Scratching by pad asperities in copper electrochemical-mechanical polishing

Yan-fei Bian , Wen-jie Zhai , Yuan-yuan Cheng , Bao-quan Zhu

Journal of Central South University ›› 2014, Vol. 21 ›› Issue (11) : 4157 -4162.

PDF
Journal of Central South University ›› 2014, Vol. 21 ›› Issue (11) : 4157 -4162. DOI: 10.1007/s11771-014-2411-8
Article

Scratching by pad asperities in copper electrochemical-mechanical polishing

Author information +
History +
PDF

Abstract

Low dielectric constant materials/Cu interconnects integration technology provides the direction as well as the challenges in the fabrication of integrated circuits (IC) wafers during copper electrochemical-mechanical polishing (ECMP). These challenges arise primarily from the mechanical fragility of such dielectrics, in which the undesirable scratches are prone to produce. To mitigate this problem, a new model is proposed to predict the initiation of scratching based on the mechanical properties of passive layer and copper substrate. In order to deduce the ratio of the passive layer yield strength to the substrate yield strength and the layer thickness, the limit analysis solution of surface scratch under Berkovich indenter is used to analyze the nano-scratch experimental measurements. The modulus of the passive layer can be calculated by the nano-indentation test combined with the FEM simulation. It is found that the film modulus is about 30% of the substrate modulus. Various regimes of scratching are delineated by FEM modeling and the results are verified by experimental data.

Keywords

electrochemical-mechanical polishing / scratch / pad asperities / nano-scratch / model / nano-indentation

Cite this article

Download citation ▾
Yan-fei Bian, Wen-jie Zhai, Yuan-yuan Cheng, Bao-quan Zhu. Scratching by pad asperities in copper electrochemical-mechanical polishing. Journal of Central South University, 2014, 21(11): 4157-4162 DOI:10.1007/s11771-014-2411-8

登录浏览全文

4963

注册一个新账户 忘记密码

References

[1]

ElshochtS V, DelabieA, DewildeS, MeersschautJ, SwertsJ, TielensH, VerdonckP, WittersT, VancoilleE. ALD barrier deposition on porous low-k dielectric materials for interconnects [J]. ECS Transactions, 2011, 41(2): 25-32

[2]

ZhouW, BaileyS, SooryakumarR, KingS, XuG, MaysE, EgeC, BielefeldJ. Elastic properties of porous low-k dielectric nano-films [J]. Journal of Applied Physics, 2011, 110: 043520

[3]

XiK, HeH, XuD, GeR J, MengZ, JiaX D, YuX H. Ultra low dielectric constant polysilsequioxane films using T8(Me4NO)8 as porogen [J]. Thin Solid Films, 2010, 518: 4768-4772

[4]

TerenceK S W. Time dependent dielectric breakdown in copper low-k interconnects: Mechanisms and reliability models [J]. Materials, 2012, 5: 1602-1625

[5]

CHEN F, SHINOSKY M. Soft breakdown characteristics of ultra low-k time-dependent dielectric breakdown for advanced complementary metal-oxide semiconductor technologies [J]. Applied Physics Letters, 2010, 108, 054107.

[6]

ZhaoL, TokeiZ, CroesK, WilsonC J, BaklanovM, BeyerG P, ClaeysC. Direct observation of the 1/E dependence of time dependent dielectric breakdown in the presence of copper [J]. Applied Physics Letters, 2011, 98: 023107

[7]

LinW C, LinJ, TsaiT C, HsuC M, LiuC C, LinJ F, HwangC C, WuJ Y. Effects of Cu surface roughness on TDDB for direct polishing ultra-low k dielectric Cu interconnects at 40 nm technology node and beyond [J]. Microelectronic Engineering, 2012, 92: 115-118

[8]

HeM, NovakS, VanamurthyL, BakhruH, PlawskyJ, LuT M. Cu penetration into low-k dielectric during deposition and bias-temperature stress [J]. Applied Physics Letters, 2010, 97: 252901

[9]

SakaN, EusnerT, ChunJ H. Nano-scale scratching in chemical-mechanical polishing [J]. CIRP Annals-Manufacturing Technology, 2008, 57: 341-344

[10]

SakaN, EusnerT, ChunJ H. Scratching by pad asperities in chemical-mechanical polishing [J]. CIRP Annals-Manufacturing Technology, 2010, 59: 329-332

[11]

OliverW C, PharrG M. Measurement of hardness and elastic modulus by instrumented indentation: Advances in understanding and refinements to methodology [J]. Journal of Materials Research, 2004, 19: 3-20

[12]

ZengF L, LiuY Z, SunY, HuE L, ZhouY. Nanoindentation, nanoscratch, and nanotensile testing of poly(vinylidene fluoride)-polyhedral oligomeric silsesquioxane nanocomposites [J]. Journal of Polymer Physics, 2012, 50(23): 1597-1611

[13]

ZhaiW J, YangY Z. Tribo-electrochemical performance of copper ECMP in mixed phosphate electrolytes [J]. Advanced Materials Research, 2011, 314/315/316: 2565-2568

[14]

BianY F, ZhaiW J, ZhuB Q. 5-methyl-1H-benzotriazole as potential corrosion inhibitor for electrochemical-mechanical planarization of copper [J]. Transactions of Nonferrous Metals Society of China, 2013, 23(8): 2431-2438

[15]

PanC T, WuT T, LiuC F, SuC Y, WangW J, HuangJ C. Study of scratching Mg-based BMG using nanoindenter with Berkovich probe [J]. Materials Science and Engineering A, 2010, 527: 2342-2349

[16]

LichinchiM, LenardiC, HauptJ, VitaliR. Simulation of Berkovich nanoindentation experiments on thin films using finite element method [J]. Thin Solid Films, 1998, 312: 240-248

[17]

ChenX, VlasakJ. Numerical study on the measurement of thin film mechanical properties by means of nanoindentation [J]. Journal of Materials Research, 2001, 16(10): 2974-2982

[18]

MesarovicS D, FleckN A. Frictionless indentation of dissimilar elastic-plastic spheres [J]. International Journal of Solids and Structures, 2000, 37(46): 7071-7079

[19]

JohnsonK LContact mechanics [M], 1985, UK, Cambridge University Press: 93-94

AI Summary AI Mindmap
PDF

95

Accesses

0

Citation

Detail

Sections
Recommended

AI思维导图

/