Cerium enrichment on sinter skin of mischmetal doped WC-Co cemented carbide

Abstract

Rare earth-doped WC-Co cemented carbides with low carbon-containing level were prepared by adding mischmetal (mainly containing lanthanum and cerium) in the form of cobalt pre-alloyed powder during ball-milling. After sintering, the sinter skin (exterior) was observed and analyzed by scanning electron microscopy (SEM) and energy disperse X-ray spectroscopy (EDXS). The results show that during the sintering process lanthanum and cerium are separated and cerium predominantly migrates towards the surface forming precipitates containing oxygen. Thermodynamic analysis and polarization of cerium atom caused by the strong interaction between cerium atoms and high energy carbon atoms were used in explaining the observed phenomenon.

Keywords

hardmetal / lanthanum / cerium / atom polarization thermoldynamics / enrichment

References

[1] Dübel W, Flurschütz W, Kohlermann R. Hard Metal Alloy[P]. UK 1 077 921, 1967.

[2] XuChong-hai, AiXing, HuangChuan-zhen. Research and development of rare-earth cemented carbides[J]. International Journal of Refractory Metals & Hard Materials, 2001, 19(3): 159-168

[3] ChenLi-min, LinCheng-guang, GerhardG, et al.. Rare earth elements (RE) doped cemented carbides [J]. P/M Science & Technology Briefs, 1999, 1(5): 11-15

[4] XiongJi, YangJian-gao, GuoXing-hua. Application of rare earth elements in cemented carbide inserts, drawing dies and mining tools[J]. Materials Science and Engineering A, 1996, A209: 287-293

[5] ZhangLi, ChenShu. Rare earth elements doped new cemented carbide with Ni-Co binder for mining [J]. Journal of Central South University of Technology, 2000, 7(3): 143-145

[6] WangYou-ming, HeCong-xun, ZhaoBo-lan, et al.. Cemented carbides with rare earth in China[J]. Chinese Tungsten Industry, 1999, 14(5–6): 186-194(in Chinese)

[7] YuanYi, WangXing-yi, WuYing-fang. Mechanism of improving the wearability of WC78-TiC14-Co8 cemented carbide with yttrium addition[J]. Journal of Rare Earths, 1997, 15(4): 276-281

[8] ZhangLi, SchubertW D, HuangBai-yun, et al.. Surface observation of rare earth doped cemented carbide[J]. P/M Science & Technology Briefs, 2003, 5(3): 17-21

[9] ZhangLi, SchubertW D, ChenShu, et al.. Rare earth enrichment phenomenon during the sintering process of grainy hardmetal[J]. Materials Science and Engineering A, 2004, 384(1–2): 395-401

[10] ZHANG Li, CHEN Shu, HUANG Bai-yun, et al. Separation phenomenon of La and Ce during the sintering process of rare earth doped cemented carbides [A]. Kneringer G, Rödhammer P, Wildner H. Proceedings of the 16th International Plansee Seminar [C]. Reutte: Plansee Holding AG, 2005. 574–587.

[11] BrookesK J A. Rock tools lead the way in drilling [J]. Metal Powder Report, 1992, 47(12): 48-51

[12] LiZheng-wei, HeYe-dong, QiHui-bin, et al.. Diagrams on the standard free energy change per unit volume for the formation of oxide, sulfide, carbide, nitride[J]. The Chinese Journal of Nonferrous Metals, 1998, 8(S1): 55-60(in Chinese)

[13] Metal Department of Zhong Shan UniversityData on the Physics and Chemistry of Rare Earths[M], 1978, Beijing, Metallurgy Industry Press(in Chinese)

[14] JiZhe-sheng, XiaLi-fang, WanHai-bo, et al.. Phase composition of initial rare earth-B-Al permeation layer[J]. The Chinese Journal of Nonferrous Metals, 1998, 8(S1): 66-69(in Chinese)

[15] KolaskaH, HirschfeldD, GreweHPowder Metallurgy of Hardmetals-Lecture 9-Testing of Hardmetals [M], 1995, Shrewsbury, EPMA: 9122-9122