Behavioral characteristics and renewal mechanism of deadman coke in the hearth under low-carbon ironmaking blast furnace conditions

Abstract

As the sole solid material in the lower part of a blast furnace (BF), the multiphase reaction behavior of coke within the dead-man region of the hearth is of significant theoretical and practical importance for carbon emission control and low-carbon production. The multidimensional characterization of the occurrence state, multiphase reaction behavior, and renewal mechanism of deadman coke in the hearth was performed through the dissection of a 3200-m³ BF, combining various methods such as rope-sawing residual iron removal, image processing techniques, microscopic analysis, and coke dissolution experiments. The results showed that the deadman root in the hearth exhibited a “curved” shape and a distinct ‘floating’ state, with the floating height at the center approximately 0.45 m, increasing toward the hearth edge. Vertically, the deadman was divided into three regions: the “slag–coke zone,” the “iron–coke zone,” and the “coke–free zone.” The average deadman voidage was calculated to be 54.75% (±0.85%), and the coke particle size was 21.47 mm (± 0.53 mm), based on image processing techniques. A “slag + CaS isolation layer” was identified on the outer surface of the deadman coke during the dissolution and erosion process of hot metal analysis of the “slag–iron–coke” three-phase microstructure indicated that this layer suppressed the carburization reaction and represented the most limiting factor for deadman coke renewal. A coke renewal formula was established from the coke dissolution experiments, and the renewal time was calculated to be 14.74 d. The renewal mechanism of deadman coke was elucidated through comprehensive analysis, and recommendations for low-carbon operation were proposed. These findings provide a scientific basis and theoretical guidance for low-carbon production and fuel optimization in ironmaking blast furnaces.

Keywords

deadman / coke / blast furnace hearth / renewal mechanism / slag–iron–coke

References

[1] Liu YX, Jiao KX, Zhang JL, Wang C, Zhang L, Fan XY. Research progress and future prospects in the service security of key blast furnace equipment. Int. J. Miner. Metall. Mater., 2024, 31(10): 2121

[2] X.Y. Meng, K.L. Pang, M.M. Sun, et al., Study on the characteristics of coke in the coupled reaction between iron ore and coke simulating the blast furnace environment, Fuel, 378(2024), art. No. 132715.

[3] J.L. Zhang, L.Y. Hao, S.J. Duan, R.S. Xu, K.J. Zhang, and Y.M. Wang, Review on the progress of hydrogen-rich gas injection into blast furnace, Metall. Res. Technol., 122(2025), No. 3, art. No. 308.

[4] S. Meng, K.X. Jiao, J.L. Zhang, et al., Analysis of the coke distribution characteristics in hearth based on blast furnace dissection, Fuel Process. Technol., 242(2023), art. No. 107650.

[5] K. Yao, Y. Deng, R. Liu, L. Liu, Y.J. Gao, and Y.T. Liu, Factors affecting the hearth activity of blast furnace and corresponding measures, Metall. Res. Technol., 122(2025), No. 2, art. No. 205.

[6] Niu Q, Cheng SS, Xu WX, et al. . Changes in microstructure and chemical composition of deadman coke of a 2800 m³ industrial blast furnace. ISIJ Int., 2018, 58(4): 667

[7] S. Meng, K.X. Jiao, J.L. Zhang, et al., Dissection study of the deadman in a commercial blast furnace hearth, Fuel Process. Technol., 221(2021), art. No. 106916.

[8] Liu PB, Cheng SS, Cheng XM, Liu Z. Study on coke properties in deadman of blast furnace. Ironmaking Steelmaking, 2024, 51(8): 776

[9] Chen JB, Zhang SF, Chen H, et al. . Insights into particle size degradation and structural evolution of native-state coke extracted above the tuyere centerline in a large-scale blast furnace. Metall. Mater. Trans. B, 2025, 56(5): 4495

[10] Dong ML, Jin RZ, Cui SM, Shen HB, Zheng PC. Theoretical study on coke behavior in blast furnace of the coke in BF. Henan Metall., 2019, 27(1): 4

[11] Nogami H, Toda K, Pintowantoro S, Yagi JI. Cold-model experiments on deadman renewal rate due to sink-float motion of hearth coke bed. ISIJ Int., 2004, 44(12): 2127

[12] Li KJ, Zhang JL, Liu YX, et al. . Graphitization of coke and its interaction with slag in the hearth of a blast furnace. Metall. Mater. Trans. B, 2016, 47(2): 811

[13] Jiao KX, Zhang JL, Chen CL, Wu SR, Liang LS. Analysis of the deadman features in hearth based on blast furnace dissection by comprehensive image-processing technique. ISIJ Int., 2019, 59(1): 16

[14] Sun MM, Zhang JL, Zhang L, Li KJ. Investigation of the microstructure interaction mechanism of coke-slag-metal in deadman of blast furnace. Ironmaking Steelmaking, 2021, 48(9): 1089

[15] Niu Q, Cheng SS, Xu WX, Niu WJ, Mei YG. Analysis of the coke particle size distribution and porosity of deadman based on blast furnace hearth dissection. ISIJ Int., 2019, 59(11): 1997

[16] Geerdes M, Chaigneau R, Kurunov I, Lingiardi O, Ricketts J. Modern Blast Furnace Ironmaking: An Introduction, 20153rd ed.Amsterdam, IOS Press: 217

[17] Committee on Reaction within Blast FurnaceJoint Society on Iron and Steel Basic ResearchThe Iron and Steel Institute of Japan. Blast Furnace Phenomena and Modelling, 1987, Amsterdam, Elsevier applied science publishers: 182

