Photoluminescence properties of ZnO thin films prepared by DC magnetron sputtering

Abstract

ZnO thin films were prepared by direct current(DC) reactive magnetron sputtering under different oxygen partial pressures. And then the samples were annealed in vacuum at 450 °C. The effects of the oxygen partial pressures and the treatment of annealing in vacuum on the photoluminescence and the concentration of six intrinsic defects in ZnO thin films such as oxygen vacancy(V_O), zinc vacancy(V_Zn), antisite oxygen(O_Zn), antisite zinc(Zn_O), interstitial oxygen(O_i) and interstitial zinc(Zn_i) were studied. The results show that a green photoluminescence peak at 520 nm can be observed in all the samples, whose intensity increases with increasing oxygen partial pressure; for the sample annealed in vacuum, the intensity of the green peak increases as well. The green photoluminescence peak observed in ZnO may be attributed to zinc vacancy, which probably originates from transitions between electrons in the conduction band and zinc vacancy levels, or from transitions between electrons in zinc vacancy levels and up valence band.

Keywords

ZnO thin films / photoluminescence / zinc vacancy / magnetron sputtering

References

[1] TangZ. K., WongG. K. L., YuP.. Room-temperature ultraviolet laser emission from self-assembled ZnO microcrystallite thin films [J]. Appl Phys Lett, 1998, 72(25): 3270-3272

[2] LeeS., ImY. H., KimS. H., HahnY. B.. Structural and optical properties of high quality ZnO films on Si grown by atomic layer deposition at low temperatures [J]. Superlattices and Microstructures, 2006, 39(1/4): 24-32

[3] LimS. H., KimJ. W., KangH. S., KimG. H., CangH. W., LeeS. Y.. Characterizations of phosphorus doped ZnO multi-layer thin films to control carrier concentration [J]. Superlattices and Microstructures, 2005, 38(4/6): 377-384

[4] BurovaL. I., PetukhovD. I., EliseevA. A., LukashinA. V., TretyakovY. D.. Preparation and properties of ZnO nanoparticles in the mesoporous silica matrix [J]. Superlattices and Microstructures, 2006, 39(1/4): 257-266

[5] FanX.-m., LianJ.-s., GuoZ.-x., JiangQing.. Surface morphology and photoluminescence properties of ZnO thin films obtained by PLD [J]. Trans Nonferrous Met Soc China, 2005, 15(3): 519-523

[6] LuQ.-f., WeiH.-x., HuZ.-dong.. ZnO nanoneedles fabricated by a simple approach and their optical properties [J]. Trans Nonferrous Met Soc China, 2004, 14(5): 973-976

[7] XuX. L., LauS. P., ChenJ. S., ChenG. Y., TayB. K.. Polycrystalline ZnO thin films on Si(100) deposited by filtered cathodic vacuum arc [J]. Journal of Crystal Growth, 2001, 223(1/2): 201-205

[8] KimC., ParkA., PrabakarK., LeeC.. Physical and electronic properties of ZnO:Al/porous silicon [J]. Materials Research Bulletin, 2006, 41(2): 253-259

[9] GaoH.-y., ZhuangH.-z., XueC.-s., DongZ.-h., HeJ.-t., LiuY., WuY.-x., TianD.-heng.. Fabrication of GaN films through reactive reconstruction of magnetron sputtered ZnO/Ga₂O₃ [J]. Journal of Central South University of Technology, 2005, 12(1): 9-12

[10] LiH.-q., NingZ.-y., ChengS.-h., JiangM.-fu.. Photoluminescence centers and shift of ZnO films deposited by RF magnetron sputtering [J]. Acta Physica Sinaca, 2004, 53(3): 867-870

[11] LiuX., WuX.-h., CaoH., ChangR. P. H.. Growth mechanism and properties of ZnO nanorods synthesized by plasma-enhanced chemical vapor deposition [J]. J Appl Phys, 2004, 95(6): 3141-3147

[12] ZuP., TangZ. K., WongG. K. L., KawasakiM., OhtomoA., KoinumaH., SegawaY.. Ultraviolet spontaneous and stimulated emissions from ZnO microcrystallite thin films at room temperature [J]. Solid State Commun, 1997, 103(8): 459-463

[13] ChoS., MaJ., KimY., SunY., GeorgeK. L. W., JohnB. K.. Photoluminescence and ultraviolet lasing of polycrystalline ZnO thin films prepared by the oxidation of the metallic Zn [J]. Appl Phys Lett, 1999, 75(18): 2761-2763

[14] BagnallD. M., ChenY. F., ShenM. Y., ZhuZ., GotoT., YaoT.. Room temperature excitonic stimulated emission from zinc oxide epilayers grown by plasma-assisted MBE [J]. Journal of Crystal Growth, 1998, 174(184/185): 605-609

[15] KohanA. F., CederG., MorganD.. First-principles study of native point defect in ZnO [J]. Physical Review B, 2000, 61(22): 15019-15027

[16] ReynoldsD. C., LookD. C., JogaiB., MorkoçH.. Similarities in the band edge and deep-centre photoluminescence mechanisms of ZnO and GaN [J]. Solid State Commun, 1997, 101(9): 643-646

[17] LiuM., KitaiA. H., MascherP.. Point defects and luminescence centers in zinc oxide and zinc oxide doped with manganese [J]. Journal of Luminescence, 1992, 54(1): 35-42

[18] LüJ.-g., YeZ.-z., HuangJ.-y., ZhaoB.-h., WangLei.. Influence of postdeposotion annealing on crystallinity of zinc oxide films [J]. Chinese Journal of Semiconductors, 2003, 24(7): 729-736

[19] BylanderE. G.. Surface effects on the low-energy cathodoluminescence of zinc oxide [J]. J Appl Phys, 1978, 49(3): 1188-1195

[20] XuP.-s., SunY.-m., ShiC.-shu.. Native point defect states in ZnO [J]. Chin Phys Lett, 2001, 18(9): 1252-1253