In-situ measurement of elastic modulus for ceramic top-coat at high temperature

Abstract

The ceramic thermal barrier coatings (TBCs) play an increasingly important in advanced gas turbine engines because of their ability to further increase the engine operating temperature and reduce the cooling, thus help achieve future engine low emission, high efficiency and improve the reliability goals. Currently, there are two different processes such as the plasma spraying (PS) and the electron beam-physical vapor deposition (EB-PVD) techniques. The PS coating was selected to test the elastic modulus. Using the nanoindentation and resonant frequency method, the mechanical properties of ceramic top-coat were measured in-situ. According to the theory of the resonant frequency and composite beam, the testing system was set up including the hardware and software. The results show that the accurate characterization of the elastic properties of TBCs is important for stress-strain analysis and failure prediction. The TBCs systems are multi-layer material system. It is difficult to measure the elastic modulus of top-coat by tensile method. The testing data is scatter by nanoindentation method because of the microstructure of the ceramic top-coat. The elastic modulus of the top-coat between 20–1 150 °C is obtained. The elastic modulus is from 2 to 70 GPa at room temperature. The elastic modulus changes from 62.5 GPa to 18.6 GPa when the temperature increases from 20 °C to 1 150 °C.

Keywords

thermal barrier coatings / plasma spraying / resonant frequency / elastic modulus

References

[1] ZhuD., MilerR. A.. Thermophysical and thermomechanical properties of thermal barrier coatings system [J]. Ceram Eng Sci, 2000, 21: 623-633

[2] EvansA. G., HutchinsonJ. W.. Thermal barrier coatings for advanced gas-turbine engines [J]. MRS Bulletin, 2000, 27: 43-47

[3] QiH.-y., YangX.-guang.. Oxidation damage of APS thermal barrier coatings under high temperature [J]. Journal of Rare Earths, 2006, 324/325: 595-598

[4] JohnsonC. A., RuudJ. A.. Relationships between residual stress, microstructure and mechanical properties of electron beam-physical vapor deposition thermal barrier [J]. Surface and Coating Technology, 1998, 34: 80-85

[5] PomeroyM. J.. Coatings for gas turbine materials and long term stability issues [J]. Materials and Design, 2005, 26: 223-231

[6] RYBICKI E F, SHADLEY J R. In situ evaluations of Young’s modulus and Poission’s rate using a cantilever beam specimen [C]// Proceedings of the 8th national thermal spray conference. Houston, 1995.

[7] YangL., ZhouY.-chun.. Wavelet analysis of acoustic emission signals from thermal barrier coatings [J]. Trans Nonferrous Met Soc China, 2007, 17(3): 871-873

[8] MnmmD. R., WatanabeM., EvansA. G., PfaendtnerJ. A.. The influence of test method on failure mechanisms and durability of a thermal barrier system [J]. Acta Materialia, 2004, 52: 1123-1131

[9] LiM.-h., SunX.-f., HuW.-y., GuanH.-rong.. Thermal shock behavior of EB-PVD thermal barrier coatings [J]. Surface and Coatings Technology, 2007, 201: 7387-7391

[10] QiH.-y., ZhouL.-zhu.. Measurement of Young’s modulus and Poission’s rate of thermal barrier coating [J]. Chinese Journal of Aeronautics, 2005, 18(2): 180-183

[11] ThompsonJ. A., ClyneT. W.. The effect of heat treatment on the stiffness of zirconia top coats in plasma-sprayed TBCs [J]. Acta Mater, 2001, 49: 1565-1575

[12] OliverW. C., PharrG. M.. An improved technique for determining hardness and elastic modulus using load and displacement sensing indentation experiment [J]. J Mater Res, 1992, 12: 17-28

[13] JangB. K., HideakiM.. Influence of porosity on hardness and Young’s modulus of nanoporous EB-PVD TBCs by nanoindentation [J]. Materials Letters, 2005, 59: 3462-3466

[14] TaoL., ChenF., DingH.-d., HanD.-feng.. Properties of plasma sprayed NiCrAlY+(ZrO₂+Y₂O₃) coating on refractory steel surface [J]. Journal of Central South University of Technology, 2005, 12(suppl.2): 246-249

[15] QiH.-y., LiRui.. Thermal fatigue life of thermal barrier coatings [J]. Journal of Rare Earths, 2007, 25: 370-374

[16] ZhaoX., XiaoP.. Residual stresses in thermal barrier coatings measured by photoluminescence piezospectroscopy and indentation technique [J]. Surface and Coatings Technology, 2006, 201: 1124-1131

[17] BouzakisK. D., LontosA.. Determination of mechanical properties of electron beam-physical vapor deposition-thermal barrier coatings (EB-PVD-TBCs) by means of nanoindentation and impact testing [J]. Surface and Coatings Technology, 2003, 163/164: 75-80