The effect of urea pretreatment on the formaldehyde emission and properties of straw particleboard

Abstract

For manufacturing low-formaldehyde emission particleboard from wheat straw and urea-formaldehyde (UF) resins using urea treatment for indoor environments, we investigated the influence of urea treatment on the formaldehyde emission, physical and mechanical properties of the manufactured particleboard. Wheat straws were treated at three levels of urea concentration (5%, 10%, 15%) and 95°C as holding temperature. Wheat straw particleboards were manufactured using hot press at 180°C and 3 MPa with two types of UF adhesive (UF-45, UF-91). Then the formaldehyde emission values, physical properties and mechanical properties were considered. The results show that the formaldehyde emission value was decreased by increasing urea concentration. Furthermore, the results indicate that the specimens under urea treatment have better mechanical and physical properties compared with control specimens. Also specimens under urea treatment at 10% concentration and UF-91 type adhesive have the most optimum physical and mechanical strength.

Keywords

formaldehyde emission / physical and mechanical properties / wheat straw particleboard / Urea formaldehyde resin

References

[1] Boquillon N., Elbez G., Schonfeld U.. Properties of wheat straw particleboards bonded with different types of resin. Journal of Wood Science, 2004, 50(3): 230-235.

[2] Cöpür Y., Güler C., Tascioğlu C., Tozluoğlu A.. Incorporation of hazelnut shell and husk in MDF production. Bioresource Technology, 2008, 99(15): 7402-7406.

[3] Dunky M, Pizzi A, Leemput MV. 2002. Wood adhesion and glued products. Report on the State of the Art, COST Action E13 — WG 1, 1st Edition.

[4] Dunky M.. Urea-formaldehyde (UF) adhesive resins for wood. International Journal of Adhesion and Adhesives, 1998, 18(2): 95-107.

[5] EN 310. Wood-based panels, determination of modulus of elasticity in bending and bending strength. 1993, Brussels, Belgium: European Committee for Standardization

[6] EN 317. Particleboards and fibreboards, determination of swelling in thickness after immersion. 1993, Brussels, Belgium: European Committee for Standardization

[7] EN 319. Particleboards and fibreboards, determination of tensile strength perpendicular to plane of the board. 1993, Brussels, Belgium: European Committee for Standardization

[8] EN 717-3. Wood-based panels, Determination of formaldehyde release by the flask method. 1996, Brussels, Belgium: European Committee for Standardization

[9] Han G., Umemura K., Zhang M., Honda T., Kawai S.. Development of high-performance UF-bonded reed and wheat straw medium-density fiberboard. Journal of Wood Science, 2001, 47(5): 350-355.

[10] Han G., Umemura K., Kawai S., Kajita H.. Improvement mechanism of bondability in UF-bonded reed and wheat straw boards by silane coupling agent and extraction treatments. Journal of Wood Science, 1999, 45(4): 299-305.

[11] Mo X., Cheng E., Wang D., Sun X.. Physical properties of medium-density wheat straw particleboard using different adhesives. Industrial Crops and Products, 2003, 18(1): 47-53.

[12] Mo X., Hu J., Sun X., Ratto J.. Compression and tensile strength of low-density straw-protein particleboard. Industrial Crops and Products, 2001, 14(1): 1-9.

[13] Nemli G., Öztürk I.. Influences of some factors on the formaldehyde content of particleboard. Building and Environment, 2006, 41(6): 770-774.

[14] Pizzi A.. Wood Adhesives Chemistry and Technology. 1983, New York, USA: Marcel Dekker, Inc.

[15] Sekine Y., Nishimura A.. Removal of formaldehyde from indoor air by passive type air-cleaning materials. Atmospheric Environment, 2001, 35(11): 2001-2007.

[16] Wang D., Sun X.. Low density particleboard from wheat straw and corn pith. Industrial Crops and Products, 2002, 15(1): 43-50.

[17] Ye X.P., Julson J., Kuo M., Womac A., Myers D.. Properties of medium density fibreboards made from renewable biomass. Bioresource Technology, 2007, 98(5): 1077-1084.

[18] Yu H., Liu R., Shen D., Wu Z., Huang Y.. Arrangement of cellulose microfibrils in the wheat straw cell wall. Carbohydrate Polymers, 2008, 72(1): 122-127.

[19] Zheng Y., Pan Z., Zhang R., Jenkins B., Blunk S.. Particleboard quality characteristics of saline jose tall wheatgrass and chemical treatment effect. Bioresource Technology, 2007, 98(6): 1304-1310.

[20] Zhang Y., Lu X., Pizzi A., Delmotte L.. Wheat straw particleboard bonding improvements by enzyme pretreatment. Holz als Roh-und Werkstoff, 2003, 61(1): 49-54.