Characterization of microstructure evolution of cement paste by micro computed tomography

Abstract

Micro computed tomography (Micro-CT) was applied to obtain three-dimensional images of the microstructure of cement paste (water-to-cement mass ratio of 0.5) at different ages. By using the Amira software, component phases of the cement paste such as pores, hydration products, and unhydrated clinker particles were segmented from each other based on their 3D image grey levels; their relative contents were also calculated with the software, and the data are 61.2%, 0% and 38.8% at the beginning of hydration and 11.8%, 78.5% and 9.7% at 28 d age, respectively. The hydration degree of cement paste at different ages was compared with the experimental data acquired by loss on ignition (LOI) tests. The results show that the calculated and measured data reasonably agree with each other, which indicates that micro-CT is a useful and reliable approach to characterize the micro structure evolution of hydrating cement paste.

Keywords

Micro computed tomography (Micro-CT) / 3D image / microstructure / cement paste

References

[1] MonteiP J M, KirchheimA P, ChaeS, FischerP, MacdowellA A, SchaibleE, WenkH R. Characterizing the nano and micro structure of concrete to improve its durability [J]. Cement & Concrete Composites, 2009, 31: 577-584

[2] SugiyamaT, RitthichauyW, TsujiY. Experimental investigation and numerical modeling of chloride penetration and calcium dissolution in saturated concrete [J]. Cement and Concrete Research, 2008, 38: 49-67

[3] MostafaN Y, MohsenQ, El-HemalyS A S, El-KorashyS, BrownP W. High replacements of reactive pozzolan in blended cements: Microstructure and mechanical properties [J]. Cement & Concrete Composites, 2010, 32: 386-391

[4] ZhangY-s, SunW, LiZ-jin. Preparation and microstructure characterization of poly-sialate-disiloxo type of geopolymeric cement [J]. Journal of Central South University of Technology, 2009, 16: 906-913

[5] KatzA, BenturA, KovlerK. A novel system for in-situ observations of early hydration reactions in wet conditions in conventional SEM [J]. Cement and Concrete Research, 2007, 37: 32-37

[6] GoňiS, GuerreroA. SEM/EDX characterization of the hydration products of belite cements from class C coal fly ash [J]. Journal of the American Ceramic Society, 2007, 90: 3915-3922

[7] VenkiteelaG, SunZ. In situ observation of cement particle growth during setting [J]. Cement & Concrete Composites, 2010, 32: 211-218

[8] ZengQ, LiK-f, TeddyC, PatrickD. Pore structure characterization of cement pastes blended with high-volume fly-ash [J]. Cement and Concrete Research, 2012, 42: 194-204

[9] ZhouJ, YeG, BreugelK V. Characterization of pore structure in cement-based materials using pressurization-Depressurization cycling mercury intrusion porosimetry (PDC-MIP) [J]. Cement and Concrete Research, 2010, 40: 1120-1128

[10] KumarR, BhattacharjeeB. Study on some factors affecting the results in the use of MIP method in concrete research [J]. Cement and Concrete Research, 2003, 33(3): 417-424

[11] DiamondS. Mercury porosimetry, an inappropriate method for the measurement of pore size distributions in cement-based materials [J]. Cement and Concrete Research, 2000, 30(10): 1517-1525

[12] GallucciE, ScrivenerK, GrosoA, StampanoniM, MargaritondoG. 3D experimental investigation of the microstructure of cement pastes using synchrotron X-ray microtomography [J]. Cement and Concrete Research, 2007, 37: 360-368

[13] DiamondS, LandisE. Microstructural features of a mortar as seen by computed microtomography [J]. Materials and Structures, 2007, 40: 989-993

[14] AshebridgeD A, ThorneM S, RiversM L, MuccinoJ C, O’DayP A. Image optimization and analysis of synchrotron X-ray computed microtomography (CuT) data [J]. Computers and Geosciences, 2003, 29(7): 823-836

[15] LuS, LandisE N, KeaneD T. X-ray microtomographic studies of pore structure and permeability in Portland cement concrete [J]. Materials and Structures, 2006, 39(6): 611-620

[16] StockS RMicrocomputed tomography: Methodology and applications [M], 2009New YorkCRC press336-345

[17] PromentillaM A B, SugiyamaT, HitomiT, TakedaN. Characterizing the 3D pore structure of hardened cement paste with synchrotron microtomography [J]. Journal of Advanced Concrete Technology, 2008, 6(2): 273-286

[18] WillisK L, AbellA B, LangeD A. Image-based characterization of cement pore structure using wood’s metal intrusion [J]. Cement and Concrete Research, 1998, 28(12): 1695-1705

[19] OlsonR, NeubauerC, JenningsH. Damage to the pore structure of hardened Portland cement paste by mercury intrusion [J]. Journal of the American Ceramic Society, 1997, 80(9): 2454-2458

[20] FengX, GarbocziE J, BentzD P, StutzmanP E, MasonT O. Estimation of the degree of hydration of blended cement pastes by a scanning electron microscope point-counting procedure [J]. Cement and Concrete Research, 2004, 34(10): 1787-1793