Surface Finish Improvement of Selective Laser Melted Aluminium Alloy by Surface Mechanical Attrition Treatment

Abstract

Surface mechanical attrition treatment (SMAT) has been used to treat the surfaces of an aluminium alloy manufactured by selective laser melting (SLM). SMAT involved impacting the SLM sample surface with spherical balls at a frequency of 30 Hz for 10 min to 30 min, which induced plastic deformation of the sample surface, leading to a change in surface finish and surface hardness. The surface finish, morphology, hardness, and structural features have been investigated. The results show that SMAT is very effective in improving the surface finish of the SLM aluminium alloy surface. After 30 min of treatment, the roughness value (Ra) was reduced by 87%, from 19.4 μm to 2.6 μm. SMAT also has the benefit of increasing the surface hardness of SLM aluminium alloy from 125 HV_0.1 to 160 HV_0.1, and generating a strain hardened layer of about 300 μm thick at the subsurface, and thus has the potential of improving wear resistance. In addition, SMAT induced a compressive residual stress of around 100 MPa on the treated surface, which would be beneficial in improving the fatigue properties of SLM aluminium alloy. The mechanisms underlying surface smoothing, hardness increase, and the evolution of compressive residual stress in SMAT are discussed in terms of severe surface plastic deformation and strain hardening.

Keywords

Aluminium alloy / Selective laser melting / Surface mechanical attrition treatment / Surface finish / Hardness / Residual stress

References

[1] Radhika C, Shanmugam R, Ramoni M, Gnanavel BK. A review on additive manufacturing for aerospace application. Mater. Res. Expr. 2024, 11, 022001. DOI: 10.1088/2053-1591/ad21ad

[2] Segonds F. Design by additive manufacturing: An application in aeronautics and defence. Virtual Phys. Prototy 2018, 13, 237-245. DOI: 10.1080/17452759.2018.1498660

[3] Rouway M, Tarfaoui M, Chakhchaoui N, Omari LEH, Fraija F, Cherkaoui O. Additive manufacturing and composite materials for marine energy: Case of tidal turbine. 3D Print. Addit. Manuf. 2023, 10, 1309-1319. DOI: 10.1089/3dp.2021.0194

[4] Davim JP. (Ed.) Laser in Manufacturing ; Wiley: Hoboken, NJ, USA, 2012. ISBN: 978-1-848-21369-2.

[5] Mahmood MR, Chioibasu D, Rehman AU, Mibai S, Popescu AC. Post-processing techniques to enhance the quality of metallic parts produced by additive manufacturing. Metals 2022, 12, 77. DOI: 10.3390/met12010077

[6] Wang H, Lee YL, Bai Y, Zhang J. (Eds). Post-Processing Techniques for Metal-Based Additive Manufacturing ; Taylor & Fracncis, CRC Press: London, UK, 2024; pp. 29-52.

[7] Vayre B, Vignat F, Villeneuve F. Metallic additive manufacturing: State-of-the-art review and prospects. Mech. Ind. 2012, 13, 80-96. DOI: 10.1051/meca/2012003

[8] Brinksmeier E, Levy G, Mayer D, Spierings AB. Surface integrity of selective laser melted components. CIRP Ann. Manuf. Technol. 2010, 149, 601-606. DOI: 10.1016/j.cirp.2010.03.131

[9] Chen Z, Wu X, Tomus D, Davis CHJ. Surface roughness of selective laser melted Ti-6Al-4V alloy components. Add. Manuf. 2018, 21, 91-103. DOI: 10.1016/j.addma.2018.02.009

[10] Kuntoglu M, Salur E, Canli E, Aslan A, Gupta MK, Waqar S, et al. A state of the art on surface morphology of selective laser melted metallic alloys. Int. J. Adv. Manuf. Technol. 2023, 127, 1103-1142. DOI: 10.1007/s00170-023-11534-7

[11] Mohammadian N, Turenne S, Brailovski V. Surface finish control of additively manufactured Inconel 625 components using combined chemical abrasive flow polishing. J. Mater. Process. Technol. 2018, 252, 728-738. DOI: 10.1016/j.jmatprotec.2017.10.020

[12] Alrbaey K, Wimpenny D, Rosi R, Manning W, Moroz A. On optimization of surface roughness of selective laser melted stainless steel parts: A statistical study. J. Mater. Eng. Perform. 2014, 23, 2139-2148. DOI: 10.1007/s11665-014-0993-9

[13] Tian Y, Gora WS, Cabo AP, Parimi LL, Hand DP, Tammas-Williams S, et al. Materials interaction in laser polishing powder bed additive manufactured Ti6Al4V components. Add. Manuf. 2018, 20, 11-22. DOI: 10.1016/j.addma.2017.12.010

[14] Petropoulos G, Pandazaras C, Davim J. Surface texture characterization and evaluation related to machining. In Surface Integrity in Machining ; Davin J, Ed.; Springer: London, UK, 2010. DOI: 10.1007/978-1-84882-874-2_2

