Hook formation and control mechanisms in continuously cast slabs of ultra-low carbon steel

Abstract

The hook formation mechanism in continuously cast slabs of ultra-low carbon steel was analyzed in detail through numerical calculations and experimental observations using optical microscopy, and its distribution characteristics were determined. Numerical simulations confirmed that the freezing–overflow mechanism is the primary cause of hook formation. They also revealed that the freezing event occurs unpredictably, while the overflow event takes place during the positive strip time. The average pitch of oscillation marks (OMs) on the slab surface was 8.693 mm, while the theoretical pitch was 8.889 mm, with a difference of approximately 2%. This discrepancy primarily results from varying degrees of overflow, which affects the morphology of the OMs and the positions of their deepest points. Notably, this result further confirmed that the freezing and overflow in the meniscus were indeed caused by the periodic oscillation of the mold. Higher superheat hindered hook formation, leading to a negative correlation between the hook depth distribution around the slab and the temperature distribution within the mold. Therefore, the depth of the corner hook was greater than that of other positions, which was caused by the intensified cooling effect of the corner. Moreover, key factors influencing hook development were analyzed, providing insights into transient fluid flow and heat transfer characteristics within the mold. Transient fluid flow and heat transfer contributed to the randomness and tendency of hook formation. This randomness was reflected in the varying angles of the hooks, whereas the tendency was evident in the negative correlation between superheat and hook length. Based on the randomness and tendency of hook formation and its profile characteristics, a new method for controlling hook depth based on “sine law” is proposed.

Keywords

meniscus / surface defect / ultra-low carbon steel / hook / oscillation mark / numerical simulation

References

[1] TakeuchiE, BrimacombeJK. The formation of oscillation marks in the continuous casting of steel slabs. Metall. Trans. B, 1984, 153493.

[2] YamamuraH, MizukamiY, MisawaK. Formation of a solidified hook-like structure at the subsurface in ultra low carbon steel. ISIJ Int., 1996, 36S223.

[3] SenguptaJ, ShinHJ, ThomasBG, KimSH. Micrograph evidence of meniscus solidification and sub-surface microstructure evolution in continuous-cast ultralow-carbon steels. Acta Mater., 2006, 5441165.

[4] SchmidtKD, FriedelF, ImlauKP, JägerW, MüllerKT. Consequent improvement of surface quality by systematic analysis of slabs. Steel Res. Int., 2003, 7411–12659.

[5] BiratJP, LarrecqM, LamantJY, PetegniefJ. Continuous casting mold: a basic tool for surface quality and strand productivity. The 74th Steelmaking Conference, 19913

[6] ShinHJ, ThomasBG, LeeGG, ParkJM, LeeCH, KimSH. Analysis of hook formation mechanism in ultra low carbon steel using CON1D heat flow-solidification model. Mater. Sci. Technol., 2004, 211

[7] FredrikssonH, ElfsbergJ. Thoughts about the initial solidification process during continuous casting of steel. Scand. J. Metall., 2002, 315292.

[8] EmiT, NakatoH, IidaY, et al.. Influence of physical and chemical properties of mold powders on the solidification and occurrence of surface defects of strand cast slabs. 61st Nat. Open Hearth Basic Oxygen Steel Conference Proceedings, 1978350

[9] SavageJ, PritchardWH. The problem of rupture of the billet in the continuous casting of steel. J. Iron Steel Inst., 1954, 1783269

[10] SatoR. National Open Hearth and Basic Oxygen. Steelmaking Conference Proceedings, 197948

[11] SchwerdtfegerK, ShaH. Depth of oscillation marks forming in continuous casting of steel. Metall. Mater. Trans. B, 2000, 314813.

[12] ThomasBG, ZhuH. Thermal distortion of solidifying shell near meniscus in continuous casting of steel. JIM/TMS Solidification Science and Processing Conference, 199513

[13] SahaiY, EmiT. Melt flow characterization in continuous casting tundishes. ISIJ Int., 1996, 366667.

