Developing sodium-doped ceria-based electrolytes for low-temperature solid oxide fuel cells

Abstract

Na-doped CeO₂ (NDC) electrolytes with 0.05, 0.10, 0.15, and 0.20 molar ratios of Na ions (0.05NDC, 0.1NDC, 0.15NDC, and 0.2NDC) were synthesized and systematically evaluated for low-temperature solid oxide fuel cell (SOFC) applications. Density functional theory (DFT) calculations reveal that Na doping lowers the oxygen-vacancy formation energy. Structural analysis confirms progressive lattice expansion in NDCs and a maximum oxygen-vacancy concentration in 0.15NDC, while incomplete incorporation of Na in 0.2NDC yields residual Na₂CO₃. Conductivity studies demonstrate negligible electronic conductivity and a peak ionic conductivity in 0.15NDC, suggesting that moderate Na doping enhances ionic transport, whereas excessive dopant is detrimental. Two 0.15NDC-based SOFCs are fabricated by ceramic and dry-pressing methods, and their maximum power densities at 550°C are 208 and 778 mW·cm⁻², respectively, indicating the rapid ionic transport of the 0.15NDC electrolyte. These results demonstrate that Na doping is an effective route for developing advanced low-temperature SOFC electrolytes.

Keywords

solid oxide fuel cells / Na-doped CeO₂ electrolyte / oxygen vacancy / ionic conductivity / high performance

References

[1] Humayun M, Li ZS, Israr M, et al. . Perovskite type ABO₃ oxides in photocatalysis, electrocatalysis, and solid oxide fuel cells: State of the art and future prospects. Chem. Rev., 2025, 125(6): 3165

[2] P. Vinchhi, M. Khandla, K. Chaudhary, and R. Pati, Recent advances on electrolyte materials for SOFC: A review, Inorg. Chem. Commun., 152(2023), art. No. 110724.

[3] Li J, Cai Q, Horri BA. Highly conductive and stable electrolytes for solid oxide electrolysis and fuel cells: Fabrication, characterisation, recent progress and challenges. Mater. Adv., 2025, 6(1): 39

[4] J. Zhang, C. Lenser, N.H. Menzler, and O. Guillon, Comparison of solid oxide fuel cell (SOFC) electrolyte materials for operation at 500°C, Solid State Ionics, 344(2020), art. No. 115138.

[5] Zakaria Z, Hassan SHA, Shaari N, Yahaya AZ, Kar YB. A review on recent status and challenges of yttria stabilized zirconia modification to lowering the temperature of solid oxide fuel cells operation. Int. J. Energy Res., 2020, 44(2): 631

[6] M. Stojmenović, N. Nišić, M. Kragović, et al., Multidoped CeO₂ single-phase as electrolyte for IT-SOFC, Solid State Ionics, 414(2024), art. No. 116645.

[7] Jeong I, Yu H, Lee D, Roh KM, Wachsman ED, Lee KT. Advances in the development and application of δ-Bi₂O₃-based ionic conductors for ceramic electrochemical cells. ACS Appl. Mater. Interfaces, 2025, 17(20): 28961

[8] L.T. Li, M. Watanabe, M. Inada, and T. Ishihara, Planar type reversible solid oxide cells using LaGaO₃ electrolyte thin-film prepared by dip-coating and co-sintering method, J. Power Sources, 624(2024), art. No. 235560.

[9] J.M. Jing, J. Pang, L.Y. Chen, H. Zhang, Z. Lei, and Z.B. Yang, Structure, synthesis, properties and solid oxide electrolysis cells application of Ba(Ce, Zr)O₃ based proton conducting materials, Chem. Eng. J., 429(2022), art. No. 132314.

[10] R. Kumar, V. Yadav, P. Singh, P.K. Sonkar, U. Kumar, and S. Singh, Effect of calcination temperature on the structural, microstructure, and electrical properties of CeO₂ nanoparticles as a solid electrolyte for IT-SOFC application, Adv. Powder Technol., 35(2024), No. 12, art. No. 104710.