[15] Read N, Wang W, Essa K, Attallah MM. Selective laser melting of AlSi10Mg alloy: Process optimisation and mechanical properties development. Mater. Des. 2015, 65, 417-424. DOI: 10.1016/j.matdes.2014.09.044

[16] Niu N, Singh S, Garg A, Singh H, Panda B, Peng X, et al. Review of materials used in laser-aided additive manufacturing processes to produce metallic parts. Front. Mech. Eng. 2019, 14, 282-298. DOI: 10.1007/s11465-019-0526-1

[17] Xue L, Liao C, Wu M, Li Q, Hu Z, Yang Y, et al. Improvement of mechanical properties and corrosion resistance of SLM-AlSi10Mg alloy by an eco-friendly electric pulse treatment. J. Clean. Prod. 2024, 439, 140864. DOI: 10.1016/j.jclepro.2024.140864

[18] Masood H, Ruan D, Palanisamy S. Mechanical properties of SLM-printed aluminum alloys: A review. Materials 2020, 13, 4301. DOI: 10.3390/ma13194301

[19] Dasari J, Xavior MA. Review of additive manufacturing and post processing techniques for aluminum alloys with focus on microstructure changes mechanical performance and emerging trends. Discov. Mech. Eng. 2026, 5, 48. DOI: 10.1007/s44245-026-00189-9

[20] Tang H, Gao C, Zhang Y, Zhang N, Lei C, Bi Y, et al. Effects of direct aging treatment of microstructure, mechanical properties and residual stress of selective laser melted AlSi10Mg alloy. J. Mate Sci. Technol. 2023, 139, 198-209. DOI: 10.1016/j.jmst.2022.08.032

[21] Michi RA, Plotkowski A, Shyam A, Dehoff RR, Babu SS. Towards high temperature applications of aluminum alloys enabled by additive manufacturing. Int. Mater. Rev. 2021, 67, 1-48. DOI: 10.1080/09506608.2021.1951580

[22] Tang H, Gao C, Zhang S, Xiong X, Cao S, Wu X, et al. Multivariate relationships between microstructure evolution and strengthening mechanisms in laser powder bed fusion of Al-Mn-Sc alloy: towards improved fatigue performance. Light Adv. Manuf. 2024, 5, 1. DOI: 10.37188/lam.2024.001

[23] Boban J, Ahmed A, Gokcekaya O, Nakano T. Ultra-precision surface treatment of beta-titanium alloy printed using laser and electron beam melting sources. CIRP J. Manuf. Sci. Technol. 2025, 58, 1-19. DOI: 10.1016/j.cirpj.2025.01.006

[24] Ma CP, Guan YC, Zhou W. Laser polishing of additive manufactured Ti alloys. Opt. Lasers Eng. 2017, 93, 171-177. DOI: 10.1016/j.optlaseng.2017.02.005

[25] Bhaduri D, Ghara T, Penchev P, Paul S, Pruncu CI, Dimov S, et al. Pulsed laser polishing of selective laser melted aluminum alloy parts. App. Surf. Sci. 2021, 558, 149887. DOI: 10.1016/j.apsusc.2021.149887

[26] Alfieri V, Argenio P, Gaiazzo F, Sergi V. Reduction of surface roughness by means of laser processing over additive manufacturing metal parts. Materials 2017, 10, 30. DOI: 10.3390/ma10010030

[27] Zhao D, Li X. Chemical mechanical polishing: Theory ad experiment. Friction 2013, 1, 306-326. DOI: 10.1007/s40544-013-0035-x

[28] Gunnerek R, Soundarapandiyan G, Mishurova T, Schroder J, Bruno G, Boykin J, et al. Chemical mechanical polishing of powder bed fusion-laser beam processed 316L stainless steel. J. Mater. Process Technol. 2025, 345, 119055. DOI: 10.1016/j.jmatprotec.2025.119055

[29] Acquesta A, Monetta T. The electropolishing of additively manufactured parts in titanium: State of the art. Adv. Eng. Mater. 2021, 23, 2100545. DOI: 10.1002/adem.202100545

[30] Urlea V, Brailovski V. Electropolishing and electropolishing-related allowances for powder bed selectively laser-melted Ti-6Al-4V alloy components. J. Mater. Process Technol. 2017, 242, 1-11. DOI: 10.1016/j.jmatprotec.2016.11.014

[31] Valentincic J, Koroth JE, Zeidler H. Advances in surface finish for additive manufacturing of metal parts: A comprehensive review of plasma electrolytic polishing (PEP). Virtual Phys. Prototy 2024, 19, e2364222. DOI: 10.1080/17452759.2024.2364222

[32] Yang L, Laugel N, Housden J, Espitalier L, Matthews A, Yerokhin A. Plasma additive layer manufacture smoothing (PALMS) technology-An industrial prototype development and a comparative study on both additive manufactured and conventional machined AISI316 stainless steel. Add. Manuf. 2020, 34, 101204. DOI: 10.1016/j.addma.2020.101204

