Correlations between the optical properties and the microstructure of TiO₂ thin films prepared by reactive electron-beam evaporation

Abstract

High refractive index TiO₂ thin films were deposited on BK7 glass by reactive electron—beam (REB) evaporation at pressure of 2×10⁻² Pa, deposition rate of 0.2 nm/s and at various substrate temperatures from 120°C to 300°C. The refractive index and the thickness of the films were measured by visible spectroscopic ellipsometry (SE) and determined from transmission spectra. Optical properties and structure features were characterized by UV-VIS, SEM and XRD, respectively. The measurement and analysis on transmission spectra of all samples show that with the substrate temperature increasing from 120°C to 300°C, the refractive indices of thin films increase from 1.7 to 2.1 and the films after heat treatment have higher refractive indices due to its crystallizing. The XRD analysis results indicate that the structure of TiO₂ thin films deposited on BK7 glass at substrate temperatures of 120°C, 200°C and 300°C is amorphous, after post-annealing under air condition at 400°C for 1 hour, the amorphous structure is crystallized, the crystal phase is of 100% anatase with strong preferred orientation (004) and the grain size of crystalline is within 3.6–8.1 nm, which is consistent with results from SEM observation.

Keywords

thin film / titania / XRD / SEM / reactive evaporation

References

[1] Jianhong Wei, Jing Xiao, Xiujian Zhao, . Preparation of Ag−TiO₂ Thin Film by Sol-gel Method. J. Wuhan Univ. of Tech.-Mater. Sci. Ed., 2001, 16(4): 27-30.

[2] Jiaguo Yu, Xiujian Zhao, Gaoke Zhang, . Grain Size and Photocatalytic Activity of Nanometer TiO₂. J. Wuhan Univ. of Tech.-Mater. Sci. Ed., 2001, 16(2): 1-5.

[3] Feng He, Qiantao Li, Wangkai Hu, . Preparation of Nanometer Structured TiO₂ Thin Films by Sol-Gel Meth. J. Wuhan Univ. of Tech.-Mater. Sci. Ed., 2002, 17(4): 20-22.

[4] Wang X H, Xue Y Y, Zhao L, . Optical Thin Films and Its New Status. Journal of Wuhan University of Technology-Mater. Sci. Ed., 2002, 24(2): 20-23. (in Chinese)

[5] Brady G S, Clauser H R. Materials Handbook, 1991 13th Ed. Wuhan: Mc Graw-Hill. 948-948.

[6] Palik E D. Handbook of Optical Cons tants of Solids II, 1991 Wuhan: Academic Press. 795-795.

[7] Wang X H, Xue Y Y, Zhao L, . Study on the Structure and Optical Properties of TiO₂ Thin Films Deposited by Reactive Electron Beam Evaporation. Journal of Wuhan University of Technology-Mater. Sci. Ed., 2002, 24(11): 30-33. (in Chinese)

[8] Macleod H A. Thin-film Optical Filters, 2001 P. A.: Institute of Physics Publishing. 40-43.

[9] Swanepoel R. Determination of the Thickness and Optical Constants of Amorphous Silicon. J. Phys, E SCI Instrum, 1983, 16(6): 1214-1222.

[10] Dannenberg Rand, Greene Phil. Reactive Sputter Deposition of Titanium Dioxide. Thin Solid Films, 2000, 360: 122-127.

[11] Wang Y L, Souche D, Zhang K Y, . Relations between the Optical Properties and Microstructure and of TiO₂ Thin Films Prepared by Ion-assisted Depos-ition. Thin Solid Films, 1997, 307(1,2): 38-42.

[12] Ohring Milton. Materials Science of Thin Films Deposition and Structure, 2001 2nd Ed. Wuhan: Academic Press. 498-501.

[13] Negishi Nobuaki, Takeuchi Koji. Structural Changes of Transparent TiO₂ Thin Films with Heat-treatment. Materials Letters, 1999, 38: 150-153.

[14] Klugm H P, Alexander L E. X-ray Diffraction Procedures, 1974 2nd edition Wuhan: Wiley Intersci.