Optimization of low-temperature alkaline smelting process of crushed metal enrichment originated from waste printed circuit boards

Abstract

A novel low-temperature alkaline smelting process is proposed to convert and separate amphoteric metals in crushed metal enrichment originated from waste printed circuit boards. The central composite design was used to optimize the operating parameters, in which mass ratio of NaOH-to-CME, smelting temperature and smelting time were chosen as the variables, and the conversions of amphoteric metals tin, lead, aluminum and zinc were response parameters. Second-order polynomial models of high significance and 3D response surface plots were constructed to show the relationship between the responses and the variables. Optimum area of 80%–85% Pb conversion and over 95% Sn conversion was obtained by the overlaid contours at mass ratio of NaOH-to-CME of 4.5–5.0, smelting temperature of 653–723 K, smelting time of 90–120 min. The models were validated experimentally in the optimum area, and the results demonstrate that these models are reliable and accurate in predicting the smelting process.

Keywords

low-temperature alkaline smelting / waste printed circuit board / amphoteric metals / central composite design / conversion

References

[1] ZhouY-h, QiuK-qiang. A new technology for recycling materials from waste printed circuit boards [J]. Journal of Hazardous Materials, 2010, 175(1): 823-828

[2] SakaiS, WatanabeJ, HondaY, TakatsukiH, AokiI, FutamatsuM, ShiozakiK. Combustion of brominated flame retardants and behavior of its byproducts [J]. Chemosphere, 2001, 42(5): 519-531

[3] GooseyM, KellnerR. Recycling technologies for the treatment of end of life printed circuit boards (PCBs) [J]. Circuit World, 2003, 29(3): 33-37

[4] VeitH M, DiehlT R, SalamiA P, RodriguesJ S, BernardesA M, TenórioJ A S. Utilization of magnetic and electrostatic separation in the recycling of printed circuit boards scrap [J]. Waste Management, 2005, 25(1): 67-74

[5] HallW J, WilliamsP T. Separation and recovery of materials from scrap printed circuit boards [J]. Resources, Conservation and Recycling, 2007, 51(3): 691-709

[6] YangX-n, SunL-s, XiangJ, HuS, SuSheng. Pyrolysis and dehalogenation of plastics from waste electrical and electronic equipment (WEEE): A review [J]. Waste Management, 2013, 33(2): 462-473

[7] BientinesiM, PetarcaL. Comparative environmental analysis of waste brominated plastic thermal treatments [J]. Waste Management, 2009, 29(3): 1095-1102

[8] HuangZ-y, XieF-c, MaYang. Ultrasonic recovery of copper and iron through the simultaneous utilization of printed circuit boards (PCB) spent acid etching solution and PCB waste sludge [J]. Journal of Hazardous Materials, 2011, 185(1): 155-161

[9] JhaM K, LeeJ, KumariA, ChoubeyP K, KumarV, JeongJ. Pressure leaching of metals from waste printed circuit boards using sulfuric acid [J]. JOM, 2011, 63(8): 29-32

[10] QuinetP, ProostJ, van LierdeA. Recovery of precious metals from electronic scrap by hydrometallurgical processing routes [J]. Minerals and Metallurgical Processing, 2005, 22(1): 17-22

[11] YangT, XuZ, WenJ-k, YangL-mei. Factors influencing bioleaching copper from waste printed circuit boards by Acidithiobacillus ferrooxidans [J]. Hydrometallurgy, 2009, 97(1): 29-32

[12] HongY, ValixM. Bioleaching of electronic waste using acidophilic sulfur oxidising bacteria [J]. Journal of Cleaner Production, 2014, 65(15): 465-472

[13] TangM-t, TangC-b, ChenY-m, YangJ-g, YangS-h, HeJ, OuZhao. A promising low carbon clean metallurgical method — Low-temperature molten salt metallurgy of heavy metal [J]. China Nonferrous Metallurgy, 2010, 39(4): 49-53

[14] GuoX-q, LiuJ-x, TianQ-h, LiDong. Principle and method of low temperature alkaline smelting in non-ferrous metallury complicated resources [J]. Nonferrous Metals Science and Engineering, 2013, 4(2): 8-13

[15] GuoX-q, LiuJ-x, TianQ-hua. Elemental behavior of multicomponent metal powders from waste printed circuit board during low-temperature alkaline smelting [J]. The Chinese Journal of Nonferrous Metals, 2013, 23(6): 1757-1763

[16] MontgomeryD CDesign and analysis of experiments [M], 2008, New York, John Wiley & Sons: 164-185

[17] BaşD, Boyaciİ H H. Modeling and optimization I: Usability of response surface methodology [J]. Journal of Food Engineering, 2007, 78(3): 836-845

[18] BoxG E P, WilsonK B. On the experimental attainment of optimum conditions [J]. Journal of the Royal Statistical Society. Series B (Methodological), 1951, 13(1): 1-45

[19] BoxG E P, HunterJ S. Multi-factor experimental designs for exploring response surfaces [J]. The Annals of Mathematical Statistics, 1957, 28(1): 195-241

[20] ObengD P, MorrellS, Napier-MunnT J. Application of central composite rotatable design to modelling the effect of some operating variables on the performance of the three-product cyclone [J]. International Journal of Mineral Processing, 2005, 76(3): 181-192

[21] MohapatraS, PradhanN, MohantyS, SuklaL B. Recovery of nickel from lateritic nickel ore using Aspergillus niger and optimization of parameters [J]. Minerals Engineering, 2009, 22(3): 311-313

[22] BreretonR GChemometrics: data analysis for the laboratory and chemical plant [M], 2003, Hoboken, John Wiley & Sons: 76-84

[23] ObengD P, MorrellS, Napier-munnT J. Application of central composite rotatable design to modelling the effect of some operating variables on the performance of the three-product cyclone [J]. International Journal of Mineral Processing, 2005, 76(3): 181-192

[24] FlandinetL, TedjarF, GhettaV, FouletierJ. Metals recovering from waste printed circuit boards (WPCBs) using molten salts [J]. Journal of Hazardous Materials, 2012, 213(4): 485-490