[11] Jiang SS, Qiu H, Xu SH, et al. . Investigation and optimization of high-valent Ta-doped SrFeO_3−δ as air electrode for intermediate-temperature solid oxide fuel cells. Int. J. Miner. Metall. Mater., 2024, 31(9): 2102

[12] Liang FY, Yang JR, Wang HQ, Wu JW. Fabrication of Gd₂O₃-doped CeO₂ thin films through DC reactive sputtering and their application in solid oxide fuel cells. Int. J. Miner. Metall. Mater., 2023, 30(6): 1190

[13] J. Kang, W.Q. Feng, D. Guo, et al., Performance optimization of Ca and Y co-doped CeO₂-based electrolyte for intermediate-temperature solid oxide fuel cells, J. Alloy. Compd., 913(2022), art. No. 165317.

[14] M. Akbar, B. Jin, Z.W. Tu, et al., High-performing and stable non-doped ceria electrolyte with amorphous carbonate coating layer for low-temperature solid oxide fuel cells, Electrochim. Acta, 393(2021), art. No. 139067.

[15] Jakati MH, Momin N, Manjanna J. Effect of Sr²⁺ and Sr²⁺, La³⁺ co-doping on ionic conductivity of ceria based electrolytes at 350 ≤ T ≤ 800°C. Ceram. Int., 2025, 51(24): 42262

[16] Van herle J, Horita T, Kawada T, Sakai N, Yokokawa H, Dokiya M. Low temperature fabrication of (Y, Gd, Sm)-doped ceria electrolyte. Solid State Ionics, 1996, 86: 1255

[17] Artini C. Rare-earth-doped ceria systems and their performance as solid electrolytes: A puzzling tangle of structural issues at the average and local scale. Inorg. Chem., 2018, 57(21): 13047

[18] Mahato N, Gupta A, Balani K. Doped zirconia and ceria-based electrolytes for solid oxide fuel cells: A review. Nanomater. Energy, 2012, 1(1): 27

[19] Dalslet B, Blennow P, Hendriksen PV, Bonanos N, Lybye D, Mogensen M. Assessment of doped ceria as electrolyte. J. Solid State Electrochem., 2006, 10(8): 547

[20] Venkataramana K, Ravindranath K, Madhuri C, Madhusudan C, Kumar NP, Reddy CV. Low temperature microwave sintering of yttrium and samarium co-doped ceria solid electrolytes for IT-SOFCs. Ionics, 2018, 24(5): 1429

[21] Kobi S, Jaiswal N, Kumar D, Parkash O. Ionic conductivity of Nd³⁺ and Y³⁺ co-doped ceria solid electrolytes for intermediate temperature solid oxide fuel cells. J. Alloy. Compd., 2016, 658: 513

[22] Venkataramana K, Madhuri C, Reddy YS, Bhikshamaiah G, Reddy CV. Structural, electrical and thermal expansion studies of tri-doped ceria electrolyte materials for IT-SOFCs. J. Alloy. Compd., 2017, 719: 97

[23] S. Rajendran, N.K. Thangavel, S. Alkatie, Y. Ding, and L.M.R. Arava, Y, Gd, and Pr tri-doped perovskite-type proton conducting electrolytes with improved sinterability and chemical stability, J. Alloy. Compd., 870(2021), art. No. 159431.

[24] Kaur P, Singh K. Cerium oxide-based electrolytes for low- and intermediate-temperature solid oxide fuel cells: State of the art, challenges and future prospects. Sustainable Energy Fuels, 2025, 9(15): 3981

[25] Pei ZX, Zhang J, Zhang Y, et al. . Enhancing performance and stability of Sm_0.2Ce_0.8O_1.9-decorated La_0.6Sr_0.4CoO_3−δ composite cathode in flat-tube solid oxide fuel cell. Int. J. Miner. Metall. Mater., 2025, 32(11): 2676

[26] Riess I. Neutral and metallic vs. charged and semiconducting surface layer in acceptor doped CeO₂. Int. J. Miner. Metall. Mater., 2024, 31(4): 795

[27] Tuller HL, Nowick AS. Defect structure and electrical properties of nonstoichiometric CeO₂ single crystals. J. Electrochem. Soc., 1979, 126(2): 209

[28] Zhang LF, Meng JL, Yao F, et al. . Insight into the mechanism of the ionic conductivity for Ln-doped ceria (Ln = La, Pr, Nd, Pm, Sm, Gd, Tb, Dy, Ho, Er, and Tm) through first-principles calculation. Inorg. Chem., 2018, 57(20): 12690

[29] Avram D, Dominguez MS, Cojocaru B, Florea M, Parvulescu V, Tiseanu C. Toward a unified description of luminescence–local structure correlation in Ln doped CeO₂ nanoparticles: Roles of Ln ionic radius, Ln concentration, and oxygen vacancies. J. Phys. Chem. C, 2015, 119(28): 16303

