Relationship between interfacial structure and property of steel-mushy Al-28Pb bonding pate

Abstract

The interfacial properties of steel-mushy Al-28Pb bonding plate with different interfacial structures, and the influence of ratio of Fe-Al compound at the interface on interfacial shear strength were investigated. The results show that there is a nonlinear relationship between the ratio of Fe-Al compound at the interface and the interfacial shear strength. When the ratio of Fe-Al compound at the interface is smaller than 71.4%, with the increase of the ratio of Fe-Al compound at the interface, the interfacial shear strength increases gradually; when the ratio of Fe-Al compound at the interface is larger than 71.4%, with the increase of the ratio of Fe-Al compound at the interface, the interfacial shear strength decreases continuously; when the ratio of Fe-Al compound at the interface is 71.4%, the largest interfacial shear strength 70.2 MPa is obtained.

Keywords

interfacial structure / ratio of Fe-Al compound / interfacial shear strength

References

[1] KennethBMetal base composite material[M], 1982, Beijing, National Defense Industry Press

[2] DavisJ RAluminum and aluminum alloys[M], 1993, Ohio, Materials Park

[3] ZhangPeng, DuYun-hui. Relationship between solid fraction and distribution of Pb in Al-Pb ingot[J]. Trans Nonferr Metal Soc, 2001, 11(3): 409-412

[4] SUN Da-ren, ZHANG Ming-zhe. Fabrication and microstructure of casting Al-Pb sliding bearing alloy[J]. Journal of Special Casting and Nonferrous Metal, 1998 (5): 24–26. (in Chinese)

[5] Pathak J P, Malhotra S L. Production of high-lead aluminum by impeller mixing [J]. Met Tech, 1979 (11): 442–448.

[6] MohanS, RayS. The effect of lead content on wear characteristic of Astir-cast Al-Pb alloy [J]. Wear, 1990, 140: 83-92

[7] LuoZhong-anThe Study on rolling forming of steel-backed Al-Pb alloy bearing [D], 1993, Shenyang, Northeastern University(in Chinese)

[8] LepperK, ChashechkinaJ. Sliding behavior of selected aluminum[J]. Wear, 1997, 203: 46-56

[9] ZhangPeng, DuYun-hui. Modeling and optimizing of steel and mushy Al-28Pb alloy bonding[J]. Trans Nonferr Metal Soc, 2001, 11(2): 239-243

[10] ZhangPeng, DuYun-hui. Relationship between solid fraction of slurry and property of steel/mushy Al-20Sn semi-solid bonding[J]. Trans Nonferr Metal Soc, 2002, 12(5): 914-917

[11] ZhangPeng, DuYun-hui. Semi-solid processing of steel-Al-7 graphite binding plate[J]. Journal of Wuhan University of Technology-Materials Science Edition, 2002, 17(3): 46-49

[12] ZhangPeng, DuYun-hui. Semi-solid pressing bonding strength between steel and Cu-graphite composite[J]. Journal of Materials Science & Technology, 2005, 21(2): 265-268

[13] ZhangPeng, DuYun-hui. Preparation of QTi4. 3–4 graphite by semi-solid casting technology[J]. Journal of Wuhan University of Technology-Materials Science Edition, 2005, 20(4): 69-72

[14] NetaT. Structure analysis of hot impregnated Al-Si coating[J]. Met Surface Technol, 1982, 33: 537-540

[15] ZhangPeng, DuYun-hui. Interface of solid steel and liquid aluminum under nonequilibrium diffusion [J]. Trans Nonferr Metal Soc, 2000, 10(3): 389-392

[16] FangJun-xinSolid physics[M], 1980, Shanghai, Shanghai Science and Technology Press(in Chinese)