CO₂ nanobubble-enhanced cement–fly ash backfill: Optimizing aggregate gradation and microstructure

Abstract

Mine filling materials urgently need to improve mechanical properties and achieve low-carbon transformation. This study explores the mechanism of the synergistic effect of optimizing aggregate fractal grading and introducing CO₂ nanobubble technology to improve the performance of cement–fly ash-based backfill materials (CFB). The properties including fluidity, setting time, uniaxial compressive strength, elastic modulus, porosity, microstructure and CO₂ storage performance were systematically studied through methods such as fluidity evaluation, time test, uniaxial compression test, mercury intrusion porosimetry (MIP), scanning electron microscopy-energy dispersive spectroscopy analysis (SEM-EDS), and thermogravimetric-differential thermogravimetric analysis (TG-DTG). The experimental results show that the density and strength of the material are significantly improved under the synergistic effect of fractal dimension and CO₂ nanobubbles. When the fractal dimension reaches 2.65, the mass ratio of coarse and fine aggregates reaches the optimal balance, and the structural density is greatly improved at the same time. At this time, the uniaxial compressive strength and elastic modulus reach their peak values, with increases of up to 13.46% and 27.47%, respectively. CO₂ nanobubbles enhance the material properties by promoting hydration reaction and carbonization. At the microscopic level, CO₂ nanobubble water promotes the formation of C–S–H (hydrated calcium silicate), C–A–S–H (hydrated calcium aluminium silicate) gel and CaCO₃, which is the main way to enhance the performance. Thermogravimetric studies have shown that when the fractal dimension is 2.65, the dehydration of hydration products and the decarbonization process of CaCO₃ are most obvious, and CO₂ nanobubble water promotes the carbonization reaction, making it surpass the natural state. The CO₂ sequestration quality of cement–fly ash-based materials treated with CO₂ nanobubble water at different fractal dimensions increased by 12.4wt% to 99.8wt%. The results not only provide scientific insights for the design and implementation of low-carbon filling materials, but also provide a solid theoretical basis for strengthening green mining practices and promoting sustainable resource utilization.

Keywords

cement–fly ash-based backfill / CO₂ nanobubble / fractal dimension / macro and micro performance / carbon sequestration

References

[1] Wang B, Cui CQ, Zhao YX, Yang B, Yang QZ. Carbon emissions accounting for China’s coal mining sector: Invisible sources of climate change. Nat. Hazards, 2019, 99(3): 1345.

[2] Shao S, Liu JH, Geng Y, Miao Z, Yang YC. Uncovering driving factors of carbon emissions from China’s mining sector. Appl. Energy, 2016, 166: 220.

[3] M. Nasih, I. Harymawan, Y.I. Paramitasari, and A. Handayani, Carbon emissions, firm size, and corporate governance structure: Evidence from the mining and agricultural industries in Indonesia, Sustainability, 11(2019), No. 9, art. No. 2483.

[4] M. Li, J.X. Zhang, A.L. Li, and N. Zhou, Reutilisation of coal gangue and fly ash as underground backfill materials for surface subsidence control, J. Cleaner Prod., 254(2020), art. No. 120113.

[5] G.R. Feng, W.H. Liu, X.J. Du, J.W. Wang, X.L. Li, and Y.X. Zheng, Crack evolution characteristics of cemented–gangue–fly-ash backfill with different proportions of fly ash and cement, Constr. Build. Mater., 385(2023), art. No. 131498.

[6] Y.H. Sun, S.R. Xie, C.W. Wu, et al., Influence of the ultra-fine fly ash dosages on the mechanical properties of the sulfoaluminate cement-based high water backfilling material, Sci. Rep., 13(2023), No. 1, art. No. 1564.

[7] B.C. Cheng, R.T. Liu, X.H. Li, E. del Rey Castillo, M.J. Chen, and S.C. Li, Effects of fly and coal bottom ash ratio on backfill material performance, Constr. Build. Mater., 319(2022), art. No. 125831.

[8] Deng XJ, Jiao Y, Li SC, et al. . Evaluation of the migration and environmental effects of metal elements within cementitious gangue–fly ash backfill in underground coal mines. Int. J. Min. Sci. Technol., 2024, 34(11): 1551.

[9] I. Cavusoglu, E. Yilmaz, and A.O. Yilmaz, Additivity effect on properties of cemented coal fly ash backfill containing water-reducing admixtures, Constr. Build. Mater., 267(2021), art. No. 121021.

[10] Jiang ML, Cao S, Yilmaz E. Enhanced strength and fracture features of tailings-based concrete reinforced with fibers and X-shaped rocks. J. Mater. Res. Technol., 2025, 36: 62.

