Mechanical properties of 3D carbon/carbon composites by nanoindentation technique

Abstract

Nanoindentation tests were conducted to investigate the near-surface mechanical properties of the individual components (fiber and matrix) for three-dimensional reinforced carbon/carbon composites (3D C/C). Optical microscope and polarizing light microscope were used to characterize the microstructure of 3D C/C. The microscopy results show that large number of pores and cracks exist at both bundle/matrix interface and pitch carbon matrix. These defects have important effect on the mechanical behavior of 3D C/C. The in situ properties for components of 3D C/C were acquired by nanoindentation technique. Relative to the matrix sample, the fiber samples have more larger values for modulus, stiffness and hardness. However, there is no significant difference of modulus and stiffness among fiber samples with different directions.

Keywords

C/C composites / mechanical properties / nanoindentation / microstructure

References

[1] XuH.-j., XiongX., YiM.-z., HuangB.-y., WangHui.. Thermal conductivity properties of carbon/carbon composites with thin felt laminate at high temperature [J]. Journal of Central South University: Science and Technology, 2008, 39(3): 500-505

[2] GeY.-c., YiM.-z., TuX.-d., PengKe.. To-fro sliding tribological behavior of C/C composite under different loads [J]. Journal of Central South University: Science and Technology, 2010, 41(1): 114-119

[3] LeiB.-l., YiM.-z., XuH.-juan., RanL.-p., GeY.-c., PengKe.. Raman spectroscopy investigation of structural and textural change in C/C composites during braking [J]. Journal of Central South University of Technology, 2011, 18(1): 29-35

[4] SavageG.Carbon-carbon composites [M], 1993, London, Chapman and Hall: 101-105

[5] FischerA. C.Nanoindentation [M], 2004, New York, Springer-Verlag: 2-3

[6] JakesJ. E., FrihartC. R., BeecherJ. F., MoonR. J., StoneD. S.. Experimental method to account for structural compliance in nanoindentation measurements [J]. Journal of Materials Research, 2008, 23: 1113-1127

[7] LeeS. H., WangS. Q., PharrG. M., XuH. T.. Evaluation of interphase properties in a cellulose fiber-reinforced polypropylene composite by nanoindentation and finite element analysis [J]. Composites: Part A-Applied Science and Manufacturing, 2007, 38: 1517-1524

[8] KonnerthJ., VallaA., GindlW.. Nanoindentation mapping of a wood-adhesive bond [J]. Applied Physics A-Materials Science & Processing, 2007, 88: 371-375

[9] LiW. H., ShinK., LeeC. G., WeiB. C., ZhangT. H., HeY. Z.. The characterization of creep and time-dependent properties of bulk metallic glasses using nanoindentation [J]. Materials Science and Engineering A, 2008, 478: 371-375

[10] LI Rui-zhi, LI Ya-di, SU Jun-ming, CUI Hong, SU Zhe-an, ZHOU Shao-jian. Study of the properties of axial rod 4D woven C/C composite [C]// Eurocarbon’98. Strasbourg, France: 1998: 110.

[11] OliverW. C., PharrG. M.. An improvement technique for determining hardness and elastic modulus using load and displacement sensing indentation experiments [J]. Journal of Materials Research, 1992, 7: 1564-1583

[12] KanariM., TanakaK., BabaS., EtoM.. Nanoindentation behaviour of a two-dimensional carbon-carbon composite for nuclear applications [J]. Carbon, 1997, 35: 1429-1437

[13] MarxD. T., RiesterL.. Mechanical properties of carbon-carbon composite components determined using nanoindentation [J]. Carbon, 1999, 37: 1679-1684

[14] ChammsC. C.WeetonJ. W., PetelsD. M., ThomasK. L.Engineers guide to composite materials [M], 1987, Ohio, American Society of Metals: 3-11

[15] HAY J L, PHARR G M. Instrumented indentation testing [S]. ASM Handbook, 2000: 232–243.

[16] GongJ.-h., MiaoH.-z., PengZ.-jian.. On the contact area for nanoindentation tests with Berkovich indenter: case study on soda-lime glass [J]. Materials Letter, 2004, 58: 1349-1353

[17] LemoineP., QuinnJ. P., MaguireP., MaclaughlinJ. A.. Comparing hardness and wear data for tetrahedral amorphous carbon and hydrogenated amorphous carbon thin films [J]. Wear, 2004, 257: 509-522