Intensifying gibbsite precipitation from sodium aluminate solution by adding a mixed seed

Abstract

Gibbsite precipitation from sodium aluminate solution was intensified by adding mixed industrial and self-prepared active seeds, and its mechanism was researched preliminarily. The interfacial properties of seed/aluminate solution were determined for separate industrial and active seed. Contact angles of seed/aluminate solution and the specific surface area of seeds were respectively measured by sessile drop and BET method, and the morphology and particle size of precipitates were recorded by SEM and laser diffraction. The results show that, compared with the industrial seed, the active seed has a better wettability, lower interfacial tension, and larger specific surface area, being conducive to enhancing gibbsite precipitation from sodium aluminate solution. SEM analysis of the precipitates indicates that the embedment and accumulation/agglomeration of extremely fine particles on the surface of coarse industrial seed can effectively control the content of fine particles in the precipitation product. With extra 3.1–4.6 g/L active seed, the gibbsite precipitation ratio was increased by 3.23%–3.92%. Moreover, the mass percentage of particles <45 μm in precipitation product has even a slight decrease compared with that for the traditional precipitation product or of the industrial seed itself. The result presented is favorable to developing an intensified gibbsite precipitation process for commercial alumina manufacture.

Keywords

gibbsite / seeded precipitation / sodium aluminate solution / active seed / intensification

References

[1] XueS, YeY, ZhuF, WangQ, JiangJ, WilliamH. Changes in distribution and microstructure of bauxite residue aggregates following amendments addition [J]. Journal of Environmental Sciences, 2019, 78: 276-286

[2] XueS, WuY, LiY, KongX, ZhuF W H, LiX, YeYu. Industrial wastes applications for alkalinity regulation in bauxite residue: A comprehensive review [J]. Journal of Central South University, 2019, 26(2): 268-288

[3] LiX, ZhaoD, WangD, YanLi. Research progress in theory and technology of gibbsite precipitation from sodium aluminate solution [J]. The Chinese Journal of Nonferrous Metals, 2011, 21(10): 2577-2593

[4] LiX, WangD, ZhouQ, LiuG, PengZhi. Influence of magnetic field on the seeded precipitation of gibbsite from sodium aluminate solution [J]. Minerals Engineering, 2012, 32(3): 12-18

[5] ZhangB, LiJ, ChenQ, ChenGuo. Precipitation of Al(OH)3 crystals from supersaturated sodium aluminate solution irradiated with ultrasonic sound [J]. Minerals Engineering, 2009, 22(910): 853-858

[6] ChenN, LuW, ZhangL, GuS, QiL, BaiWan. Liquid-liquid extraction modified Bayer process and its physic-chemical basis [J]. Journal of the Chinese Rare Earth Society, 2006

[7] LiY, ChenQ, WangS, YinZ, ZhangPing. Preparation of Al(OH)3 by ion membrane electrolysis and precipitation of sodium aluminate solution with seeds [J]. The Chinese Journal of Nonferrous Metals, 2008, 18(4): 974-979

[8] WilhelmyR BControl of form of crystal precipitation of aluminum hydroxide using cosolvents and varying caustic concentration: United States, 4900537 [P], 1990

[9] ZhangY, ZhengS, DuH, XuH, WangS, ZhangYi. Improved precipitation of gibbsite from sodium aluminate solution by adding methanol [J]. Hydrometallurgy, 2009, 98(12): 38-44

[10] LiuG, WuG, ChenW, LiX, PengZ, ZhouQ, QiTian. Increasing precipitation rate from sodium aluminate solution by adding active seed and ammonia [J]. Hydrometallurgy, 2018, 176: 253-259

[11] ZengJ, YinZ, ChenQi. Effect of tetracarbon additives on gibbsite precipitation from seeded sodium aluminate liquor [J]. Journal of Central South University, 2008, 15(5): 622-626

[12] LiX, YanL, ZhouQ, PengZ, LiuGui. Effect of ethers additive B35 on seeded precipitation of sodium aluminate solution [J]. The Chinese Journal of Nonferrous Metals, 2011, 21(2): 459-464

[13] BrownN. Effect of calcium ions on agglomeration of bayer aluminium trihydroxide [J]. Journal of Crystal Growth, 1988, 92(1): 26-32

