Effect of nitrocarburizing on sulphide layer during nitrocarburizing-sulphurating treatment

Abstract

Compared with the single sulphurating treatment, the duplex treatment of nitrocarburizing-sulphurating can more effectively improve the properties of steel such as friction-reducing, wear resistance and anti-scuffing. Under the same processing parameters, the sulphide layers were fabricated on the surface of CrMoCu alloy cast iron by single ion-sulphurating treatment and nitrocarburizing-sulphurating duplex treatment, respectively. Through the analysis of the sulphide, the effect of the nitrocarburizing on the fabrication of the sulphide layer was investigated. And the result shows that the fabrication of sulphide layer is promoted by the nitrocarburizing treatment.

Keywords

nitrocarburizing-sulphurating / duplex treatment / sulphide layer

References

[1] XuBin-shi, ZhuShao-hua, LiuShi-can, et al.Theories and Technologies on Surface Engineering [M], 1999, Beijing, National Defence Industry Press(in Chinese)

[2] ZhangNing, ZhuangDa-ming, LiuJia-jun, et al.. Tribological behaviors of the duplex-treated surface by ionnitrocarburizing+ion-sulphurizing [J]. China Surface Engineering, 2000, 13(2): 18-22(in Chinese)

[3] MaShi-ning, HuChun-hua, LiXin, et al.. Study on friction and wear characteristics and structure of compound layer from combined treatment of ion nitrcarburizing-ion sulphurizing of CrMoCu alloy cast iron [J]. Transactions of Materials and Heat Treatment, 2004, 25(5): 649-652

[4] QuBao-jian, WangXiu-chun, LiHong-min, et al.. Study on microscopical constitution of sulphurized layer and technology for low temperature ion-sulphurizing [J]. Shangdong Science, 1998, 11(3): 22-25(in Chinese)

[5] ZhangDe-yuan, PengWen-yi, FuQing-feng, et al.. Effects and mechanism of carbon on ion nitrocarburizing[J]. Metal Heat Treatment, 1998, 10: 26-27(in Chinese)