[30] Nolan M. Charge compensation and Ce³⁺ formation in trivalent doping of the CeO₂(110) surface: The key role of dopant ionic radius. J. Phys. Chem. C, 2011, 115(14): 6671

[31] Bezkrovnyi O, Szymczak M, Marciniak L, et al. . Advances and limitations of the Eu³⁺ luminescent probe for monitoring Ce⁴⁺/Ce³⁺ transitions in ceria. J. Phys. Chem. C, 2025, 129(3): 1724

[32] Z.H. Liu, Y.H. Guo, H. Wang, and X.L. Zhu, Role of Na in the stability enhancement of CeO₂ catalysts for ketonization of propionic acid, Appl. Catal. A, 672(2024), art. No. 119593.

[33] B.W. Lu, T. Zhang, L.Q. Zhang, et al., Promotion effects of oxygen vacancies on activity of Na-doped CeO₂ catalysts for reverse water gas shift reaction, Appl. Surf. Sci., 587(2022), art. No. 152881.

[34] Feng XY, Ran MJ, Yuan MM, et al. . Na doping and CeO₂ nanoparticle surface modification enhancing the Li-rich Li_1.2Mn_0.54Ni_0.13Co_0.13O₂ cathode material for a lithium-ion battery. ACS Appl. Nano Mater., 2024, 7(11): 13173

[35] Jaidka S, Khan S, Singh K. Na₂O doped CeO₂ and their structural, optical, conducting and dielectric properties. Physica B, 2018, 550: 189

[36] Chen Z, Chen G, Zhang R, Dai RX, Lv XH, Geng SJ. Toward understanding of temperature dependence of an advanced ceramic fuel cell with Ni_0.8Co_0.15Al_0.05LiO₂ as an electrode. ACS Appl. Energy Mater., 2021, 4(8): 8386

[37] Sarfraz, Rasool S, Khalid M, et al. . Al³⁺ doped CeO₂ for proton conducting fuel cells. Int. J. Miner. Metall. Mater., 2024, 31(10): 2253

[38] T. Lu, A comprehensive electron wavefunction analysis toolbox for chemists, Multiwfn, J. Chem. Phys., 161(2024), No. 8, art. No. 082503.

[39] Momma K, Izumi F. VESTA: A three-dimensional visualization system for electronic and structural analysis. J. Appl. Crystallogr., 2008, 41(3): 653

[40] A. Khabibrakhmanov, D.V. Fedorov, A. Ambrosetti, et al., Accurate noncovalent interactions in atomistic systems via quantum Drude oscillators, J. Chem. Phys., 163(2025), No. 15, art. No. 151001.

[41] Li Q, Qiao Y, Guo SH, et al. . Both cationic and anionic co(de)intercalation into a metal-oxide material. Joule, 2018, 2(6): 1134

[42] Takeda Y, Nakahara K, Nishijima M, et al. . Sodium deintercalation from sodium iron oxide. Mater. Res. Bull., 1994, 29(6): 659

[43] Xie YT, Dai KS, Wang QY, Gu FP, Shui M, Shu J. Understanding the sodium ion transport properties, deintercalation mechanism, and phase evolution of a Na₂Mn₂Si₂O₇ cathode by atomistic simulation. Phys. Chem. Chem. Phys., 2021, 23(2): 1750

[44] Zhang F, Wang P, Koberstein J, Khalid S, Chan SW. Cerium oxidation state in ceria nanoparticles studied with X-ray photoelectron spectroscopy and absorption near edge spectroscopy. Surf. Sci., 2004, 563(1–3): 74

[45] Naganuma T, Traversa E. Stability of the Ce³⁺ valence state in cerium oxide nanoparticle layers. Nanoscale, 2012, 4(16): 4950

[46] Gao TF, Kumar A, Shang ZC, et al. . Promoting electrochemical conversion of CO₂ to formate with rich oxygen vacancies in nanoporous tin oxides. Chin. Chem. Lett., 2019, 30(12): 2274

[47] Caracciolo L, Madec L, Martinez H. XPS analysis of K-based reference compounds to allow reliable studies of solid electrolyte interphase in K-ion batteries. ACS Appl. Energy Mater., 2021, 4(10): 11693

[48] Pirovano MVG, Hofmann A, Sauer J. Oxygen vacancies in transition metal and rare earth oxides: Current state of understanding and remaining challenges. Surf. Sci. Rep., 2007, 62(6): 219

[49] Parkash O, Singh N, Singh NK, Kumar D. Preparation and characterization of ceria co-doped with Ca and Mg. Solid State Ionics, 2012, 212: 100

[50] N. Momin, J. Manjanna, L. D’Souza, S.T. Aruna, and S.S. Kumar, Synthesis, structure and ionic conductivity of nanocrystalline Ce_1−xLa_xO_2−δ as an electrolyte for intermediate temperature solid oxide fuel cells, J. Alloy. Compd., 896(2022), art. No. 163012.

