, Cooman B C D. The Influence of the Substitution of Si by Al on the Properties of Cold Rolled C−Mn−Si TRIP Steels[J]. ISIJ Int., 1999, 39: 813-822.

[16] Sugimoto K I, Kobayashi M, Hashimoto S I. Ductility and Strain-Induced Transformation in a High-Strength Transformation-Induced Plasticity-Aided Dual-Phase Steel[J]. Metall. Trans., 1992, 23A: 3 085-3 091.