Effect of optimal aging treatment on magnetic performance and mechanical properties of sintered Nd-Fe-B permanent magnets

Abstract

The magnetic performance and mechanical properties including hardness, brittleness, fracture toughness and strength characteristics of the as-sintered and the optimal aged Nd-Fe-B magnets were examined in this work. A new method of Vickers hardness indentation combined with acoustic emission was used to test the brittleness of the magnets.The results show that the magnetic properties of the magnets could be improved through aging treatment, especially the intrinsic coercive force. But it is accompanied by a decrease of strength and fracture toughness. Theoretical calculation confirms that acoustic emission energy accumulated count value could be used to characterize the material brittleness. The bending fracture morphologies of the as-sintered and the optimal aged NdFeB magnets were investigated with the emphasis on the relationship between mechanical properties and microstructure using a field emission scanning electron microscopy (FE-SEM). The research results indicate that the intergranular fracture is the primary fracture mechanism for both as-sintered and optimal aged NdFeB magnets. Aging treatment changes the morphology and distribution of the Nd-rich phases, reducing the sliding resistance between Nd₂Fe₁₄B main crystal grains and lowers the grain boundary strength, which is the main reason for the strength and fracture toughness decrease of the aged Nd-Fe-B magnets.

Keywords

Nd-Fe-B permanent magnets / aging treatment / mechanical property / acoustic emission / fracture analysis / Nd-rich phase

References

[1] FabianoF., CelegatoF., GiordanoA., BorsellinoC., BonaccorsiL., CalabreseL., TibertoP., CordascoG., MatareseG., FabianoV., AzzerboniB.. Assessment of corrosion resistance of Nd–Fe–B magnets by silanization for orthodontic applications [J]. Physica B: Condensed Matter, 2014, 435: 92-95

[2] ShengH.-c., ZengX.-r., JinC.-x., QianH.-x.. Microstructure and magnetic properties of directly quenched Nd2Fe14B/a-Fe nanocomposite materials at different temperatures [J]. Journal of Central South University, 2014, 21: 1275-1278

[3] SalibasilvaA., FariaR. N., BakerM. A., CostaI.. Improving the corrosion resistance of NdFeB magnets: An electrochemical and surface analytical study [J]. Surface and Coating Technology, 2004, 185: 321-328

[4] LiW. F., OhkuboT., HonoK.. Effect of post-sinter annealing on the coercivity and microstructure of Nd–Fe–B permanent magnets [J]. Acta Materialia, 2009, 57: 1337-1346

[5] VialF., JolyF., NevalainenE., SagawaM., HiragaK., ParkK. T.. Improvement of coercivity of sintered NdFeB permanent magnets by heat treatment [J]. Journal of Magnetism and Magnetic Materials, 2002, 242-245: 1329-1334

[6] RabinovichY. M., SergeevV. V., MaystrenkoA. D., KulakovskyV., SzymuraS., BalaH.. Physical and mechanical properties of sintered Nd-Fe-B type permanent magnets [J]. Intermetallics, 1996, 4: 641-645

[7] JiangJ.-h., ZengZ.-p., YuJ., WuJ.-s., TokunagaM.. The effect of Co addition on the fracture strength of NdFeB sintered magnets [J]. Intermetallics, 2001, 9: 269-272

[8] JiangJ.-h., ZengZ.-p., WuJ.-s., TokunagaM.. Influence of alloying elements on mechanical properties and microstructures of sintered Nd–Fe–Co–B magnet [J]. Journal of Magnetism and Magnetic Materials, 2000, 214: 61-68

[9] LiA.-h., LiW., DongS.-z., LiX.-m.. Sintered Nd–Fe–B magnets with high strength [J]. Journal of Magnetism and Magnetic Materials, 2003, 265: 331-336

[10] DingX., WangX.-l., SiC.-h., ZhaoL.-n., DingK.-h., CuiS.-l., SunY.-c., LiM.-s.. Study on the relativity between intrinsic coercivity and microstructure of the Nd-Fe-B magnet treated by the optimized aging treatment [J]. Advanced Materials Research, 2014, 1002: 73-76

[11] BS EN ISO 3327.Hardmetals-determination of transverse rupture strength [S], 2009

[12] FerreiraJ. A. M., AmaralM. A. P., AntunesF. V., CostaJ. D. M.. A study on the mechanical behaviour of WC/Co hardmetals [J]. International Journal of Refractory Metals and Hard Materials, 2009, 27: 1-8

[13] PetersC. T.. The relationship between Palmqvist indentation toughness and bulk fracture toughness for some WC/Co cemented carbides [J]. Journal of Materials Science, 1979, 14: 1619-1623

[14] ChenB., LiuJ.-y.. Experimental study on AE characteristics of three-point-bending concrete beams [J]. Cement and Concrete Research, 2004, 34: 391-397

[15] AlamS. Y., SalibaJ., LoukiliA.. Fracture examination in concrete through combined digital image correlation and acoustic emission techniques [J]. Construction and Building Materials, 2014, 69: 232-242

[16] BourasS., ZerizerI., GheldaneF., BouazzaoM. T., BouzabataB.. Study of the resistance to crack propagation in alumina by acoustic emission [J]. Ceramics International, 2008, 34: 1857-1865

[17] LiuW., WuJ.-s.. Mechanical properties and fracture mechanism study of sintered Nd–Fe–B alloy [J]. Journal of Alloys and Compounds, 2008, 458: 292-296

[18] ZengZ.-p.. A study of alloy elements affecting the fracture strength of sintered Nd-Fe-B magnets [J]. Physical Testing and Chemical Analysis Part A: Physical Testing, 1999, 33(9): 19-21

[19] LiuZ.-e.Material science [J], 2007214-222

[20] ZengZ.-p.. A study of the fracture in sintered Nd-Fe-B permanent magnetic materials [J]. Rare Metal Materials and Engineering, 1996, 25(3): 18-21

[21] JiangJ.-h., ZengZ.-p.. Study of alloy elements affecting the fracture strength of sintered Nd-Fe-B magnets [J]. Rare Metal Materials and Engineering, 1999, 28(3): 144-147