[51] Klie RF, Ito Y, Stemmer S, Browning ND. Observation of oxygen vacancy ordering and segregation in Perovskite oxides. Ultramicroscopy, 2001, 86(3–4): 289

[52] Kaur T, Kolte J, Singh K. Defect-induced improved structural and electrical properties of Gd–Sr co-doped ceria for solid oxide fuel cell applications. Ceram. Int., 2024, 50(10): 17054

[53] Wang GL, Wu JZ, Li S, et al. . Effect of the online reaction byproducts of LiNi_0.8Co_0.15Al_0.05O_2−δ electrodes on the performance of solid oxide fuel cells. Int. J. Hydrogen Energy, 2022, 47(79): 33850

[54] Zheng ZW, Jing JM, Lei Z, et al. . Performance and DRT analysis of infiltrated functional cathode based on the anode supported SOFCs with long-term stability. Int. J. Hydrogen Energy, 2022, 47(41): 18139

[55] Tian YF, Wang WJ, Liu Y, et al. . Achieving strong coherency for a composite electrode via one-pot method with enhanced electrochemical performance in reversible solid oxide cells. ACS Catal., 2021, 11(6): 3704

[56] Xu SW, Chen G, Wei K, et al. . Preparation and performance of LiNi_1−xAl_xO₂ electrodes for low-temperature ceramic fuel cells. ACS Appl. Energy Mater., 2024, 7(2): 576

[57] C. Xia, Y.Q. Mi, B.Y. Wang, B. Lin, G. Chen, and B. Zhu, Shaping triple-conducting semiconductor BaCo_0.4Fe_0.4Zr_0.1 Y_0.1O_3−δ into an electrolyte for low-temperature solid oxide fuel cells, Nat. Commun., 10(2019), No. 1, art. No. 1707.

[58] X.M. Zhou, J.J. Yang, R.M. Wang, W. Zhang, S.N. Yun, and B.Y. Wang, Advances in lithium-ion battery materials for ceramic fuel cells, Energy Mater., 2(2022), art. No. 200041.

[59] Yang D, Chen G, Liu HL, et al. . Electrochemical performance of a Ni_0.8Co_0.15Al_0.05LiO₂ cathode for a low temperature solid oxide fuel cell. Int. J. Hydrogen Energy, 2021, 46(17): 10438

[60] S.F. Wang, Y.L. Liao, Y.F. Hsu, and P. Jasinski, Effects of LiNi_0.8Co_0.15Al_0.05O₂ electrodes on the conduction mechanism of Sm_0.2Ce_0.8O_2−δ electrolyte and performance of low-temperature solid oxide fuel cells, J. Power Sources, 546(2022), art. No. 231995.

[61] Wen LC, Hsieh CY, Tsai YI, et al. . Electrical properties of Sm-doped ceria (SDC) and SDC carbonate composite. J. Chin. Chem. Soc., 2013, 60(11): 1359

[62] Fan LD, He CX, Zhu B. Role of carbonate phase in ceria–carbonate composite for low temperature solid oxide fuel cells: A review. Int. J. Energy Res., 2017, 41(4): 465

[63] Korte C, Peters A, Janek J, Hesse D, Zakharov N. Ionic conductivity and activation energy for oxygen ion transport in superlattices: The semicoherent multilayer system YSZ (ZrO₂ + 9.5mol% Y₂O₃)/Y₂O₃. Phys. Chem. Chem. Phys., 2008, 10(31): 4623

[64] Guo ZG, Xu L, Ling YH, Wang PX, Wei KW, Qiu P. A perspective on cathode materials for proton-conducting solid oxide fuel cells. Int. J. Hydrogen Energy, 2025, 106: 52

RIGHTS & PERMISSIONS

University of Science and Technology Beijing