Transformation of β to α phase of isotactic polypropylene nucleated with nano styrene butadiene rubber-based β-nucleating agent under microwave irradiation

Abstract

This paper investigates the effect of microwave irradiation on the β to α phase transformation of the β-nucleated isotactic polypropylene (iPP). Ten microwave irradiation cycles was applied to the iPP and iPP modified with 0.3 wt% and 0.5 wt% β-NA, and the data at 2nd, 4th, 6th, 8th and 10th irradiation were reported. As expected, the sample temperature was found to increase with the irradiation time, by more than 130 °C, due to high frequency of microwave processing. This was the major factor that induced the β-phase transformation and structural change. Both the differential scanning calorimetry (DSC) and X-ray diffraction (XRD) results indicated that β-phase was mainly transformed to α-phase and partially converted to the amorphous section. It was reflected as 1) the reduction of the enthalpy of β-crystal melting (ΔH_mβ), 2) the increased enthalpy of α-crystal melting (ΔH_mα), 3) the decreased β-crystalline phase fraction (K_β) and 4) the decrease of the overall degree of crystallinity (X_all). Under impact force, neat iPP showed a slight increase in the impact strength with the irradiation time, due to the increase of amorphous region. For the β-iPP, it decreased due to the reduction of the β-phase content.

Keywords

polypropylene / crystallization / mechanical properties / thermal properties

References

[1] LiJ W, YangK, SongL, HanL, FengY K. Non-isothermal crystallisation of polypropylene/hollow glass microspheres composites [J]. Plastics, Rubber and Composites, 2015, 44: 68-73

[2] ChandrasekaranS, RamanathanS, BasakT. Microwave material processing-a review [J]. AIChE Journal, 2012, 58: 330-363

[3] ClarkD E, FolzD C, WestJ K. Processing materials with microwave energy [J]. Materials Science and Engineering A, 2000, 287: 153-158

[4] VenkateshM S, RaghavanG S V. An overview of microwave processing and dielectric properties of agri-food materials [J]. Biosystems Engineering, 2004, 88: 1-18

[5] BurdickD, CoxN A, ThompsonJ E, BaileyJ S. Heating by microwave, hot air, and flowing steam to eliminate inoculated Salmonella from poultry feed [J]. Poultry Science, 1983, 62: 1780-1785

[6] PetchwattanaN, CovavisaruchS, SripanyaP. Effect of nano-scaled styrene butadiene rubber based nucleating agent on the thermal, crystallization and physical properties of isotactic polypropylene [J]. Journal of Alloys and Compounds, 2014, 582: 190-195

[7] MaoH, LiuY, LiuW, NieM, WangQ. Investigation of crystallisation and interfacial nature of polyhedral oligomeric silsesquioxane/polypropylene composites in the presence of β-nucleating agent [J]. Plastics, Rubber and Composites, 2017, 46: 322-328

[8] ChenZ, KangW, KangJ, ChenJ, YangF, CaoY, XiangM. Non-isothermal crystallization behavior and melting behavior of Ziegler–Natta isotactic polypropylene with different stereo-defect distribution nucleated with bi-component β-nucleation agent [J]. Polymer Bulletin, 2015, 72: 3283-3303

[9] LiX, WuH, WangY, BaiH, LiuL, HuangT. Study on the β to α transformation of PP/POE blends with β-phase nucleating agent during the tensile deformation process [J]. Materials Science and Engineering A, 2010, 527: 531-538

[10] XuW, MartinaD C, ArrudaE M. Finite strain response, microstructural evolution and β/α phase transformation of crystalline isotactic polypropylene [J]. Polymer, 2005, 46: 455-470

[11] KotekJ, KelnarI, BaldrianJ, RaabM. Structural transformations of isotactic polypropylene induced by heating and UV light [J]. European Polymer Journal, 2004, 40: 2731-2738

[12] GregoriouV G, KandiliotiG, BollasS T. Chain conformational transformations in syndiotactic polypropylene/layered silicate nanocomposites during mechanical elongation and thermal treatment [J]. Polymer, 2005, 46: 11340-11350

[13] ZhangR H, ShiD, TjongS C, LiR K Y. Study on the β to α transformation of polypropylene crystals in compatibilized blend of polypropylene/polyamide-6 [J]. Journal of Polymer Science: Polymer Physics Edition, 2007, 45: 2674-2681

[14] ShangguanY G, SongY H, PengM, LiB P, ZhengQ. Formation of β-crystal from nonisothermal crystallization of compression-molded isotactic polypropylene melt [J]. European Polymer Journal, 2005, 41: 1766-1771

[15] LiJ X, CheungW L, JiaD M. A study on the heat of fusion of β-polypropylene [J]. Polymer, 1999, 40: 1219-1222

[16] JainS, GoossensH, VanD M, LemstraP. Effect of in situ prepared silica nano-particles on nonisothermal crystallization of polypropylene [J]. Polymer, 2005, 46: 8805-8818

[17] LiX, WuH, HuangT, ShiY, WangY, XiangF, ZhouZ. β/α transformation of β-polypropylene during tensile deformation: effect of crystalline morphology [J]. Colloid and Polymer Science, 2010, 288: 1539-1549

[18] RadhakrishnanJ, IchikawaK, YamadaK, TodaA, HikosakaM. Nearly pure α2 form crystals obtained by melt crystallization of high tacticity isotactic polypropylene [J]. Polymer, 1998, 39: 2995-2997

[19] BaiH, WangY, ZhangZ, HanL, LiY, LiuL, ZhouZ, MenY. Influence of annealing on microstructure and mechanical properties of isotactic polypropylene with β-phase nucleating agent [J]. Macromolecules, 2009, 42: 6647-6655

[20] TordjemanP, RobertC, MarinG, GerardP. The effect of α, β crystalline structure on the mechanical properties of polypropylene [J]. The European Physical Journal E, 2001, 4: 459-465

[21] BaiH, WangY, SongB, LiY, LiuL. Detecting crystallization structure evolution of polypropylene injection-molded bar induced by nucleating agent [J]. Polymer Engineering and Science, 2008, 48: 1532-1541