Microstructure and mechanical properties of 6061 aluminum alloy laser-MIG hybrid welding joint

Abstract

In this paper, 3 mm 6061 aluminum alloy sheets were welded by laser MIG hybrid welding. Based on the experiment, the best welding parameters were determined to ensure the penetration welding. The detailed microstructure, tensile and fatigue fracture morphology and surface fatigue damage of the welded joints were analyzed by optical microscope (OM), scanning electron microscope (SEM) and energy dispersive spectrometer (EDS). The results show that there are two main kinds of precipitates, one is the long Si rich precipitates at the grain boundaries, the other is the intragranular Cu rich precipitates. The tensile test results show that the tensile strength of the joint is 224 MPa, which is only 70.2% of the base metal. Through the analysis of tensile fracture, there are great differences in the formation of tensile dimple. In the tensile-tensile fatigue test with a stress rate of 0.1, the conditional fatigue limits of base metal and welded joint are 101.9 MPa and 54.4 MPa, respectively. By comparing the fatigue fracture of the welded joints under different stress amplitudes, it was found that the main factor leading to the fracture of the joint is porosity. Through further analysis of the pore defects, it was found that there are transgranular and intergranular propagation ways of microcracks in the pores, and the mixed propagation way was also found.

Keywords

aluminum alloy / laser-MIG hybrid welding / fatigue property / microstructure / mechanical properties

References

[1] ZhangJ, YeJ, SongB, et al.. Comparative study on microstructure and electrochemical corrosion resistance of Al7075 alloy prepared by laser additive manufacturing and forging technology [J]. Journal of Central South University, 2021, 28(4): 1058-1067

[2] YanS, XingB, ZhouH, et al.. Effect of filling materials on the microstructure and properties of hybrid laser welded Al−Mg−Si alloys joints [J]. Materials Characterization, 2018, 144: 205-218

[3] WangL, GaoM, ZhangC, et al.. Effect of beam oscillating pattern on weld characterization of laser welding of AA6061-T6 aluminum alloy [J]. Materials & Design, 2016, 108: 707-717

[4] ZhangL, LiK, HeH, et al.. Influence of prolonged natural aging followed by artificial aging ontensile properties and compressive behavior of a thin-walled6005 aluminum alloy tube [J]. Journal of Central South University, 2021, 28(9): 2647-2659

[5] de SalazarJ M G, UreñaA, VillaurizE, et al.. TIG and MIG welding of 6061 and 7020 aluminium alloys. Microstructural studies and mechanical properties [J]. Welding International, 1999, 13(4): 293-295

[6] YanS, NieY, ZhuZ, et al.. Characteristics of microstructure and fatigue resistance of hybrid fiber laser-MIG welded Al−Mg alloy joints [J]. Applied Surface Science, 2014, 298: 12-18

[7] LiangY, HuS, ShenJ, et al.. Geometrical and microstructural characteristics of the TIG-CMT hybrid welding in 6061 aluminum alloy cladding [J]. Journal of Materials Processing Technology, 2017, 239: 18-30

[8] GaurV, EnokiM, OkadaT, et al.. A study on fatigue behavior of MIG-welded Al−Mg alloy with different filler-wire materials under mean stress [J]. International Journal of Fatigue, 2018, 107: 119-129

[9] LiuJ, ZhuH, LiZ, et al.. Effect of ultrasonic power on porosity, microstructure, mechanical properties of the aluminum alloy joint by ultrasonic assisted laser-MIG hybrid welding [J]. Optics & Laser Technology, 2019, 119: 105619

[10] SteenW M. Arc augmented laser processing of materials [J]. Journal of Applied Physics, 1980, 51(11): 5636-5641

[11] YanS, ChenH, ZhuZ, et al.. Hybrid laser-metal inert gas welding of Al−Mg−Si alloy joints: Microstructure and mechanical properties [J]. Materials & Design, 2014, 61160-167

[12] YanJ, ZengX, GaoM, et al.. Effect of welding wires on microstructure and mechanical properties of 2A12 aluminum alloy in CO₂ laser-MIG hybrid welding [J]. Applied Surface Science, 2009, 255(16): 7307-7313

[13] TangG, ChenH, YangX, et al.. Effects of different welding process on the electronic temperature of plasma and weld shape during laser-MIG hybrid welding of A7N01P-T4 aluminum alloy [J]. Journal of Laser Applications, 2018, 30(2): 022002

