Characterization of the formation of slag rims of mold powder during hypo-peritectic steel continuous casting based on full-sectional microstructures

Abstract

A full-sectional microstructure characterization method was developed to investigate the formation of coarse slag rims during the continuous casting of hypo-peritectic steel. The cross-sectional microstructural analysis of typical slag rims for two highly crystalline powders revealed that their formation was primarily driven by the solidification of the liquid slag. Distinct differences were observed in the microstructures of slag rims from the two powders. Powder A (characterized by a higher breaking temperature and viscosity) displayed alternating lamellar microstructures of coarse and fine phases, with the coarse phases composed of akermanite–gehlenite transition phases. In contrast, powder B (with a lower breaking temperature and viscosity) predominantly comprised regular akermanite–gehlenite crystals interspersed with a certain amount of glassy phases. Numerical simulations of a three-phase fluid flow coupled with heat transfer indicate that slag rim formation correlates with mold oscillation. Solidification of the liquid slag at the slag rim front predominantly occurs during the negative stroke of the mold oscillation. The average heating rate during the ascending stage of the mold reaches approximately 100 K·s⁻¹, whereas the average cooling rate during the descending stage attains 400 K·s⁻¹. This temperature variation leads to the formation of lamellar microstructures, whereas the ascending stage promotes the formation of coarse structures and thicker slag rims. Based on the powder properties, two distinct formation pathways exist for highly crystalline mold powders. For the powders with a higher breaking temperature, higher viscosity, and narrower solidification range (powder A), coarse microstructures and thicker slag rims were preferentially formed. For powders with lower breaking temperature and viscosity and wider solidification ranges (powder B), the liquid slag resisted rapid solidification, and the extended mushy zone allowed the partial liquid slag to persist at the slag rim front, promoting the formation of a thin slag rim. This study enhances the understanding of slag rim formation in highly crystalline mold powders and provides critical insights into the control of longitudinal surface cracks in hypo-peritectic steel.

Keywords

hypo-peritectic steel / longitudinal surface crack / continuous casting / slag rim / full-sectional microstructures / mold powder

References

[1] Tong WJ, Luo S, Wang XH, Wei CX, Wang WL, Zhu MY. Hook formation and control mechanisms in continuously cast slabs of ultra-low carbon steel. Int. J. Miner. Metall. Mater., 2025, 3271580

[2] Wolf MM. Strand surface quality and the peritectic reaction: A look into the basics. The 81st Steelmaking Conference Proceedings, 199853

[3] Zhang ZD, Chen JZ, Ji C, Ma Y T, Zhu M Y, Wang WX. Numerical simulation of the deformation risk in thin slab continuous casting process with liquid core reduction. Int. J. Miner. Metall. Mater., 2025, 3251114

[4] Li QH, Lan P, Wang HJ, Ai HZ, Chen DL, Wang HD. Formation and control of the surface defect in hypo-peritectic steel during continuous casting: A review. Int. J. Miner. Metall. Mater., 2023, 30122281

[5] Kawamoto M, Tsukaguchi Y, Nishida N, Kanazawa T, Hiraki S. Improvement of the initial stage of solidification by using mild cooling mold powder. ISIJ Int., 1997, 372134

[6] Hanao M, Kawamoto M, Yamanaka A. Influence of mold flux on initial solidification of hypo-peritectic steel in a continuous casting mold. ISIJ Int., 2012, 5271310

[7] Moon SC, Dippenaar R, Kim SY. The peritectic phase transition of steel during the initial stages of solidification in the mold. AISTech Conference, 2015

[8] Wang FK, He H, Wang WLet al.. Effect of mold cooling intensity on the depression-type crack formation and mold flux infiltration during continuous casting process. Metall. Mater. Trans. B, 2023, 5462906

[9] Peng ZQ, Hou ZB, Tang P, Li H. Immersion depth optimization of single nozzle during beam blank continuous casting based on multiphysics characteristics. Metall. Mater. Trans. B, 2024, 5542153

[10] Li QP, Wen GH, Chen FH, Tang P, Hou ZB, Mo XY. Irregular initial solidification by mold thermal monitoring in the continuous casting of steels: A review. Int. J. Miner. Metall. Mater., 2024, 3151003

[11] Lopez PER, Lee PD, Mills KC. Explicit modelling of slag infiltration and shell formation during mould oscillation in continuous casting. ISIJ Int., 2010, 503425

