Influence of potential on structure and properties of microarc oxidation coating on Mg alloy

Abstract

In order to obtain optimizing microarc oxidation coating on Mg alloy from a friendly-enviormental electrolyte free of Cr⁶⁺ and PO₄³⁻, constant potential regime was applied to produce it. The influence of potential on the morphology, composition, structure and other properties, such as microhardness and corrosion resistance were investigated by scanning electron microscopy (SEM), energy dispersive spectroscope (EDS), X-ray diffraction (XRD), hardness tester and electrochemical method. The results clearly show that oxidation potential plays an important role in the formation of coating’s structure and properties. The microarc oxidation coating is smooth and white, which consists of two layers. The external layer is loose and porous and enriched in Al and Si. Moreover, its content of Al and Si increases with the increasing operated potential. While the inner layer is compact and the content of Al and Si are lower than that of the external layer. The coating is composed of several phases and the major phases are MgAl₂O₄ and MgO, and the minor phases are Al₂O₃ and SiO₂ when the potential is higher. The microhardness of coating is obtained the maximum at the potential of 45 V, so does the corrosion resistance.

Keywords

microarc oxidation / magnesium alloy / structure / property

References

[1] EifertA J, ThomasJ P, RateickR G. Influence of anodization on the fatigue life of WE43A-T6 magnesium[J]. Scripta Materialia, 1999, 40(8): 929-935

[2] AbulsainM, BerkaniA, BonillaF A. Anodic oxidation of Mg-Cu and Mg-Zn alloys [J]. Electrochim Acta, 2004, 49(6): 929-935

[3] ZozulinJ A, BarcakE. Anodic oxidation for Mg alloy[J]. Metal Finishing, 1994, 92(3): 39-44

[4] ChongK Z, ShihT S. Conversion-coating treatment for magnesium alloys by a permanganate-phosphate solution[J]. Materials Chemistry and Physics, 2003, 80(1): 191-200

[5] Gonzalez-nunezM A, Nunez-lopezC A, SkeldonP, et al.. A non-chromate conversion coating for Mg alloy and Mg-based metal matrix composites[J]. Corrosion Science, 1995, 37(11): 1763-1772

[6] HaoJian-min, ChenHong, ZhangRong-jun, et al.. Corrosion resistance of Mg alloy microarcoxidization ceramic coating[J]. The Chinese Journal of Nonferrous Metals, 2003, 13(4): 988-991(in Chinese)

[7] ApelfeldA V, BespalovaO V, BorisovA M, et al.. Application of the particle backscattering methods for the study of new oxide protective coatings at the surface of Al and Mg alloys[J]. Nuclear Instruments and Methods in Physics Research B, 2000, 161–163(3): 553-557

[8] SharmaA K, SureshM R, BhojrajH, et al.. Electroless nickel plating on Mg alloy[J]. Metal Finishing, 1998, 96(3): 10-18

[9] RajanA, ZhouW. Electroless nickel-plating on AZ91D magnesium alloy: effect of substrate microstructure and plating parameters[J]. Surface and Coatings Technology, 2004, 179(2–3): 124-134

[10] YinJian-jun, LiYuan-dong, LiangWei-dong, et al.. Investigation of pretreatment process with zinc plating for Mg alloy electroplating[J]. Journal of Gansu University of Technology, 2003, 29(1): 36-38(in Chinese)

[11] TruongV T, LaiP K, MooreB T, et al.. Corrosion protection of magnesium by electroactive polyprroler/paint coatings [J]. Synthetic Methods, 2000, 110(1): 7-15

[12] WeiZhong-ling, ChenQin-rong, GuoXin-cong, et al.. Microstructure and corrosion resistance of ceramic coating on magnesium alloys [J]. Materials Protection, 2003, 36(10): 21-23