[14] SenguptaJ, ThomasBG, ShinHJ, et al.. A new mechanism of hook formation during continuous casting of ultra-low-carbon steel slabs. Metall. Mater. Trans. A, 2006, 3751597.

[15] BadriA, NatarajanTT, SnyderCC, et al.. A mold simulator for continuous casting of steel: Part II. The formation of oscillation marks during the continuous casting of low carbon steel. Metall. Mater. Trans. B, 2005, 363373.

[16] PützO, BreitfeldO, RödlS. Investigations of flow conditions and solidification in continuous casting moulds by advanced simulation techniques. Steel Res. Int., 2003, 7411–12686.

[17] ShinHJ, LeeGG, ChoiWY, et al.. Effect of mold oscillation on powder consumption and hook formation in ultra low carbon steel slabs. Iron and Steel Technology Iron and Steel Technology Conference Proceedings, 20041157

[18] BoKT, ChengGG, WuJ, ZhaoP, WangJ. Mechanism of oscillation mark formation in continuous casting of steel. J. Univ. Sci. Technol. Beijing—Miner. Metall. Mater., 2000, 73189

[19] BadriA, NatarajanTT, SnyderCC, PowersKD, MannionFJ, CrambAW. A mold simulator for the continuous casting of steel: Part I. the development of a simulator. Metall. Mater. Trans. B, 2005, 363355.

[20] LeeGG, ThomasBG, KimSH, et al.. Microstructure near corners of continuous-cast steel slabs showing three-dimensional frozen meniscus and hooks. Acta Mater., 2007, 55206705.

[21] YangJ, MengXN, ZhuMY. Transient thermo-fluid and solidification behaviors in continuous casting mold: Oscillation behaviors. ISIJ Int., 2018, 58112071.

[22] JonayatASM, ThomasBG. Transient thermo-fluid model of meniscus behavior and slag consumption in steel continuous casting. Metall. Mater. Trans. B, 2014, 4551842.

[23] Ramirez LopezPE, MillsKC, LeePD, SantillanaB. A unified mechanism for the formation of oscillation marks. Metall. Mater. Trans. B, 2012, 431109.

[24] ZhangXB, WangQQ, YangW, WangSD, ZhangLF. Three-dimensional distribution of hooks in Al-killed low-carbon continuous casting steel slabs. Metall. Mater. Trans. B, 2018, 4952533.

[25] SorimachiK, HasunumaJ. Development of continuous casting technologies at Kawasaki Steel. Kawasaki Steel Tech. Rep., 1996, 3552

[26] TongWJ, LuoS, WangWL, ZhuMY. Numerical simulation of oscillation mark formation and slag consumption in meniscus region during a mold oscillation cycle. Metall. Mater. Trans. B, 2024, 552727.

[27] BikermanJJ. Adhesion in friction. Wear, 1976, 3911.

[28] DengXX, LiLP, WangXH, JiYQ, JiCX, ZhuGS. Subsurface macro-inclusions and solidified hook character in aluminum-killed deep-drawing steel slabs. Int. J. Miner. Metall. Mater., 2014, 216531.

[29] TongWJ, LuoS, WangWL, ZhuMY. Modelling of meniscus behavior and slag consumption during initial casting stage of continuous casting process. Met. Mater. Int., 2024, 3082183.

[30] TongWJ, LuoS, ZhouYL, WangYC, WangWL, ZhuMY. Inclusion capture mechanism of hook in low carbon steel continuously cast slab. Metall. Mater. Trans. B, 2025, 561723.

[31] LiQP, WenGH, ChenFH, TangP, HouZB, MoXY. Irregular initial solidification by mold thermal monitoring in the continuous casting of steels: A review. Int. J. Miner. Metall. Mater., 2024, 3151003.

[32] TeshimaT, KubotaJ, SuzukiM, OzawaK, MasaokaT, MiyaharaS. Influence of casting conditions on molten steel flow in continuous casting mold at high speed casting of slabs. Tetsu-to-Hagané, 1993, 795576.

RIGHTS & PERMISSIONS

University of Science and Technology Beijing