[12] Ludlow V, Harris B, Riaz S, Normanton A. Continuous casting mould powder and casting process interaction: Why powders do not always work as expected. Ironmaking Steelmaking, 2005, 322120

[13] Peng ZQ, Liu Q, Guo DW, Zeng ZH, Cao JH, Hou Z B. Independent change law of mold heat transfer in continuous casting based on big data mining. Acta Metall Sin, 2023, 59101389

[14] Wang XJ, Guo YX, Xiao PC, Zhu LG, Di TC. Influence of the slag rim on the heat transfer behavior of a mold. ISIJ Int., 2023, 634639

[15] Kromhout JA, Melzer S, Zinngrebe EW, Kamperman AA, Boom R. Mould powder requirements for high-speed casting. Steel Res. Int., 2008, 792143

[16] Mills KC, Däcker C. The Casting Powders Book, 2017, Germany, The Springer International Publishing

[17] Perrot C, Pontoire JN, Marchionni C, Ridolfi MR, Sancho LF. Several slag rims and lubrication behaviours in slab casting. Rev. Met. Paris, 2005, 10212887

[18] Di TC, Wang XJ, Liu ZX, Zhai J, Li H, Piao ZL. Analysis on formation and growth mechanism of 430 stainless steel mold powder slag-bonding rim and control measures. Spec. Steel, 2022, 43563

[19] Ren L, Zhang LF, Wang QQ, Zhao X. Formation mechanism of slag rim in 304 stainless steel continuous casting mold. Iron Steel, 2016, 51835

[20] Marschall I, Kölbl N, Harmuth H. Comparison of the slag rim formation of two different mould powders. Materials Science & Technology Conference and Exhibition 2010 (MS&T 10), 20101591

[21] Yan W, Chen WQ, Lippold C, Zheng HG. Effect of properties change of mold flux and slag rim on concasting of non-magnetic steel 20Mn23AlV. Spec. Steel, 2013, 34145

[22] Liu Q, Wang W, Gao M, Yin YB, Zhang JM. Slag rim structure and phase formation mechanism in molds during the continuous casting of high-Mn high-Al steel. Ceram. Int., 2025, 5155955

[23] Yang J, Cai ZZ, Chen DF, Zhu MY. Characteristics of slag infiltration in high-Mn steel castings. Metall. Mater. Trans. B, 2019, 5021104

[24] Cao MH, Liu YH, Yu B, Zhou C, Zhang XZ. Modeling study on the initial solidification and formation of oscillation marks in continuous casting mold. Trans. Indian Inst. Met., 2024, 77151

[25] P.C. Xiao, X.Y. Wu, L.G. Zhu, and Z.X. Liu, Hook evolution and inclusion entrapment during initial solidification process of continuous casting slab, Metall. Res. Technol., 116(2019), No. 1, art. No. 103.

[26] Wei ZJ, Wang ZH, Zhang D, Liu Y, Wang XD, Yao M. Study on behavior of slag rim and shell initial solidification at meniscus in continuous casting slab mold. Metall. Mater. Trans. B, 2024, 5553773

[27] S.P. Gu, G.H. Wen, J.L. Guo, Z. Wang, P. Tang, and Z.B. Hou, Effect of Al₂O₃ on non-Newtonian property and its relation to structure of mold fluxes during shear stress field at 1573 K, J. Non Cryst. Solids, 547(2020), art. No. 120312.

[28] Dong F, Wang YC, Wang BF. Influence of BaO on melting behavior and crystalline phase of concasting mold powder. Spec. Steel, 2006, 2767

[29] M. Leng, F. Lai, and J. Li, Effect of cooling rate on phase and crystal morphology transitions of CaO-SiO₂-based systems and CaO-Al₂O₃-based systems, Materials, 12(2018), No. 1, art. No. 62.

[30] L. Giuliani, G. Iezzi, F. Vetere, et al., Evolution of textures, crystal size distributions and growth rates of plagioclase, clinopyroxene and spinel crystallized at variable cooling rates from a mid-ocean ridge basaltic melt, Earth Sci. Rev., 204(2020), art. No. 103165.

[31] Long X, He SP, Wang Q. Experiment on solidification and composition segregation of solidified mold flux film for peritectic steel continuous casting. Iron Steel, 2017, 52543

[32] Yao C, Wang M, Ni YJet al.. Effect of traveling-wave magnetic field on dendrite growth of high-strength steel slab: Industrial trials and numerical simulation. Int. J. Miner. Metall. Mater., 2023, 3091716

RIGHTS & PERMISSIONS

University of Science and Technology Beijing