[33] Bai Y, Zhao C, Yang J, Fuh JYH, Weng C, Wang H. Dry mechanical-electrochemical polishing of selective laser melted 316L stainless steel. Mater. Des. 2020, 193, 108840. DOI: 10.1016/j.matdes.2020.108840

[34] Dixit N, Sharma V, Kumar P. Research trends in abrasive flow machining: A systematic review. J. Manuf. Proc. 2021, 64, 1434-1461. DOI: 10.1016/j.jmapro.2021.03.009

[35] Sun Y, Bailey R, Moroz A. Surface finish and properties enhancement of selective laser melted 316L stainless steel by surface mechanical attrition treatment. Surf. Coat. Tech. 2019, 378, 124993. DOI: 10.1016/j.surfcoat.2019.124993

[36] Partella Q, Chemkhi M, Retraint D. Influence of surface mechanical attrition treatment (SMAT) post-treatment on microstructure, mechanical and tensile behaviour of additive manufactured ALSI 316. Mater. Charact. 2020, 167, 110463. DOI: 10.1016/j.matchar.2020.110463

[37] Sausto F, Tezzele C, Beretta S. Analysis of fatigue strength of L-PBF AlSi10Mg with different surface post-processes: Effect of residual stresses. Metals 2022, 12, 898. DOI: 10.3390/met12060898

[38] Joshy J, George A, Kuriachen B, Mathew J. Influence of post processing on the micro-machining of selective laser melted AISI AlSi10Mg: An experimental investigation. Mater. Manuf. Process 2023, 38, 516-528. DOI: 10.1080/10426914.2022.2075886

[39] Zhang D, Yu J, Li H, Zhou X, Song C, Zhang C, et al. Investigation of laser polishing of four selective laser melting alloy samples. Appl. Sci. 2020, 10, 760. DOI: 10.3390/app10030760

[40] Liu ZG, Fecht HJ, Umemoto M. Microstructural evolution and nanocrystal formation during deformation of Fe-C alloys. Mater. Sci. Eng. 2004, A375, 839-843. DOI: 10.1016/j.msea.2003.10.136

[41] Lu K, Lu J. Nanostructured surface layer on metallic materials induced by surface mechanical attrition treatment. Mater. Sci. Eng. 2004, A375-377, 38-45. DOI: 10.1016/j.msea.2003.10.261

[42] Sun Y. Sliding wear behaviour of surface mechanical attrition treated AISI 304 stainless steel. Tribol. Int. 2013, 57, 67-75. DOI: 10.1016/j.triboint.2012.07.015

[43] Roland T, Retraint D, Lu K, Lu J. Fatigue life improvement through surface nanostructuring of stainless steel by means of surface mechanical attrition treatment. Scr. Mater. 2006, 54, 1949-1954. DOI: 10.1016/j.scriptamat.2006.01.049

[44] Maleki E, Bagherifard S, Bandini M, Guagliano M. Surface post-treatments for metal additive manufacturing: Progress, challenges, and opportunities. Add. Manuf. 2021, 37, 101619. DOI: 10.1016/j.addma.2020.101619

[45] Gangwar K, Ramulu M. Residual stress measurement using X-ray diffraction in friction stir-welded dissimilar titanium alloys. Materials 2024, 17, 1482. DOI: 10.3390/ma17071482

[46] Beretta S, Gargourimotlagh Foletti MS, Plessis AD, Riccio M. Fatigue strength assessment of ‘as build’ AlSi10Mg manufactured by SLM with different build orientations. Int. J. Fatigue 2020, 139, 105737. DOI: 10.1016/j.ijfatigue.2020.105737

[47] Beretta S, Patriarca L, Gargourimotlagh M, Hardaker A, Bracket D, Salimian M, et al. A benchmark activity on the fatigue life assessment of AlSi10Mg components manifactured by L-PBF. Mater. Des. 2021, 218, 110713. DOI: 10.1016/j.matdes.2022.110713

[48] Sausto F, Carrion P, Shamsaei N, Beretta S. Fatigue failure mechanisms for AlSi10Mg manufactured by L-PBF under axial and torsional loads: The role of defects and residual stresses. Int. J. Fatigue 2022, 162, 106903. DOI: 10.1016/j.ijfatigue.2022.106903

[49] Schanz J, Hofele M, Hitzler L, Merkel M, Riegel H. Laser polishing of additive manufactured AlSi10Mg parts with an oscillating laser beam. In Machining, Joining and Modifications of Advanced Materials; Advanced Structured Materials; Ochsner A, Altenbach H, Eds.; Springer: Singapore, 2016; Volume 61. DOI: 10.1007/978-981-10-1082-8_16

[50] Jeong JU, Lee KK, Ahn DG, Jeong WL. Study of surface roughness change of AlSi10Mg based on selectrive laser melting (SLM) using electro-polishing technique. J. Mech. Sci. Technol. 2024, 38, 4579-4585. DOI: 10.1007/s12206-024-2412-y