Microstructure, mechanical properties, and milling performance of arc-PVD AlTiN-Cu and AlTiN/AlTiN-Cu coatings

Abstract

AlTiN, AlTiN-Cu and AlTiN/AlTiN-Cu coatings were prepared on WC-6%Co substrates by cathode arc evaporation deposition technology. Two kinds of nitrogen pressures were used to deposit both AlTiN-Cu and AlTiN/AlTiN-Cu coatings. Surface and cross-sectional morphologies of films were observed by scanning electron microscopy (SEM). Crystal structure of films was analyzed by X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS). Hardness and adhesion of films were measured by nano-indentation and nano-scratch tester. Cutting tests were performed under milling conditions during wet machining of TC4 alloy. The results show that with addition of Cu, more droplets occur on AlTiN coating surface, but the grain size of it is refined, and the hardness decreases but the toughness is improved. Under higher N₂ pressure, the defects on the surface of AlTiN-Cu and AlTiN/AlTiN-Cu coatings diminish, and the hardness of them is enhanced, while the adhesion is reduced. Compared to AlTiN coated cemented carbide tool, the lifetimes of AlTiN-Cu and AlTiN/AlTiN-Cu coated tools under the same N₂ pressure are improved by 11% and 24%, respectively.

Keywords

coated cemented carbide / AlTiN-Cu / AlTiN/AlTiN-Cu / N₂ pressure / milling

References

[1] EzugwuE O. Key improvements in the machining of difficult-to-cut aerospace superalloys [J]. International Journal of Machine Tools & Manufacture, 2005, 45(1213): 1353-1367

[2] BiksaA, YamamotoK, DosbaevaG, VeldhuisS C, Fox-RabinovichG S, ElfizyA, ShusterL S. Wear behavior of adaptive nano-multilayered AlTiN/MexN PVD coatings during machining of aerospace alloys [J]. Tribology International, 2010, 43(8): 1491-1499

[3] ZhuX-s, FuY-d, LiZ-f, LengKe. Wear resistance of TC4 by deformation accelerated plasma nitriding at 400 °C [J]. Journal of Central South University, 2016, 23(11): 2771-2776

[4] GhaniJ A, CheH C H, HamdanS H, SaidA Y M, TomadiS H. Failure mode analysis of carbide cutting tools used for machining titanium alloy [J]. Ceramics International, 2013, 39(4): 4449-4456

[5] MayrhoferP H, MittererC, HultmanL, ClemensH. Microstructural design of hard coatings [J]. Progress in Materials Science, 2006, 51(8): 1032-1114

[6] Fox-RabinovichG S, KovalevA I, AguirreM H, BeakeB D, YamamotoK, VeldhuisS C, EndrinoJ L, WainsteinD L, RashkovskiybA Y. Design and performance of AlTiN and TiAlCrN PVD coatings for machining of hard to cut materials [J]. Surface & Coatings Technology, 2009, 204(4): 489-496

[7] WangX Q, ZhaoY H, YuB H, XiaoJ Q, LiF Q. Deposition, structure and hardness of Ti–Cu–N hard films prepared by pulse biased arc ion plating [J]. Vacuum, 2011, 86(4): 415-421

[8] DosbaevaG K, VeldhuisS C, ElfizyA, Fox-RabinovichG, WaggT. Microscopic observations on the origin of defects during machining of direct aged (DA) Inconel 718 superalloy [J]. Journal of Materials Engineering & Performance, 2010, 19(8): 1193-1198

[9] GuleryuzC G, KrzanowskiJ E, VeldhuisS C, Fox-RabinovichG S. Machining performance of TiN coatings incorporating indium as a solid lubricant [J]. Surface & Coatings Technology, 2009, 203(22): 3370-3376

[10] LeuM S, LoS C, WuJ B, LiA K. Microstructure and physical properties of arc ion plated TiAlN/Cu thin film [J]. Surface & Coatings Technology, 2006, 201: 3982-3986

[11] Fox-RabinovichG S, YamamotoK, AguirreM H, CahillD G, VeldhuisS C, BiksaA, DosbaevaG, ShusterL S. Multi-functional nano-multilayered AlTiN/Cu PVD coating for machining of Inconel 718 superalloy [J]. Surface & Coatings Technology, 2010, 204(15): 2465-2471

[12] MiyanoR, KimuraK, IzumiK, TakikawaH, SakakibaraT. Preparation of metal nitride and oxide thin films using shielded reactive vacuum arc deposition [J]. Vacuum, 2000, 59: 159-167

[13] HarrisS G, DoyleE D, WongY C, MunroeP R, CairneyJ M, LongJ M. Reducing the macroparticle content of cathodic arc evaporated TiN coatings [J]. Surface & Coatings Technology, 2004, 183(2): 283-294

[14] MiyanoR, FujimuraY, TakikawaH, SakakibaraT. Cathode spot motion in vacuum arc of zinc cathode under oxygen gas flow [J]. IEEE Transactions on Plasma Science, 2001, 29(5): 713-717

[15] ZhangL, MaG J, LinG Q, HanK C, MaH. Synthesis of Cu doped TiN composite films deposited by pulsed bias arc ion plating [J]. Nuclear Instruments & Methods in Physics Research, 2014, 320: 17-21

[16] GachonJ C, RogachevA S, GrigoryanH E, IllarionovaE V, KuntzJ J, KovalevD Y, NosyrevA N, SachkovaN V, TsygankovP A. On the mechanism of heterogeneous reaction and phase formation in Ti/Al multilayer nanofilms [J]. Acta Materialia, 2005, 53(4): 1225-1231

[17] PolychronopoulouK, DemasN G, GibsonP N, RebholzC, PolycarpouA A. Effect of Cu content on the structure, and performance of substoichiometric Cr–N coatings [J]. Tribology Letters, 2010, 38(1): 57-68

[18] CaiF, ZhangS-h, LiJ-l, ChenZ, LiM-x, WangLei. Effect of nitrogen partial pressure on Al–Ti–N films deposited by arc ion plating [J]. Applied Surface Science, 2011, 258(5): 1819-1825

[19] FengC-j, HuX-h, JiangY-f, ZhaoQing. Effects of Cu addition on microstructure and adhesion properties of Ti-Al-N nanocomposite films deposited by magnetron sputtering [J]. Advanced Materials Research, 2013, 652–654: 1751-1754

[20] WangC Y, XieY X, QinZ, LinH S, YuanY H, WangQ M. Wear and breakage of TiAlN-and TiSiN-coated carbide tools during high-speed milling of hardened steel [J]. Wear, 2015, 336–337: 29-42