[14] GnyraN, BrownN. The coarsening of Bayer alumina trihydrate by means of crystallization modifiers [J]. Powder Technology, 1975, 11(2): 101-105

[15] TianLvStudy on preparation of high whiteness aluminum trihydroxide powder from high concentration sodium aluminate solution by seeded precipitation [D], 2012, Changsha, Central South University

[16] PradhanJ K, GochhayatP K, BhattacharyaI N, DasS C. Study on the various factors affecting the quality of precipitated non-metallurgical alumina trihydrate particles [J]. Hydrometallurgy, 2001, 60(2): 143-153

[17] XieY, BiS, YangY, WangZhi. Surface acidity of Al(OH)3 seed and its effect on precipitation of sodium aluminate liquors [J]. The Chinese Journal of Nonferrous Metals, 2000, 10(6): 896-898

[18] YinJianIntensifying the seeded agglomeration process of supersaturated sodium aluminate liquors [D], 2007, Changsha, Central South University

[19] ZengJ, YinZ, ChenQi. Intensification of precipitation of gibbsite from seeded caustic sodium aluminate liquor by seed activation and addition of crown ether [J]. Hydrometallurgy, 2007, 89(1): 107-116

[20] ZhangXuanParticle size control of products from precipitation process with seeds prepared by inducing nucleation in sodium aluminate solution [D], 2011, Changsha, Central South University

[21] LiuG, LiZ, QiT, LiX, ZhouQ, PengZhi. Two-stage process for precipitating coarse boehmite from sodium aluminate solution [J]. JOM, 2017, 69(10): 1888-1893

[22] Addai-MensahJ, RalstonJ. The influence of interfacial structuring on gibbsite interactions in synthetic Bayer liquors [J]. Journal of Colloid and Interface Science, 1999, 215(1): 124-130

[23] Addai-MensahJ, PrestigeC A, RalstonJ. Interparticle forces, interfacial structure development and agglomeration of gibbsite particles in synthetic Bayer liquors [J]. Minerals Engineering, 1999, 12: 655-669

[24] WattsH L, UtleyD W. Volumetric analysis of sodium aluminate solutions [J]. Analytical Chemistry, 1953, 25(6): 864-867

[25] YangChongTechnology of alumina production [M], 2011, Beijing, Metallurgical Industry Press

[26] OwensD K, WendtR C. Estimation of the surface free energy of polymers [J]. Journal of Applied Polymer Science, 1969, 13(8): 1741-1747

[27] LunerP E, OhE. Characterization of the surface free energy of cellulose ether films [J]. Colloids & Surfaces A: Physicochemical & Engineering Aspects, 2001, 181(1–3): 31-48

[28] LiX, XuX, ZhouQ, QiT, LiuG, PengZ, CuiY, LiJian. Ca3WO6 prepared by roasting tungsten-containing materials and its leaching performance [J]. International Journal of Refractory Metals & Hard Materials, 2015, 52: 151-158

[29] AdamsonA W, GastA PPhysical chemistry of surfaces [M], 1997, New York, Wiley

[30] ZhuD, DaiP, LuoX, ZhangYuan. Novel characterization of wetting properties and the calculation of liquid-solid interface tension(I) [J]. Science Technology and Engineering, 2007, 7(13): 3057-3062

[31] ZhuD, ZhangY, DaiP, LuoXiao. Novel characterization of wetting properties and the calculation of liquid-solid interface tension(II) [J]. Science Technology and Engineering, 2007, 7(13): 3063-3069

[32] LiX, YanL, ZhaoD, ZhouQ, LiuG, PengZ, YangS, QiTian. Relationship between Al(OH)3 solubility and particle size in synthetic Bayer liquors [J]. Transactions of Nonferrous Metals Society of China, 2013, 23(5): 1472-1479

[33] WangJ, ChenQ, LiW, YinZhouKinetics of super-fine aluminum hydroxide precipitation from sodium aluminate solutions with gel-seed [C]//Light Metals, 2009, San Francisco, California, TMS

[34] BhattacharyaI N, PradhanJ K, GochhayatpK, DasS C. Factors controlling precipitation of finer size alumina trihydrate [J]. International Journal of Mineral Processing, 2002, 65(2): 109-124