[11] Z.Q. Huang, S. Cao, and E. Yilmaz, Microstructure and mechanical behavior of cemented gold/tungsten mine tailings-crushed rock backfill: Effects of rock gradation and content, J. Environ. Manage., 339(2023), art. No. 117897.

[12] Q.L. Li and B.W. Wang, Flowability, microstructure, early and long-term strength modification of cemented ultrafine tailings backfill using artificial lightweight aggregates, Constr. Build. Mater., 438(2024), art. No. 37253.

[13] H.Y. Lyu, Y.L. Chen, H. Pu, et al., Dynamic properties and fragmentation mechanism of cemented tailings backfill with various particle size distributions of aggregates, Constr. Build. Mater., 366(2023), art. No. 130084.

[14] J.Y. Wu, H.W. Jing, Y. Gao, Q.B. Meng, Q. Yin, and Y. Du, Effects of carbon nanotube dosage and aggregate size distribution on mechanical property and microstructure of cemented rockfill, Cem. Concr. Compos., 127(2022), art. No. 104408.

[15] Zhang XH, Maeda N, Craig VSJ. Physical properties of nanobubbles on hydrophobic surfaces in water and aqueous solutions. Langmuir, 2006, 22(11): 5025.

[16] Wang ZX, Bai L, Dong HF, et al. . Modulation of nanobubble behaviors through ionic liquids during CO₂ electroreduction. ACS Sustainable Chem. Eng., 2023, 11(5): 1909.

[17] Bai S, Guan XC, Li H, Ou JP. Effect of the specific surface area of nano-silica particle on the properties of cement paste. Powder Technol., 2021, 392: 680.

[18] J.Y. Wu, S. Yang, M. Williamson, et al., Microscopic mechanism of cellulose nanofibers modified cemented gangue backfill materials, Adv. Compos. Hybrid Mater., 8(2025), No. 2, art. No. 177.

[19] L. Silvestro and P. Jean Paul Gleize, Effect of carbon nanotubes on compressive, flexural and tensile strengths of Portland cement-based materials: A systematic literature review, Constr. Build. Mater., 264(2020), art. No. 120237.

[20] Land G, Stephan D. Controlling cement hydration with nanoparticles. Cem. Concr. Compos., 2015, 57: 64.

[21] J. Chang, H. Zhang, F.Y. Liu, and K. Cui, Exploring the mechanism of micro-nano bubble water in enhancing the mechanical properties of sulfoaluminate cement-based materials, Constr. Build. Mater., 411(2024), art. No. 134400.

[22] Cretu A, Mattea C, Stapf S, Ardelean I. The effect of silica nanoparticles on the pore structure of hydrating cement paste: A spatially resolved low-field NMR study. Mol. Phys., 2018, 117(7–8): 1006

[23] Reches Y, Thomson K, Helbing M, Kosson DS, Sanchez F. Agglomeration and reactivity of nanoparticles of SiO₂, TiO₂, Al₂O₃, Fe₂O₃, and clays in cement pastes and effects on compressive strength at ambient and elevated temperatures. Constr. Build. Mater., 2018, 167: 860.

[24] Temesgen T, Bui TT, Han M, Kim TI, Park H. Micro and nanobubble technologies as a new horizon for water-treatment techniques: A review. Adv. Colloid Interface Sci., 2017, 246: 40.

[25] L.Q. Zhang, M.Q. Bian, Z.R. Xiao, et al., Using nano-CaCO₃ and ceramic tile waste to design low-carbon ultra high performance concrete, Nanotechnol. Rev., 13(2024), No. 1, art. No. 20230198.

[26] X.X. Cao, T.Q. Jiang, H. Shimada, T. Sasaoka, and A. Hamanaka, Influence of CO₂ nano-bubble water concentration and curing time on the macroscopic and microscopic mechanical properties of cemented backfill materials, J. Build. Eng., 98(2024), art. No. 111099.

[27] H.J. Choi, J.K. Kim, W. Yeo, et al., Effect of nanobubble water on the mechanical properties and carbon sequestration efficiency of concrete cured under various conditions, Case Stud. Constr. Mater., 21(2024), art. No. e03596.

[28] Y. Jiang, Z.H. Ma, Z.J. Gu, F.Q. Liu, P.L. Shen, and C.S. Poon, A novel approach for improving aqueous carbonation kinetics with CO₂ micro- and nano-bubbles, Chem. Eng. J., 500(2024), art. No. 157363.