[18] Raipala K. Deadman and hearth phenomena in the blast furnace. Scand. J. Metall., 2000, 29(1): 39

[19] Song MB, Meng S, Jiao KX, Zhang JL, Deng Y, Ji CK. Application of comprehensive image-processing technology in blast furnace damage investigation. Metall. Ind. Autom., 2023, 47(6): 72

[20] Liu GQ, Liu SX, Huang QJ, Zhong YL, Zhong S, Qin XG. Metallography and quantitative analysis techniques of materials microstructure. Chin. J. Stereol. Image Anal., 2002, 7(4): 248

[21] D.J. Lee, H.S. Yoon, A.R. Nair, and M.I. Kim, Multiphase flow and interface dynamics in a blast furnace hearth: Effects of slag viscosity and coke diameter, Int. J. Heat Mass Transfer, 246(2025), art. No. 127085.

[22] Golybev OV, Chernousov PI, Myasoyedov SV, Karataeva AV. Review of research on coke gasification in the blast furnace with elevated hydrogen content and determination of coke’s postreactive strength. 4. Change in coke strength after gasification in the presence of H₂O. Coke Chem., 2024, 67(11): 648

[23] Zhou F, Peng DS, Li KJ, et al. . Coke behavior with H₂O in a hydrogen-enriched blast furnace: A review. Int. J. Miner. Metall. Mater., 2024, 31(5): 959

[24] Y.J. Fan, Y.F. Chai, J.Y. Wu, et al., Behavior of coke in the blast furnace for smelting Bayan Obo Mine, Fuel, 309(2022), art. No. 122147.

[25] Li J, Jin Y, Wang W, Sun YFH, et al. . The FSI simulation between hot metal flow and the hearth of a blast furnace during opening stage of tapping. Trans. Indian Inst. Met., 2023, 76(7): 1709

[26] Zhao J, Chen SF, Liu XJ, Li X, Li HY, Lü Q. Outlier screening for ironmaking data on blast furnaces. Int. J. Miner. Metall. Mater., 2021, 28(6): 1001

[27] J. Wu, C.F. Mu, X.F. Zhou, Z. Jiang, S.B. Hou, and L.G. Zhang, Characteristics of the tuyere coke in a blast furnace, Metall. Res. Technol., 122(2025), No. 4, art. No. 415.

[28] Y. Deng, R. Liu, T. Li, K.X. Jiao, S. Meng, and Z.Y. Guo, The quantitative model of hearth activity based on data mining and characteristics of deadman, Metall. Res. Technol., 120(2023), No. 1, art. No. 110.

[29] Ma HB, Jiao KX, Zhang JL, Fan XY, Zong YB. Phase and reaction behavior of the iron-coke interface along the coke-free area in a dissected blast furnace hearth. J. Sustain. Metall., 2022, 8(4): 1662

[30] Zhang L, Zhang JL, Jiao KX, Zou ZP, Zhao YJ. Observation of deadman samples in a dissected blast furnace hearth. ISIJ Int., 2019, 59(11): 1991

[31] Wang J, Wang W, Chen XH, et al. . Role of iron ore in enhancing gasification of iron coke: Structural evolution, influence mechanism and kinetic analysis. Int. J. Miner. Metall. Mater., 2025, 32(1): 58

[32] Zhu JH. Dissection research of an experimental B.F.. Iron Steel, 1982, 17(11): 1

[33] Y. Deng, K. Yao, Y. Xu, R. Liu, and Z.H. Huang, The process and mechanism of coke gasification dissolution loss in hydrogen-rich blast furnace, Chem. Eng. J., 498(2024), art. No. 155860.

[34] Zhang JL, Jiao KX, Liu ZJ, Wang ZY, Liu YX. Theory and Practice of Safety and Longevity for Blast Furnace Hearth, 2022, Beijing, The Metallurgy Industry Press: 241

[35] Zhang JL, Luo DW, Zeng H, Zuo HB, Jiao KX. Dissection Investigation of Blast Furnace, 2019, Beijing, The Metallurgy Industry Press: 2

[36] Y. Deng, K. Yao, R. Liu, Y.J. Gao, and L.X. Wang, Interfacial reaction behavior in blast furnace and analysis of influence mechanism, Metall. Res. Technol., 121(2024), No. 5, art. No. 509.

[37] Kazuberns K, Gupta S, Grigore M, et al. . Coke mineral transformations in the experimental blast furnace. Energy Fuels, 2008, 22(5): 3407

[38] P.Z. Zhao, Y.B. Zong, J.L. Zhang, et al., Characteristics of CaS distribution and formation mechanism in blast furnace hearth, Fuel, 366(2024), art. No. 131301.

[39] Lan CC, Sun QR, Shao JN, et al. . Reaction behaviors of iron-coke interface during hydrogen-rich smelting in a blast furnace. Int. J. Hydrogen Energy, 2024, 86: 465

[40] Ye SX, Wang FM, Yang P, et al. . Dissection of hydrogen-rich blast furnace: Continuous evolution in properties and microstructure of coke in lump zone. Int. J. Hydrogen Energy, 2025, 105: 565

[41] F.J. Liu, X.J. Ning, J.L. Zhang, and K.X. Jiao, Study on effect of hot metal temperature on crucible made of carbon bricks by dynamic erosion, Angang Technol., (2019), No. 1, p. 17.

RIGHTS & PERMISSIONS

University of Science and Technology Beijing