Effect of thermo-mechanical treatment on microstructure and mechanical properties of wire-arc additively manufactured Al-Cu alloy

Tao Zhang, Zhen-yang Qin, Hai Gong, Yun-xin Wu, Xin Chen

Journal of Central South University ›› 2024, Vol. 31 ›› Issue (7) : 2181-2193. DOI: 10.1007/s11771-024-5740-2
Article

Effect of thermo-mechanical treatment on microstructure and mechanical properties of wire-arc additively manufactured Al-Cu alloy

Author information +
History +

Abstract

Wire-arc additive manufacture (WAAM) has great potential for manufacturing of Al-Cu components. However, inferior mechanical properties of WAAM deposited material restrict its industrial application. Inter-layer cold rolling and thermo-mechanical heat treatment (T8) with pre-stretching deformation between solution and aging treatment were adopted in this study. Their effects on hardness, mechanical properties and microstructure were analyzed and compared to the conventional heat treatment (T6). The results show that cold rolling increases the hardness and strengths, which further increase with T8 treatment. The ultimate tensile strength (UTS) of 513 MPa and yield stress (YS) of 413 MPa can be obtained in the inter-layer cold-rolled sample with T8 treatment, which is much higher than that in the as-deposited samples. The cold-rolled samples show higher elongation than that of as-deposited ones due to significant elimination of porosity in cold rolling; while both the T6 and T8 treatments decrease the elongation. The cold rolling and pre-stretching deformation both contribute to the formation of dense and dispersive precipitated θ′ phases, which inhibits the dislocation movement and enhances the strengths; as a result, T8 treatment shows better strengthening effect than the T6 treatment. The strengthening mechanism was analyzed and it was mainly related to work hardening and precipitation strengthening.

Keywords

wire-arc additive manufacture / inter-layer cold rolling / thermal-mechanical treatment / microstructure / mechanical properties / strengthening mechanism

Cite this article

Download citation ▾
Tao Zhang, Zhen-yang Qin, Hai Gong, Yun-xin Wu, Xin Chen. Effect of thermo-mechanical treatment on microstructure and mechanical properties of wire-arc additively manufactured Al-Cu alloy. Journal of Central South University, 2024, 31(7): 2181‒2193 https://doi.org/10.1007/s11771-024-5740-2