[14] HanX, YangZ, MaY, et al.. Porosity distribution and mechanical response of laser-MIG hybrid butt welded 6082-T6 aluminum alloy joint [J]. Optics & Laser Technology, 2020, 132: 106511

[15] YonetaniH. Laser-MIG hybrid welding to aluminium alloy carbody shell for railway vehicles [J]. Welding International, 2008, 2210701-704

[16] PailKUsability of Laser-Arc hybrid welding processes in industrial applications [D], 2011, Finland, Lappeenranta, University of Lappeenranta Technology

[17] OlaO T, DoernF E. Keyhole-induced porosity in laser-arc hybrid welded aluminum [J]. The International Journal of Advanced Manufacturing Technology, 2015, 80(1–4): 3-10

[18] WangJ, NishimuraH, FujiiK, et al.. Study of improvement of gap tolerance in laser MIG arc hybrid welding of aluminium alloy [J]. Welding International, 2009, 23(10): 723-733

[19] AscariA, FortunatoA, OraziL, et al.. The influence of process parameters on porosity formation in hybrid LASER-GMA welding of AA6082 aluminum alloy [J]. Optics & Laser Technology, 2012, 44(5): 1485-1490

[20] WangL, LiuY, YangC, et al.. Study of porosity suppression in oscillating laser-MIG hybrid welding of AA6082 aluminum alloy [J]. Journal of Materials Processing Technology, 2021, 292117053

[21] ChenR, JiangP, ShaoX, et al.. Effect of magnetic field on crystallographic orientation for stainless steel 316L laser-MIG hybrid welds and its strengthening mechanism on fatigue resistance [J]. International Journal of Fatigue, 2018, 112308-317

[22] LiuH, YangS, XieC, et al.. Microstructure characterization and mechanism of fatigue crack initiation near pores for 6005A CMT welded joint [J]. Materials Science and Engineering A, 2017, 707: 22-29

[23] DuanC, YangS, GuJ, et al.. Study on microstructure and fatigue damage mechanism of 6082 aluminum alloy T-type metal inert gas (MIG) welded joint [J]. Applied Sciences, 2018, 8(10): 1741

[24] GuJ, YangS, XiongQ, et al.. Microstructure and mechanical study on laser-arc-welded Al−Zn−Mg alloy [J]. Materials Transactions, 2020, 611119-126

[25] BakerK L, WarnerD H. An atomistic investigation into the nature of near threshold fatigue crack growth in aluminum alloys [J]. Engineering Fracture Mechanics, 2014, 115: 111-121

[26] HuangY, HuangJ, NieP. Microstructures and textures of 6016 and 5182 aluminum laser welded joints [J]. Chinese Journal of Lasers, 2019, 46(4): 50-56 in Chinese)

[27] ZhanX, ZhaoY, LiuZ, et al.. Microstructure and porosity characteristics of 5A06 aluminum alloy joints using laser-MIG hybrid welding [J]. Journal of Manufacturing Processes, 2018, 35: 437-445

[28] ZhongQ, ZhaoZFractography [M], 2006, Beijing, Higher Education Press, 146155(in Chinese)

[29] ChangY, HungF Y, LuiT S. Enhancing the tensile yield strength of A6082 aluminum alloy with rapid heat solutionizing [J]. Materials Science and Engineering A, 2017, 702: 438-445

[30] QiaoK, WangK, WangW, et al.. Low-cycle Fatigue Properties of Friction Stir Welding Joint of AZ31 Magnesium [J]. Rare Metal Materials and Engineering, 2019, 48(3): 788-796

[31] LinS, DengY, TangJ, et al.. Microstructures and fatigue behavior of metal-inert-gas-welded joints for extruded Al−Mg−Si alloy [J]. Materials Science and Engineering A, 2019, 745: 63-73

[32] ZhaoY, ZhouX, LiuT, et al.. Investigate on the porosity morphology and formation mechanism in laser-MIG hybrid welded joint for 5A06 aluminum alloy with Y-shaped groove [J]. Journal of Manufacturing Processes, 2020, 57: 847-856

[33] FengL, XuanF. Effect of non-metallic inclusions on the local stress concentration within materials [J]. Journal of Mechanical Engineering, 2013, 49(8): 41-48 in Chinese)

[34] MughrabiH. Specific features and mechanisms of fatigue in the ultrahigh-cycle regime [J]. International Journal of Fatigue, 2006, 28(11): 1501-1508