[29] X.X. Cao, A. Hamanaka, H. Shimada, and T. Sasaoka, Effect of CO₂ nanobubble water on the fracture properties of cemented backfill materials under different aggregate fractal dimensions, Appl. Sci., 14(2024), No. 17, art. No.7792.

[30] Jiang XZ, Wang W, Yu G, Deng SB. Contribution of nanobubbles for PFAS adsorption on graphene and OH- and NH₂-functionalized graphene: Comparing simulations with experimental results. Environ. Sci. Technol., 2021, 55(19): 13254

[31] J.Y. Wu, H.W. Jing, Q. Yin, L.Y. Yu, B. Meng, and S.C. Li, Strength prediction model considering material, ultrasonic and stress of cemented waste rock backfill for recycling gangue, J. Cleaner Prod., 276(2020), art. No. 123189.

[32] M.M. Feng, X.X. Cao, T.Q. Jiang, and W.L. Zhang, Effects of particle gradation and material proportions on the mechanical properties of crushed stone aggregates under cyclic loading, J. Build. Eng., 97(2024), art. No. 110777.

[33] A.N. Bala, K. Shelote, and S. Gupta, Durability and cost analysis of high-volume fly ash blended self-compacting mortar, J. Mater. Civ. Eng., 36(2024), No. 3, art. No. 04024002.

[34] Maarup C, Hjuler K, Dam-Johansen K. High temperature cement raw meal flowability. Powder Technol., 2014, 253: 686.

[35] Fall M, Benzaazoua M, Saa EG. Mix proportioning of underground cemented tailings backfill. Tunnelling Underground Space Technol., 2008, 23(1): 80.

[36] Yin SH, Wu AX, Hu KJ, Wang Y, Zhang YK. The effect of solid components on the rheological and mechanical properties of cemented paste backfill. Miner. Eng., 2012, 35: 61.

[37] Hu J, Ge Z, Wang KJ. Influence of cement fineness and water-to-cement ratio on mortar early-age heat of hydration and set times. Constr. Build. Mater., 2014, 50: 657.

[38] Trtnik G, Turk G, Kavčič F, Bosiljkov VB. Possibilities of using the ultrasonic wave transmission method to estimate initial setting time of cement paste. Cem. Concr. Res., 2008, 38(11): 1336.

[39] Chen QS, Zhang QL, Qi CC, Fourie A, Xiao CC. Recycling phosphogypsum and construction demolition waste for cemented paste backfill and its environmental impact. J. Cleaner Prod., 2018, 186: 418.

[40] J.Y. Wu, H.S. Wong, H. Zhang, Q. Yin, H.W. Jing, and D. Ma, Improvement of cemented rockfill by premixing low-alkalinity activator and fly ash for recycling gangue and partially replacing cement, Cem. Concr. Compos., 145(2024), art. No. 105345.

[41] Gaviria X, Borrachero MV, Payá J, Monzó JM, Tobón JI. Mineralogical evolution of cement pastes at early ages based on thermogravimetric analysis (TG). J. Therm. Anal. Calorim., 2018, 132(1): 39.

[42] Soin AV, Catalan LJJ, Kinrade SD. A combined QXRD/TG method to quantify the phase composition of hydrated Portland cements. Cem. Concr. Res., 2013, 48: 17.

[43] H.R. Liu, Z.H. Tian, X. Sun, J.Z. Xiang, and X.C. Jiao, Study on the multiscale properties of cement-based materials containing nano-bubble water, Constr. Build. Mater., 360(2022), art. No. 129595.

[44] Chang EE, Pan SY, Yang L, Chen YH, Kim H, Chiang PC. Accelerated carbonation using municipal solid waste incinerator bottom ash and cold-rolling wastewater: Performance evaluation and reaction kinetics. Waste Manage., 2015, 43: 283.

[45] Huijgen WJJ, Witkamp GJ, Comans RNJ. Mechanisms of aqueous wollastonite carbonation as a possible CO₂ sequestration process. Chem. Eng. Sci., 2006, 61(13): 4242.

[46] Ji L, Yu H, Wang XL, et al. . CO₂ sequestration by direct mineralisation using fly ash from Chinese Shenfu coal. Fuel Process. Technol., 2017, 156: 429.

[47] J.X. Zhang, B.Y. Li, Y.C. Xie, et al., Carbon negative backfill mining in coal mines for carbon neutralization: Chemical carbon fixation performances with mineralized gangue, Int. J. Rock Mech. Min. Sci., 186(2025), art. No. 106016.

RIGHTS & PERMISSIONS

University of Science and Technology Beijing