References

[[1]]
An L-h, Cai Y, Liu W, et al.. Effect of pre-deformation on microstructure and mechanical properties of 2219 aluminum alloy sheet by thermomechanical treatment. Transactions of Nonferrous Metals Society of China, 2012, 22: s370-s375, J]
CrossRef Google scholar
[[2]]
Liu L, Wu Y-x, Gong H, et al.. A physically based constitutive model and continuous dynamic recrystallization behavior analysis of 2219 aluminum alloy during hot deformation process. Materials, 2018, 11(8): 1443, J]
CrossRef Google scholar
[[3]]
Lockett H, Ding J-l, Williams S, et al.. Design for wire+arc additive manufacture: Design rules and build orientation selection. Journal of Engineering Design, 2017, 28(7–9): 568-598, J]
CrossRef Google scholar
[[4]]
Shen C, Pan Z-x, Cuiuri D, et al.. Fabrication of Fe-FeAl functionally graded material using the wire-arc additive manufacturing process. Metallurgical and Materials Transactions B, 2016, 47(1): 763-772, J]
CrossRef Google scholar
[[5]]
Williams S W, Martina F, Addison A C, et al.. Wire+ arc additive manufacturing. Materials Science and Technology, 2016, 32(7): 641-647, J]
CrossRef Google scholar
[[6]]
Asala G, Khan A K, Andersson J, et al.. Microstructural analyses of ATI 718Plus® produced by wire-ARC additive manufacturing process. Metallurgical and Materials Transactions A, 2017, 48(9): 4211-4228, J]
CrossRef Google scholar
[[7]]
Zhang D-k, Li Q, Zhao Y, et al.. Microstructure and mechanical properties of three-layer TIG-welded 2219 aluminum alloys with dissimilar heat treatments. Journal of Materials Engineering and Performance, 2018, 27(6): 2938-2948, J]
CrossRef Google scholar
[[8]]
Tao J-s, Zhang L, Wu G-h, et al.. Effect of heat treatment on the microstructure and mechanical properties of extruded Al-4Cu-1Li-0.4Mg-0.4Ag-0.18Zr alloy. Materials Science and Engineering A, 2018, 717: 11-19, J]
CrossRef Google scholar
[[9]]
Joshi A, Yogesha K K, Jayaganthan R. Influence of cryorolling and followed by annealing on high cycle fatigue behavior of ultrafine grained Al2014 alloy. Materials Characterization, 2017, 127: 253-271, J]
CrossRef Google scholar
[[10]]
Li X-f, Lei K, Song P, et al.. Strengthening of aluminum alloy 2219 by thermo-mechanical treatment. Journal of Materials Engineering and Performance, 2015, 24(10): 3905-3911, J]
CrossRef Google scholar
[[11]]
He H-l, Yi Y-p, Huang S-q, et al.. Effects of cold predeformation on dissolution of second-phase Al2Cu particles during solution treatment of 2219 Al-Cu alloy forgings. Materials Characterization, 2018, 135: 18-24, J]
CrossRef Google scholar
[[12]]
Li H-z, Liu R-m, Liang X-p, et al.. Effect of pre-deformation on microstructures and mechanical properties of high purity Al-Cu-Mg alloy. Transactions of Nonferrous Metals Society of China, 2016, 26(6): 1482-1490, J]
CrossRef Google scholar
[[13]]
Wang H-m, Yi Y-p, Huang S-quan. Influence of pre-deformation and subsequent ageing on the hardening behavior and microstructure of 2219 aluminum alloy forgings. Journal of Alloys and Compounds, 2016, 685: 941-948, J]
CrossRef Google scholar
[[14]]
Lu Y-l, Wang J, Li X-c, et al.. Effect of pre-deformation on the microstructures and properties of 2219 aluminum alloy during aging treatment. Journal of Alloys and Compounds, 2017, 699: 1140-1145, J]
CrossRef Google scholar
[[15]]
Lu Y-l, Wang J, Li X-c, et al.. Effects of pre-deformation on the microstructures and corrosion behavior of 2219 aluminum alloys. Materials Science and Engineering A, 2018, 723: 204-211, J]
CrossRef Google scholar
[[16]]
Ortega A G, Galvan L C, Beaume F D, et al.. Effect of process parameters on the quality of aluminium alloy Al5Si deposits in wire and arc additive manufacturing using a cold metal transfer process. Science and Technology of Welding and Joining, 2017, 23(4): 316-332, J]
CrossRef Google scholar
[[17]]
Cong B-q, Ding J-l, Williams S. Effect of arc mode in cold metal transfer process on porosity of additively manufactured Al-6.3%Cu alloy. The International Journal of Advanced Manufacturing Technology, 2015, 76(9): 1593-1606, J]
CrossRef Google scholar
[[18]]
Fang X-w, Zhang L-j, Li H, et al.. Microstructure evolution and mechanical behavior of 2219 aluminum alloys additively fabricated by the cold metal transfer process. Materials, 2018, 11(5): 812, J]
CrossRef Google scholar
[[19]]
Gu J-l, Ding J-l, Williams S W, et al.. The effect of inter-layer cold working and post-deposition heat treatment on porosity in additively manufactured aluminum alloys. Journal of Materials Processing Technology, 2016, 230: 26-34, J]
CrossRef Google scholar
[[20]]
Gu J-l, Wang X-s, Bai J, et al.. Deformation microstructures and strengthening mechanisms for the wire+arc additively manufactured Al-Mg4.5Mn alloy with inter-layer rolling. Materials Science and Engineering A, 2018, 712: 292-301, J]
CrossRef Google scholar
[[21]]
Gu J-l, Ding J-l, Williams S W, et al.. The strengthening effect of inter-layer cold working and postdeposition heat treatment on the additively manufactured Al-6.3Cu alloy. Materials Science and Engineering A, 2016, 651: 18-26, J]
CrossRef Google scholar
[[22]]
Anyalebechi P N, Hogarth J. Effect of supereutectic homogenization on incidence of porosity in aluminum alloy 2014 ingot. Metallurgical and Materials Transactions B, 1994, 25(1): 111-122, J]
CrossRef Google scholar
[[23]]
Wolfer W G, Baskes M I. Interstitial solute trapping by edge dislocations. Acta Metallurgica, 1985, 33(11): 2005-2011, J]
CrossRef Google scholar
[[24]]
Horn V, Robertson K. Aluminum: Properties, physical metallurgy and phase diagrams [M]. American Society for Metals, 1967
[[25]]
Ma P P, Liu C H, Wu C L, et al.. Mechanical properties enhanced by deformation-modified precipitation of θ′-phase approximants in an Al-Cu alloy. Materials Science and Engineering A, 2016, 676: 138-145, J]
CrossRef Google scholar
[[26]]
Yoshimura R, Konno T J, Abe E, et al.. Transmission electron microscopy study of the early stage of precipitates in aged Al-Li-Cu alloys. Acta Materialia, 2003, 51(10): 2891-2903, J]
CrossRef Google scholar

Accesses

Citations

Detail

Sections
Recommended

/