Establishment of wear model and life prediction of drum of hot rolling coiler

Abstract

For the drum of hot rolling coiler is prone to be easily destroyed, the type of MMU-5G abrasion tester was applied to revealing the friction and wear behavior. The morphology observation by scanning electron microscope (SEM) demonstrates the wear mechanism of the drum, and the test data of the influence coefficient of the normal pressure, relative sliding speed and surface lubrication conditions acted on the linear rate of the wear could be obtained by the regression method. A calculation model, which considers the factors of the structure of the drum, coiling tension and coiling strip specifications, was established by the combination method to predict the wear life of the drum. Then the practical production data was applied into this model and the analysis result was in good accordance with that of actual production.

Keywords

drum / wear mechanism / combination method / wear model / wear life

References

[1] ZouJ.-xiang.The rolling and machinery [M], 2000, Beijing, Metallurgical Industry Press: 401-423

[2] DongH.-h., JiangZ.-hua.. HVOF technology and application of the surface treatment for sector plate [J]. World Iron and Steel, 2010, 10(3): 55-59

[3] QuinnT. F. J.. The role of wear in the failure of common tribosystems [J]. Wear, 1984, 100(3): 399-436

[4] FengX.-z., WangY., LiuCai.. Research of distribution of friction force and displacement field in hot strip during coiling [J]. Iron and Steel, 2008, 43(3): 57-60

[5] JinG.-ling.. Analysis of abrasion of coiler mandrel expanding mechanism in hot strip mill [J]. Metallurgical Equipment, 2009, 178(6): 63-65

[6] WenS.-z., HuangPing.Principles of tribology [M], 2008, Beijing, Tsinghua University Press: 259-309

[7] CuiX.-h., WangS.-q., JiangQ.-chuan.. High-temperature wear mechanism of cast hot-forging die steel 4Cr3Mo2NiV [J]. Acta Metallurgica Sinica, 2005, 41(10): 1116-1120

[8] GengH.-r., CuiF., TianX.-fa.. Processing technique and sliding friction and wear behavior of TiB2/ZA27 composite [J]. J Cent South Univ Technol, 2005, 12(2): 141-144

[9] LiC.-s., LiuX.-h., WangG.-dong.. New method for evaluating thermal wear of rolls in rolling process [J]. Journal of Iron and Steel Research, International, 2008, 15(6): 52-55

[10] LiuY., LiuS.-q., WangS.-xing.. Microstructure and abrasion wear behavior of Ni-based laser cladding alloy layer at high temperature [J]. J Cent South Univ Technol, 2005, 12(4): 403-405

[11] WangZ.-s., GuoJ.-t., ZhouL.-zhang.. High temperature wear behavior of NiAl-Cr(Mo)-Ho-Hf eutectic alloy [J]. Acta Metallurgica Sinica, 2009, 45(3): 297-301

[12] WangS.-q., ChenK.-m., CuiX.-hong.. Effect of alloying elements on thermal wear of cast hot-forging die steels [J]. Journal of Iron and Steel Research, International, 2006, 13(5): 53-59

[13] DongG.-n., HuaM., LiJian.. Tribological behaviors of spot-textured TiN coatings on M2 high-speed steel under boundary lubricated conditions [J]. Journal of University of Science and Technology, 2007, 14(4): 350-355

[14] ZhouG.-ying.The finishing equipment of strip [M], 1982, Beijing, Machinery Industry Press: 41-47

[15] LudemaK. C.. Mechanism-based modeling of friction and wear [J]. Wear, 1996, 200(1): 1-7

[16] PetersonM. B., WinerW. O.WangY.-l.Wear control hand book [M], 1994, Beijing, Machinery Industry Press: 309-374

[17] SuhN. P.. The delamination theory of wear [J]. Wear, 1973, 25(1): 111-124